Quartz glass-made optical fibers coated with a silicone composition
Assignee: Shin-Etsu Chemical Co Ltd
•
Filing: 1983-08-17
•
Granted: 1987-04-28
•
Expires: 2003-08-17
Abstract
Abstract The invention provides a novel silicone-coated, quartz glass-made optical fiber which is very advantageous in the high efficiency of the coating process as well as in the improved workability in the connecting works of the fiber terminals for extension of the communication lines by virtue of the excellent peelability of the coating layer from the surface of the quartz glass fiber even by mere drawing the coated fiber between fingers. The coating layer is formed of a radiation- or UV-cured silicone composition comprising (A-a) an organopolysiloxane having aliphatic unsaturation, e.g. vinyl, and/or (A-b) an organopolysiloxane having mercaptoalkyl groups, e.g. 3-mercaptopropyl groups, and (B) a curing accelerator.
Inventors
- 👤 Kiyohiro Kondow
- 👤 Nobuo Takasaka
- 👤 Yoshinori Hida
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 20:06
CPC Classifications
C; C03; C03C; C03C25/00; C03C25/10; C03C25/104; C03C25/106; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2962; Y10T428/2964; Y10T428/31504; Y10T428/31551; Y10T428/31609; Y10T428/31612
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
215 words
A quartz glass-made optical fiber coated with a silicone composition which comprises an elongated quartz glass-made fiber and a coating layer thereon formed of a cured silicone composition comprising: (A) at least one kind of orgnosilicon compound selected from the class consisting of: (A-a) an organopolysiloxane or organosilane represented by the formula ##EQU1## in which R 1 is a monovalent organic group having aliphatic unsaturation, R 2 is a substituted or unsubstituted monovalent hydrocarbon group having no aliphatic unsaturation, a is a number from 0.0004 to 4.0 inclusive and b is zero or a positive number not exceeding 2.5 with the proviso that a+b is in the range from 1.1 to 4.0 inclusive, and (A-b) an organopolysiloxane or organosilane represented by the formula ##EQU2## in which R 3 is a mercaptoalkyl group, R 4 is a substituted or unsubstituted monovalent hydrocarbon group having no aliphatic unsaturation, c is a number from 0.0004 to 4.0 inclusive and d is zero or a positive number not exceeding 2.5 with the proviso that c+d is in the range from 1.1 to 4.0 inclusive, wherein at least 8% by moles of the total organic groups bonded to the silicon atoms are phenyl groups; and (B) a curing accelerator, the coating layer having been cured by irradiation with actinic rays.
Claim 2
Dependent Claim
215 words
A quartz glass-made optical fiber coated with a silicone composition which comprises an elongated quartz glass-made fiber and a coating layer thereon formed of a cured silicone composition comprising: (A) at least one kind of orgnosilicon compound selected from the class consisting of: (A-a) an organopolysiloxane or organosilane represented by the formula ##EQU1## in which R 1 is a monovalent organic group having aliphatic unsaturation, R 2 is a substituted or unsubstituted monovalent hydrocarbon group having no aliphatic unsaturation, a is a number from 0.0004 to 4.0 inclusive and b is zero or a positive number not exceeding 2.5 with the proviso that a+b is in the range from 1.1 to 4.0 inclusive, and (A-b) an organopolysiloxane or organosilane represented by the formula ##EQU2## in which R 3 is a mercaptoalkyl group, R 4 is a substituted or unsubstituted monovalent hydrocarbon group having no aliphatic unsaturation, c is a number from 0.0004 to 4.0 inclusive and d is zero or a positive number not exceeding 2.5 with the proviso that c+d is in the range from 1.1 to 4.0 inclusive, wherein at least 8% by moles of the total organic groups bonded to the silicon atoms are phenyl groups; and (B) a curing accelerator, the coating layer having been cured by irradiation with actinic rays.
Claim 3
Dependent Claim
37 words
quartz glass-made optical fiber composition as claimed in claim 1 wherein the monovalent hydrocarbon group having aliphatic unsaturation denoted by the symbol R 1 is selected from the class consisting of vinyl, allyl, 3-acryl-oxypropyl and 3-methacryloxypropyl groups.
Claim 4
Dependent Claim
31 words
The quartz glass-made optical fiber coated with a silicone composition as claimed in claim 1 wherein the mercaptoalkyl group denoted by the symbol R 3 has 1 to 10 carbon atoms.
