Continuous vapor deposition method for producing a coated glass article
Assignee: Pilkington North America Inc
•
Filing: 1985-10-07
•
Granted: 1987-04-28
•
Expires: 2005-10-07
Abstract
Abstract A continuous, chemical vapor deposition method for producing a coated glass article is disclosed. A glass substrate is advanced continuously, while hot, past first and second treating stations. A non-oxidizing atmosphere is maintained in the vicinity of the first treating station, while an oxidizing atmosphere is maintained in the vicinity of the second station. A non-oxidizing gas which contains a silane, e.g., SiH 4 , is directed from the first treating station against a surface of the glass to form a silicon coating on that surface. An oxidizing gas which includes a metal compound in the vapor phase is directed from the second station against the silicon-coated surface of the article. The process is controlled so that the silane-containing gas forms a reflective silicon coating on the glass surface, the oxidizing gas which includes a metal compound forms a coating of an oxide of the metal, and oxidation before the article reaches the second treating station forms a silicon oxide layer on the silicon which is of sufficient thickness that the metal oxide layer is substantially free of pinholing.
Inventors
- 👤 Gerald A. Callies
- 👤 Eberhard R. Albach
- 👤 John F. Conour
- 👤 Richard A. Herrington
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 20:50
CPC Classifications
B; B05; B05D; B05D1/00; B05D1/02; C; C03; C03C; C03C17/00; C03C17/34; C03C17/3411; C03C17/3429; C03C17/3482; C23; C23C; C23C16/00; C23C16/02; C23C16/0209; C23C16/0218; C23C16/22; C23C16/30; C23C16/40; C23C16/407
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
228 words
A continuous chemical vapor deposition method for producing a coated glass article, said method comprising the steps of continuously advancing the article, while hot, past first and second successive treating stations, at least the first of which is in a closed zone, maintaining a non-oxidizing atmosphere in the closed zone in which the first treating station is situated, maintaining an oxidizing atmosphere around the second treating station and the adjacent glass, directing a non-oxidizing gas which contains a silane from the first treating station against a surface of the article to form a silicon coating on that surface, directing an oxidizing gas which includes a metal compound in the vapor phase from the second treating station against the coated surface of the glass article, controlling the temperature of the glass article, the residence time in the oxidizing atmosphere around the second treating station, the composition of the non-oxidizing gas from the first treating station and the composition of the oxidizing gas from the second station so that the silane-containing gas forms a reflective silicon coating on the glass surface, the oxidizing gas which includes a metal forms a coating of an oxide of the metal, and oxidation before the article reaches the second treating station forms a silicon oxide layer on the silicon which is of sufficient thickness that the metal oxide layer is substantially free of pinholing.
Claim 2
Dependent Claim
228 words
A continuous chemical vapor deposition method for producing a coated glass article, said method comprising the steps of continuously advancing the article, while hot, past first and second successive treating stations, at least the first of which is in a closed zone, maintaining a non-oxidizing atmosphere in the closed zone in which the first treating station is situated, maintaining an oxidizing atmosphere around the second treating station and the adjacent glass, directing a non-oxidizing gas which contains a silane from the first treating station against a surface of the article to form a silicon coating on that surface, directing an oxidizing gas which includes a metal compound in the vapor phase from the second treating station against the coated surface of the glass article, controlling the temperature of the glass article, the residence time in the oxidizing atmosphere around the second treating station, the composition of the non-oxidizing gas from the first treating station and the composition of the oxidizing gas from the second station so that the silane-containing gas forms a reflective silicon coating on the glass surface, the oxidizing gas which includes a metal forms a coating of an oxide of the metal, and oxidation before the article reaches the second treating station forms a silicon oxide layer on the silicon which is of sufficient thickness that the metal oxide layer is substantially free of pinholing.
Claim 3
Dependent Claim
32 words
A method as claimed in claim 1 wherein the non-oxidizing gas which contains a silane additionally contains an unsaturated hydrocarbon in such proportion that it imparts alkali resistance to the silicon coating.
Claim 4
Dependent Claim
83 words
A method as claimed in claim 1 which additionally includes the steps of washing the coating on the glass article, after it has cooled to a sufficiently low temperature, with dilute hydrofluoric acid, and controlling the temperature of the glass, when washed, the duration of the washing step and the concentration of the hydrofluoric acid so that neither the glass article nor the coating thereon is significantly deteriorated, while the formation of a film on the coated article upon subsequent tempering is prevented.
Claim 5
Dependent Claim
58 words
A method as claimed in claim 3 which additionally includes the step of agitating the hydrofluoric acid during the washing step, and wherein the duration of the washing step is from about four seconds to about twelve seconds while the concentration of the hydrofluoric acid is from about 2 percent by weight to about 10 percent by weight.
Claim 6
Dependent Claim
33 words
A method as claimed in claim 2, wherein said non-oxidizing gas comprises approximately 4 to 5 volume percent of an unsaturated hydrocarbon, from 9 to 13 volume percent of a silane, balance nitrogen.
Claim 7
Dependent Claim
13 words
A method as claimed in claim 5, wherein said unsaturated hydrocarbon comprises ethylene.
Claim 8
Dependent Claim
29 words
A method as claimed in claim 1, wherein said oxidizing gas which includes a metal compound comprises approximately 99 volume percent of air and 1 volume percent of tetramethyltin.
Claim 9
Dependent Claim
49 words
A method as claimed in claim 1, wherein said glass surface is at a temperature of at least 1100° F. when treated with said non-oxidizing gas containing a silane and at least 750° F. when the treatment with the oxidizing gas which contains a metal compound is carried out.
Claim 10
Dependent Claim
53 words
A method as claimed in claim 8, wherein the residence time in the oxidizing atmosphere around the second treating station is sufficient to produce a silicone oxide coating of from 20 to 50 a thickness on the silicon coating and said oxidizing gas treatment is carried out at a temperature of 970°±20° F.
Claim 11
Dependent Claim
50 words
A method as claimed in claim 8, wherein the residence time in the oxidizing atmosphere around the second treating station is sufficient to produce a silicone oxide coating of from 60 to 90 A thickness and said oxidizing gas treatment is carried out at a temperature of approximately 1170° F.
Claim 12
Dependent Claim
30 words
A method as claimed in claim 1, wherein said glass comprises a heat absorbing bronze colored composition and the coated glass article has a shading coefficient of 0.45 to 0.55.
References Cited (Backward Citations)
US3374141A
Cited
US4019887A
Cited
US4188452A
Cited
US4188444A
Cited
US4100330A
Cited
US4187336A
Cited
US4206252A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-27 | 1990-10-27 | 1991-04-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-27 | 1994-10-27 | 1995-04-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-27 | 1998-10-27 | 1999-04-28 | $7700.00 | Window Closed / Lapsed |