Hybrid and unidirectional carbon-carbon fiber reinforced laminate composites
Assignee: VOUGHT Corp A DE CORP
•
Filing: 1983-11-25
•
Granted: 1987-04-21
•
Expires: 2003-11-25
Abstract
Abstract Novel carbon-carbon laminate composite materials capable of significantly increased strengths in at least one predetermined direction of load are disclosed. The composites can comprise plies of resin impregnated woven carbon or graphite cloth material in combination with resin impregnated carbon or graphite filament unidirectional tape or can be fabricated from the unidirectional tape alone. Generally the unidirectional reinforcement of the tape plies provides higher strengths and moduli in specific directions which can be controlled during lay up of parts. The processes for obtaining the beneficial increase strength of unidirectional tape ply materials while avoiding fabrication problems resulting therefrom are also disclosed.
Inventors
- 👤 Robert E. Yeager
- 👤 Isaac E. Harder
- 👤 Earl L. Stone, III
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 02:11
CPC Classifications
B; B32; B32B; B32B9/00; B32B9/005; B32B9/007; B29; B29C; B29C70/00; B29C70/04; B29C70/06; B29C70/08; B29C70/086; B32B37/00; B32B9/04; C; C04; C04B; C04B35/00; C04B35/71; C04B35/78; C04B35/80; C04B35/83; B32B2260/00; B32B2260/02; B32B2260/021; B32B2260/04; B32B2260/046; F; F02; F02B; F02B75/00; F02B75/02; F02B2075/022; F02B2075/027; Y; Y10; Y10S; Y10S428/00; Y10S428/902; Y10T; Y10T428/00; Y10T428/30; Y10T442/00; Y10T442/30; Y10T442/3472; Y10T442/3504; Y10T442/3512
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
103 words
The process for producing carbon-carbon structural laminates which comprise plies of unidirectional resin impregnated carbon or graphite filament tape comprising the steps of: (a) laying up the plies of the carbon-carbon material in a manner such that the fibers of said filament tape plies are laid along predetermined directions so as to provide the part to be fabricated with increased strength along a predetermined direction of applied force; (b) curing said laid up laminate under pressures sufficient to provide controlled evolution of volatiles, at increasing temperatures until cured; (c) pyrolyzing said cured laminate at elevated temperatures; and (d) densifying the resulting laminate material.
Claim 2
Dependent Claim
103 words
The process for producing carbon-carbon structural laminates which comprise plies of unidirectional resin impregnated carbon or graphite filament tape comprising the steps of: (a) laying up the plies of the carbon-carbon material in a manner such that the fibers of said filament tape plies are laid along predetermined directions so as to provide the part to be fabricated with increased strength along a predetermined direction of applied force; (b) curing said laid up laminate under pressures sufficient to provide controlled evolution of volatiles, at increasing temperatures until cured; (c) pyrolyzing said cured laminate at elevated temperatures; and (d) densifying the resulting laminate material.
Claim 3
Dependent Claim
27 words
The process of claim 1 wherein said laid up laminate is subjected to initial pressure so as to remove air entrapped during lay up prior to curing.
Claim 4
Dependent Claim
32 words
The process of claim 1 wherein that portion of the impregnated resin material which migrates to the surface of said laminate during cure is allowed to remain thereon during the curing step.
Claim 5
Dependent Claim
15 words
The process of claim 1 wherein said densification is effected through chemical vapor deposition techniques.
Claim 6
Dependent Claim
18 words
The process of claim 1 wherein said densification is effected through liquid resin impregnation, cure and pyrolysis cycles.
Claim 7
Dependent Claim
45 words
The process of claim 1 wherein initial pressure of about 5 psi is employed during said cure cycle and pressure is thereafter increased to from about 30 to about 60 psi when curing temperatures reach a range of from about 200° to about 240° F.
Claim 8
Dependent Claim
61 words
In a method for forming laminate carbon-carbon substrate materials which include plies of unidirectional resin impregnated filament tape the improvement comprising: curing said laminate in a platen press by applying pressures of at least about 30 psi without a decrease in pressure during cure and allowing the resin material exuded to the surface of said laminate to reside thereon during cure.
Claim 9
Dependent Claim
61 words
In a method for forming laminate carbon-carbon substrate materials which include plies of unidirectional resin impregnated filament tape the improvement comprising: curing said laminate in a platen press by applying pressures of at least about 30 psi without a decrease in pressure during cure and allowing the resin material exuded to the surface of said laminate to reside thereon during cure.
Claim 10
Dependent Claim
171 words
A process for fabricating carbon-carbon fiber reinforced laminate parts having increased load bearing ability along predetermined directions of force to which the part will be subjected during use comprising: (a) laying up alternate plies of carbon or graphite interwoven cloth and unidirectional carbon or graphite filament tape, the number and relative orientation of said tape plies to said cloth plies being determined by the load characteristics and physical size parameters of the part to be fabricated; (b) curing the resulting laid up laminate part of step (a) under pressure conditions of up to about 200 psi, without any reduction in pressure during the cure cycle, while heating the part at temperatures up to at least about 325° F.; (c) pyrolyzing said cured laminate at temperatures of up to about 1500° F.; (d) densifying said pyrolyzed laminate part by liquid impregnation with a carbonizable liquid resin material, curing said impregnated liquid resin material and pyrolyzing same and repeating said densification process to obtain the desired density and strength of the final part.
