Silicon carbide whisker-zirconia reinforced mullite and alumina ceramics

Claim 1

A SiC whisker-reinforced ceramic composite characterized by at least one of increased flexural strength and resistance to fracture, comprising a composite defined by a matrix of mullite or alumina with an adequate concentration of zirconia in a monoclinic phase or a tetragonal phase to provide an increase in at least one of flexural strength and fracture toughness of the SiC whisker-reinforced composite over SiC whisker-reinforced composites provided without the zirconia addition, and with about 5 to 30 vol. % SiC whiskers homogenously dispersed therein, said SiC whiskers having a monocrystalline structure and a size range of about 0.6 micrometer in diameter and a length of about 10 to 80 micrometers with said whiskers being characterized in the composite by causing crack deflection and crack bridging and by whisker pull-out from the matrix when the composite is subjected to crack-forming stresses.

Claim 6

A method for Preparing a SiC whisker-reinforced ceramic composite having at least one of increased flexural strength and resistance to fracture, comprising the steps of forming a homogenous mixture of a matrix consisting essentially of particulate mullite or alumina having added thereto an adequate concentration of zirconia in a monoclinic or a tetragonal phase to provide an increase in at least one of flexural strength and fracture toughness of the SiC whisker-reinforced composite over SiC whisker-reinforced composites obtainable without the zirconia addition, and about 5 to 30 vol. % SiC whiskers having a monocrystalline structure and in a size range of about 0.6 micrometer diameter and a length of about 10 to 80 micrometers, and hot pressing the mixture at a pressure in the range of about 7 to 70 MPa at a temperature of 1400° to 1600° C. for a duration of about 0.2 to 2.0 hours to provide a composite with a density greater than about 94 percent of theoretical density of the ceramic material, zirconia and SiC whiskers, said SiC whiskers being characterized by causing crack deflection and crack bridging and by whisker pull-out from the matrix upon the composite being subjected to crack-forming stresses.

Claim 7

A method for Preparing a SiC whisker-reinforced ceramic composite having at least one of increased flexural strength and resistance to fracture, comprising the steps of forming a homogenous mixture of a matrix consisting essentially of particulate mullite or alumina having added thereto an adequate concentration of zirconia in a monoclinic or a tetragonal phase to provide an increase in at least one of flexural strength and fracture toughness of the SiC whisker-reinforced composite over SiC whisker-reinforced composites obtainable without the zirconia addition, and about 5 to 30 vol. % SiC whiskers having a monocrystalline structure and in a size range of about 0.6 micrometer diameter and a length of about 10 to 80 micrometers, and hot pressing the mixture at a pressure in the range of about 7 to 70 MPa at a temperature of 1400° to 1600° C. for a duration of about 0.2 to 2.0 hours to provide a composite with a density greater than about 94 percent of theoretical density of the ceramic material, zirconia and SiC whiskers, said SiC whiskers being characterized by causing crack deflection and crack bridging and by whisker pull-out from the matrix upon the composite being subjected to crack-forming stresses.