Rolling element bearing member
Assignee: General Electric Co
•
Filing: 1985-02-25
•
Granted: 1987-04-21
•
Expires: 2005-02-25
Abstract
Abstract A rolling element bearing member designed for use in a preselected bearing operation, such as a gas turbine engine, which develops a predetermined operating hoop tensile stress in the member includes a hardened layer contiguous with a ductile core having a hardness less than 50 Rockwell C. For example, the hardened layer is a carburized layer of high hardness in the range of 58-66 Rockwell C. The hardened layer has improved resistance to crack initiation and propagation as a result of providing the layer with compressive residual stress in an amount greater than the predetermined operating hoop tensile stress, for example in the range of about 10-60 ksi to a depth up to about 0.06 inch. Such a member is made by providing a member of a metal alloy having the capability of developing such a hardened layer, and then processing the member to develop the layer in the amount of compression.
Inventors
- 👤 Eric N. Bamberger
- 👤 John C. Clark, Jr.
- 👤 Alexander H. Nahm
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 18:29
CPC Classifications
F; F16; F16C; F16C33/00; F16C33/30; Y; Y10; Y10S; Y10S148/00; Y10S148/902; Y10S148/906; Y10S384/00; Y10S384/90; Y10S384/912
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
172 words
A rolling element bearing member for cooperation with a shaft rotating at a preselected speed, the member having a ductile core of a hardness of less than 50 Rockwell C had a hardened layer contiguous with the core, wherein: the member is construction to have a bearing bore in millimeters which, when multiplied by the speed, in revolutions per minute, of the shaft in a preselected bearing operation above a spalling fatigue mode and in a fracture failure mode, equals at least about 2.4 million (DN), the preselected bearing operation developing a predetermined operating hoop tensile stress in the member; the hardened layer has a compressive residual stress greater than the predetermined operating hoop tensile stress whereby the hardened layer maintains a condition of compressive residual stress during the entire preselected bearing operation and whereby the member has improved resistance to crack initiation and propagation during the preselected operation; and the member is constructed of an alloy capable of developing and retaining the hardened layer at least at the compressive residual stress.
Claim 2
Dependent Claim
172 words
A rolling element bearing member for cooperation with a shaft rotating at a preselected speed, the member having a ductile core of a hardness of less than 50 Rockwell C had a hardened layer contiguous with the core, wherein: the member is construction to have a bearing bore in millimeters which, when multiplied by the speed, in revolutions per minute, of the shaft in a preselected bearing operation above a spalling fatigue mode and in a fracture failure mode, equals at least about 2.4 million (DN), the preselected bearing operation developing a predetermined operating hoop tensile stress in the member; the hardened layer has a compressive residual stress greater than the predetermined operating hoop tensile stress whereby the hardened layer maintains a condition of compressive residual stress during the entire preselected bearing operation and whereby the member has improved resistance to crack initiation and propagation during the preselected operation; and the member is constructed of an alloy capable of developing and retaining the hardened layer at least at the compressive residual stress.
Claim 3
Dependent Claim
106 words
The bearing member of claim 1 of an iron base alloy, for use in gas turbine engine operation comprising: a low carbon ductile core having a hardness in the range of less than 50 Rockwell C; a carburized hardened layer of high hardness in the range of 58-66 Rockwell C contiguous with the core; the member being provided with improved resistance to crack initiation and propagation at a bearing DN of at least about 2.4 million as a result of compressive residual stress in the curburized layer, after carburizing and heat treatment, in the range of about 10-60 ksi to a depth of about 0.06 inch.
Claim 4
Dependent Claim
33 words
The bearing member of claim 2 in which the hardened layer is a carburized and heat treatment hardened layer including retained austenite in the amount of no greater than about 6 weight %.
Claim 5
Dependent Claim
10 words
The bearing member of claim 3 constructed of M-50NiL alloy.
Claim 6
Dependent Claim
88 words
In a method for operating the rolling element bearing member of claim 1, comprising the ductile core and the hardened layer, in a preselected bearing operation which develops a predetermined operating hoop tensile stress in the member at a DN of at least about 2.4 million above a spalling fatigue mode and in a fracture failure mode of the member, the step of maintaining the hardened layer under compressive stress during the entire operation of the member whereby the member has improved resistance to crack initiation and propagation.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-20 | 1990-10-20 | 1991-04-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-20 | 1994-10-20 | 1995-04-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-20 | 1998-10-20 | 1999-04-21 | $7700.00 | Window Closed / Lapsed |