Claim 5
Dependent Claim
22 words
quartz glass-made optical fiber coated with a silicone composition as claimed in claim 3 wherein the mercaptoalkyl group is a 3-mercaptopropyl group.
Claim 6
Dependent Claim
54 words
The quartz glass-made optical fiber coated with a silicone composition as claimed in claim 1 wherein the component (A) is a mixture of the components (A-a) and (A-b) in such a proportion that from 0.5 to 5 mercaptoalkyl groups in the component (A-b) are provided per each aliphatically unsaturated linkage in the component (A-a).
Claim 7
Dependent Claim
27 words
The quartz glass-made optical fiber coated with a silicone composition as claimed in claim 5 wherein the component (A-b) contains at least two mercaptoalkyl groups per molecule.
Claim 8
Dependent Claim
34 words
The quartz glass-made optical fiber coated with a silicone composition as claimed in claim 1 wherein from 5 to 80% by moles of the organic groups contained in the component (Aa) are phenyl groups.
Claim 9
Dependent Claim
28 words
The quartz glass-made optical fiber coated with a silicone composition as claimed in claim 1 wherein the irradiation with actinic rays is performed by exposure to ultraviolet light.
Claim 10
Independent Claim
230 words
A method for the preparation of a quartz glass-made optical fiber coated with a silicone composition which comprises the steps of: (a) coating an elongated quartz glass-made fiber with a radiation-curable silicone composition comprising (A) at least one kind of organosilicon compounds selected from class consisting of (A-a) an organopolysiloxane or organosilane represented by the formula ##EQU3## in which R 1 is a monovalent organic group having aliphatic unsaturation, R 2 is a substituted or unsubstituted monovalent hydrocarbon group having no aliphatic unsaturation, a is a number from 0.0004 to 4.0 inclusive and b is zero or a positive number not exceeding 2.5 with the proviso that a+b is in the range from 1.1 to 4.0 inclusive, and (A-b) an organopolysiloxane or organosilane represented by the formula ##EQU4## in which R 3 is a mercaptoalkyl group, R 4 is a substituted or unsubstituted monovalent hydrocarbon group having no aliphatic unsaturation, c is a number from 0.0004 to 4.0 inclusive and d is zero or a positive number not exceeding 2.5 with the proviso that c+d is in the range from 1.1 to 4.0 inclusive, and wherein at least 8% by moles of the total organic groups bonded to the silicon atoms are phenyl groups; (B) a curling accelerator, and (b) irradiating the thus coated quartz glass-made fiber with actinic rays to cure the silicone composition into a cured coating layer.
Claim 11
Independent Claim
230 words
A method for the preparation of a quartz glass-made optical fiber coated with a silicone composition which comprises the steps of: (a) coating an elongated quartz glass-made fiber with a radiation-curable silicone composition comprising (A) at least one kind of organosilicon compounds selected from class consisting of (A-a) an organopolysiloxane or organosilane represented by the formula ##EQU3## in which R 1 is a monovalent organic group having aliphatic unsaturation, R 2 is a substituted or unsubstituted monovalent hydrocarbon group having no aliphatic unsaturation, a is a number from 0.0004 to 4.0 inclusive and b is zero or a positive number not exceeding 2.5 with the proviso that a+b is in the range from 1.1 to 4.0 inclusive, and (A-b) an organopolysiloxane or organosilane represented by the formula ##EQU4## in which R 3 is a mercaptoalkyl group, R 4 is a substituted or unsubstituted monovalent hydrocarbon group having no aliphatic unsaturation, c is a number from 0.0004 to 4.0 inclusive and d is zero or a positive number not exceeding 2.5 with the proviso that c+d is in the range from 1.1 to 4.0 inclusive, and wherein at least 8% by moles of the total organic groups bonded to the silicon atoms are phenyl groups; (B) a curling accelerator, and (b) irradiating the thus coated quartz glass-made fiber with actinic rays to cure the silicone composition into a cured coating layer.
Claim 12
Dependent Claim
31 words
The method as claimed in claim 9 wherein the irradiation with actinic rays in the step (b) is performed by the exposure of the coated quartz glass-made fiber to ultraviolet light.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-27 | 1990-10-27 | 1991-04-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-27 | 1994-10-27 | 1995-04-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-27 | 1998-10-27 | 1999-04-28 | $7700.00 | Window Closed / Lapsed |