Reactive atmosphere processing of heavy-metal fluoride glasses
Assignee: The AT&T MVPD Group LLC
•
Filing: 1985-06-21
•
Granted: 1987-04-21
•
Expires: 2005-06-21
Abstract
Abstract Process for treating molten mixtures of fluorozirconate glass to form high purity infrared transparent glass which is essentially free of zirconium fluoride disassociation impurities and anion impurities. The molten mixture or melt is treated with a moisture-free oxygen reactive atmosphere to prevent formation of disassociation impurities or to remove any of these impurities already present in the melt. The melt is also contacted simultaneously or subsequently with a fluorine species reactive gas to remove any oxygen anion impurities formed during the oxygen reactive atmosphere treatment of the melt to thereby provide a glass having complete fluorine stoichiometry and which is free of disassociation and anion impurities.
Inventors
- 👤 Morton Robinson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 22:06
CPC Classifications
C; C03; C03C; C03C3/00; C03C3/32; C03C3/325; Y; Y10; Y10S; Y10S501/00; Y10S501/90; Y10S501/904; Y10S65/00; Y10S65/15; Y10S65/16
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
182 words
A process for treating a molten mixture of fluorozirconate glass to form high purity infrared transparent glass which is essentially free of zirconium fluoride disassociation impurities and anion impurities, said process comprising the steps of: forming a melt of fluorozirconate glass in the presence of an oxygen reactive atmosphere consisting essentially of moisture-free oxygen, said oxygen being present in a sufficient amount to prevent formation of opaque-black disassociation impurities in said melt or remove any of said impurities already present in said melt and wherein oxygen anion impurities are introduced into said glass; contacting said melt with a sufficient amount of a fluorine species reactive gas for a sufficient time to replace substantially all of said oxygen anion impurities with fluoride to provide a melt which is essentially free of disassociation and anion impurities; said fluorine species reactive gas being selected from the group consisting of CF 4 , BF 3 and SF 6 cooling said melt in the presence of said fluorine species reactive gas to form said high purity infraredtransparent glass which is essentially free of disassociation and anion impurities.
Claim 2
Dependent Claim
182 words
A process for treating a molten mixture of fluorozirconate glass to form high purity infrared transparent glass which is essentially free of zirconium fluoride disassociation impurities and anion impurities, said process comprising the steps of: forming a melt of fluorozirconate glass in the presence of an oxygen reactive atmosphere consisting essentially of moisture-free oxygen, said oxygen being present in a sufficient amount to prevent formation of opaque-black disassociation impurities in said melt or remove any of said impurities already present in said melt and wherein oxygen anion impurities are introduced into said glass; contacting said melt with a sufficient amount of a fluorine species reactive gas for a sufficient time to replace substantially all of said oxygen anion impurities with fluoride to provide a melt which is essentially free of disassociation and anion impurities; said fluorine species reactive gas being selected from the group consisting of CF 4 , BF 3 and SF 6 cooling said melt in the presence of said fluorine species reactive gas to form said high purity infraredtransparent glass which is essentially free of disassociation and anion impurities.
Claim 3
Dependent Claim
23 words
A process according to claim 1 wherein said fluorine species reactive gas is CF 4 , BF 3 , or SF 6 .
Claim 4
Dependent Claim
16 words
A process according to claim 1 wherein said fluorine species reactive gas is CF 4 .
Claim 5
Dependent Claim
22 words
A process according to claim 1 wherein said moisture-free oxygen and said fluorine species reactive gas are combined with argon or helium.
Claim 6
Dependent Claim
28 words
A process according to claim 1 wherein said fluorozirconate glass comprises ZrF 4 , BaF 2 and X where X is ThF 4 or a rare earth tri-fluoride.
Claim 7
Dependent Claim
21 words
A process according to claim 5 wherein said melt consists essentially of ZrF 4 , BaF 2 and ThF 4 .
Claim 8
Dependent Claim
23 words
A process according to claim 1 wherein the oxygen reactive gas and the fluorine species reactive gas are contacted simultaneously with said melt.
Claim 9
Dependent Claim
20 words
A process according to claim 1 wherein said oxygen reactive atmosphere is subsequently replaced by said fluorine species reactive atmosphere.
Claim 10
Dependent Claim
18 words
A process according to claim 1 wherein said oxygen reactive atmosphere contains more than 90 volume percent oxygen.
Claim 11
Dependent Claim
24 words
A process according to claim 1 wherein said fluorine species reactive atmosphere contains more than 90 volume percent of said fluorine species reactive gas.
Claim 12
Dependent Claim
23 words
A process according to claim 1 wherein said melt consists essentially of ZrF 4 , BaF 4 , LiF and AlF 3 .
Claim 13
Dependent Claim
86 words
A process for treating a molten mixture of fluorozirconate glass to form a glass which is essentially free of zirconium disassociation impurities, said process comprising the step of: forming a melt of fluorozirconate glass in the presence of an oxygen reactive atmosphere consisting essentially of moisture-free oxygen, said oxygen being present in a sufficient amount to prevent formation of opaque-black disassociation impurities in said melt or remove any of said impurities already present in said melt and wherein oxygen anion impurities are introduced into said glass.
Claim 14
Dependent Claim
86 words
A process for treating a molten mixture of fluorozirconate glass to form a glass which is essentially free of zirconium disassociation impurities, said process comprising the step of: forming a melt of fluorozirconate glass in the presence of an oxygen reactive atmosphere consisting essentially of moisture-free oxygen, said oxygen being present in a sufficient amount to prevent formation of opaque-black disassociation impurities in said melt or remove any of said impurities already present in said melt and wherein oxygen anion impurities are introduced into said glass.
Claim 15
Dependent Claim
84 words
A process for treating a molten mixture of fluorozirconate glass to form a glass which is essentially free of anion impurities, said process comprising the steps of: contacting a melt of fluorozirconate glass with a sufficient amount of a fluorine species reactive gas for a sufficient time to replace substantially all of said oxygen anion impurities with fluoride to provide a melt which is essentially free of disassociation and anion impurities; and cooling said melt in the presence of said fluorine species reactive gas.
Claim 16
Dependent Claim
84 words
A process for treating a molten mixture of fluorozirconate glass to form a glass which is essentially free of anion impurities, said process comprising the steps of: contacting a melt of fluorozirconate glass with a sufficient amount of a fluorine species reactive gas for a sufficient time to replace substantially all of said oxygen anion impurities with fluoride to provide a melt which is essentially free of disassociation and anion impurities; and cooling said melt in the presence of said fluorine species reactive gas.
References Cited (Backward Citations)
US4162908A
Cited
US4141741A
Cited
US4065280A
Cited
US4343638A
Cited
US4341873A
Cited
US4539032A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-20 | 1990-10-20 | 1991-04-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-20 | 1994-10-20 | 1995-04-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-20 | 1998-10-20 | 1999-04-21 | $7700.00 | Window Closed / Lapsed |