Claim 11
Dependent Claim
171 words
A process for fabricating carbon-carbon fiber reinforced laminate parts having increased load bearing ability along predetermined directions of force to which the part will be subjected during use comprising: (a) laying up alternate plies of carbon or graphite interwoven cloth and unidirectional carbon or graphite filament tape, the number and relative orientation of said tape plies to said cloth plies being determined by the load characteristics and physical size parameters of the part to be fabricated; (b) curing the resulting laid up laminate part of step (a) under pressure conditions of up to about 200 psi, without any reduction in pressure during the cure cycle, while heating the part at temperatures up to at least about 325° F.; (c) pyrolyzing said cured laminate at temperatures of up to about 1500° F.; (d) densifying said pyrolyzed laminate part by liquid impregnation with a carbonizable liquid resin material, curing said impregnated liquid resin material and pyrolyzing same and repeating said densification process to obtain the desired density and strength of the final part.
Claim 12
Dependent Claim
45 words
The process of claim 8 wherein the curing of said laid up laminate includes initial pressures of about 5 psi with an increase in pressure to about 30 to about 60 psi at the gel point of the resin material initially present in said plies.
Claim 13
Dependent Claim
35 words
The process of claim 8 wherein the resin material present in said plies is phenolic resin and said increase in pressure is effected at temperatures in the range of about 200° to about 240° F.
Claim 14
Dependent Claim
17 words
The process of claim 8 wherein said pressure is applied through use of a platen press apparatus.
Claim 15
Dependent Claim
14 words
The process of claim 8 wherein said interwoven cloth is a PAN based material.
Claim 16
Dependent Claim
14 words
The process of claim 8 wherein said unidirectional tape is a PAN base material.
Claim 17
Dependent Claim
17 words
The process of claim 8 wherein the resin material initially present in said cloth is phenolic resin.
Claim 18
Dependent Claim
20 words
The process of claim 8 wherein the resin material initially present in said unidirectional tape plies is phenolic resin material.
Claim 19
Dependent Claim
15 words
The process of claim 8 wherein said laid up laminate is debulked prior to cure.
Claim 20
Dependent Claim
38 words
The process of claim 8 wherein no bleeder materials are applied to the outside surfaces of said part during cure so as to allow any resin material migrating to said surfaces to remain thereon during the cure step.
Claim 21
Dependent Claim
92 words
The process for producing a laminate of carbon or graphite unidirectional filament tape plies comprising: (a) laying up plies of unidirectional tape either parallel or in a predetermined offset pattern; (b) curing the resultant laid up laminate under pressure conditions of up to about 200 psi, without any reduction in pressure during the cure cycle, which includes heating the part at increasing temperatures reaching at least about 325° F.; (c) pyrolyzing said cured laminate at temperatures of up to about 1500° F.; (d) densifying said pyrolyzed laminate part by liquid impregnation techniques.
Claim 22
Dependent Claim
92 words
The process for producing a laminate of carbon or graphite unidirectional filament tape plies comprising: (a) laying up plies of unidirectional tape either parallel or in a predetermined offset pattern; (b) curing the resultant laid up laminate under pressure conditions of up to about 200 psi, without any reduction in pressure during the cure cycle, which includes heating the part at increasing temperatures reaching at least about 325° F.; (c) pyrolyzing said cured laminate at temperatures of up to about 1500° F.; (d) densifying said pyrolyzed laminate part by liquid impregnation techniques.
Claim 23
Dependent Claim
26 words
The process of claim 18 wherein the cure cycle includes a 45 minute hold period at a temperature of from about 180° to about 200° F.
Claim 24
Dependent Claim
28 words
The process of claim 1 wherein said curing step comprises exertion of pressures of up to about 200 psi, without any drop in pressure during the cure cycle.
Claim 25
Dependent Claim
24 words
The process of claim 1 wherein the curing step comprises heating said laid up laminate at increasing temperatures reaching at least about 325° F.
Claim 26
Dependent Claim
20 words
The process of claim 1 wherein said pyrolyzing step comprises heating said cured laminate at temperatures of about 1500° F.
Claim 27
Dependent Claim
10 words
The carbon-carbon laminate produced by the process of claim 18.
Claim 28
Dependent Claim
58 words
A carbon-carbon fiber reinforced laminate composition fabricated for increased strength in a predetermined direction of load and comprising plies of unidirectional resin impregnated carbon or graphite filament tape formed by a process in which the initial cure of the laid up laminate includes pressures of at least about 30 psi which are not reduced during the cure cycle.
Claim 29
Dependent Claim
58 words
A carbon-carbon fiber reinforced laminate composition fabricated for increased strength in a predetermined direction of load and comprising plies of unidirectional resin impregnated carbon or graphite filament tape formed by a process in which the initial cure of the laid up laminate includes pressures of at least about 30 psi which are not reduced during the cure cycle.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-20 | 1990-10-20 | 1991-04-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-20 | 1994-10-20 | 1995-04-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-20 | 1998-10-20 | 1999-04-21 | $7700.00 | Window Closed / Lapsed |