Abstract
Abstract The invention concerns a method for producing a coaxial cable intended for the transmission of very high frequency signals. This coaxial cable comprises a dielectric insulating layer composed of foamed polytetrafluoroethylene or a composition comprising at least 80% of this product named hereinafter COMPOUND. The layer of insulating material is directly obtained by cold extrusion of a COMPOUND powder, the intimate mixing of a pore-forming agent and a foaming agent and a lubricating oil. The mixing of the COMPOUND powder, the pore-forming and foaming agents is effected dry or in aqueous dispersion. Principal application: Fields of use of ultra-high frequencies such as radars and transmissions.
Inventors
- 👤 Alain Battais
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 09:40
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/04; C08J9/06; H; H01; H01B; H01B11/00; H01B11/18; H01B11/1834; H01B11/1839; H01B13/00; H01B13/06; H01B13/067; H01B13/14; H01B13/142; C08J2201/00; C08J2201/02; C08J2201/03; C08J2327/00; C08J2327/02; C08J2327/12; C08J2327/18
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
83 words
A method for producing a coaxial cable comprising a central conductor and a dielectric insulating layer which comprises preparing polytetrafluoroethylene powder composition in admixture with a pore-forming agent, cold extruding said mixture onto said central conductor so as to form said dielectric insulating layer thereon, said dielectric insulating layer comprising at least about 80% of said polytetrafluoroethylene, and expanding said dielectric insulating layer by sublimation of said pore-forming agent, whereby said dielectric insulating layer has a dielectric constant no greater than about 1.3.
Claim 2
Independent Claim
83 words
A method for producing a coaxial cable comprising a central conductor and a dielectric insulating layer which comprises preparing polytetrafluoroethylene powder composition in admixture with a pore-forming agent, cold extruding said mixture onto said central conductor so as to form said dielectric insulating layer thereon, said dielectric insulating layer comprising at least about 80% of said polytetrafluoroethylene, and expanding said dielectric insulating layer by sublimation of said pore-forming agent, whereby said dielectric insulating layer has a dielectric constant no greater than about 1.3.
Claim 3
Dependent Claim
22 words
The method of claim 1 wherein said polytetrafluoroethylene powder composition is in intimate mixture with said pre-forming agent and a framing agent.
Claim 4
Dependent Claim
14 words
The method of claim 2 wherein said polytetrafluoroethylene powder composition includes a lubricating oil.
Claim 5
Dependent Claim
19 words
The method of claim 1 wherein said polytetrafluoroethylene powder composition has a granulometry of lower than about 500 microns.
Claim 6
Dependent Claim
20 words
The method of claim 4 wherein said polytetrafluoroethylene powder composition has a granulometry of between about 300 and 400 microns.
Claim 7
Dependent Claim
33 words
The method of claim 1 wherein said pore-forming agent is selected from the group consisting of benzene, toluene, naphthalene, benzaldehye, aniline or one of the mono- or polyhalogenated derivatives thereof, and mixtures thereof.
Claim 8
Dependent Claim
37 words
The method of claim 2 wherein said foaming agent is selected from the group consisting of activated and non-activated azodicarbonamide, modified azodicarbonamide, 5 phenyl tetrazol and its derivatives, the aromatic derivatives of the hydrazines, and mixtures thereof.
Claim 9
Dependent Claim
20 words
The method of claim 2 wherein said foaming agent has a decomposition point of between about 200° and 390° C.
Claim 10
Dependent Claim
26 words
The method of claim 2 wherein said intimate mixture of said pore-forming agent and said foaming agent has a granulometry of less than about 200 microns.
Claim 11
Dependent Claim
27 words
The method of claim 9 wherein said intimate mixture of said pore-forming agent and said foaming agent has a granulometry of between about 50 and 100 microns.
Claim 12
Dependent Claim
34 words
The method of claim 3 wherein said lubricating oil has an evaporating temperature which is less than the sublimation temperature or the decomposition temperature of either of said pore-forming agent or said foaming agent.
Claim 13
Dependent Claim
26 words
The method of claim 2 wherein said step of preparing said expanded polytetrafluoroethylene comprises dry mixing said polytetrafluoroethylene powder, said pre-forming agent, and said foaming agent.
Claim 14
Dependent Claim
30 words
The method of claim 2 wherein said step of preparing said expanded polytetrafluoroethylene composition comprises preparing an acqueous dispersion of said polytetrafluoroethylene powder, said pore-forming agent and said foaming agent.
Claim 15
Dependent Claim
50 words
The method of claim 2 wherein said step of preparing said expanded polytetrafluoroethylene composition comprises dispersing said polytetrafluoroethylene powder in a first liquid, dispersing said pore forming agent and said foaming agent in a second liquid, mixing said first and second liquid mixtures, and evaporating said first and second liquids.
Claim 16
Dependent Claim
15 words
The method of claim 14 wherein said first and second liquids comprises the same liquid.
Claim 17
Dependent Claim
36 words
The method of claim 14 including the steps of lubricating said evaporated mixture by adding a lubricating oil thereto prior to said cold extruding step, and subsequently evaporating and sintering said extruded layer of expanded polytetrafluoroethylene.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-05-04 | 1990-11-03 | 1991-05-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-05-04 | 1994-11-03 | 1995-05-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-05-04 | 1998-11-03 | 1999-05-05 | $7700.00 | Window Closed / Lapsed |