Process for multiple stage autodeposition of organic coatings onto metals

Claim 2

A process for applying a polymeric coating to a metal surface comprising: (a) immersing a metal substrate in an organic coating composition bath, (b) withdrawing the film coated metal substrate from the organic coating composition bath, (c) rinsing the film, (d) repeating the cycle of immersing and rinsing two to ten times, and (e) curing the coated metal substrate.

Claim 3

The process of claim 1 wherein after rinsing the coated metal substrate in water, the coating formed thereon is dried prior to repeating the cycle of immersing, rinsing and drying two to ten times.

Claim 4

The process of claim 1 wherein after repeating the cycle of immersing and rinsing two to ten times, the coated metal substrate does not increase its thickness by more than 20 percent compared to a single dried coating.

Claim 5

The process of claim 2 wherein after repeating the cycle of immersing, rinsing and drying two to ten times, the coated metal substrate does not increase its thickness by more than 20 percent compared to a single dry coating.

Claim 6

The process of claim 1 wherein the metallic substrate is selected from the group consisting of cold rolled steel, phosphatized steel, sand blasted steel, tin free steel, zinc phosphate steel, galvanized steel, iron, zinc, tin-plated steel, tin, copper, aluminum and brass.

Claim 7

The process of claim 1 wherein the coating polymer is derived from vinyl monomers selected from the group consisting of acrylic acid, methacrylic acid, acrylic acid esters, methacrylic acid esters, vinyl amides, nitriles, vinyl esters, vinyl ethers, vinyl halides, vinylidene halides, vinyl aromatic compounds, other ethylenically unsaturated compounds and combinations thereof.

Claim 8

The process of claim 6 wherein the acrylic acid ester is selected from the group consisting of methylacrylate, ethylacrylate, propylacrylate, n-butylacrylate, cyclohexylacrylate and combinations thereof.

Claim 9

The process of claim 6 wherein the methacrylic acid ester is selected from the group consisting of methyl methacrylate, ethyl methacrylate, cyclohexyl methacrylate, phenyl methacrylate, n-butyl methacrylate and combinations thereof.

Claim 10

The process in claim 6 wherein the vinyl amide is selected from the group consisting of acrylamide, N-methyl acrylamide, N,N-dimethylacrylamide, N-butylacrylamide, N-octylacrylamide, methylenebis(acrylamide), methacrylamide, N-methylmethacrylamide, N,N-dimethylmethacrylamide, diacetoneacrylamide and combinations thereof.

Claim 11

The process of claim 6 wherein the nitrile is selected from the group consisting of acrylonitrile, methacrylonitrile, itaconic acid nitrile, fumaronitrile, 1,1-dicyanoethylene and combinations thereof.

Claim 12

The process of claim 6 wherein the vinyl ester is selected from the group consisting of vinyl acetate, vinyl stearate, vinyl butyrate, vinyl propionate and combinations thereof.

Claim 13

The process of claim 6 wherein the vinyl ether is selected from the group consisting of methyl vinyl ether, ethyl vinyl ether, i-propyl vinyl ether, i-butyl vinyl ether, 2-chloroethyl vinyl ether and combinations thereof.

Claim 14

The process of claim 6 wherein the vinyl halide is selected from the group consisting of vinyl chloride, vinyl bromide, vinyl fluoride and combinations thereof.

Claim 15

The process of claim 6 wherein the vinylidene halide is selected from the group consisting of vinylidene chloride, vinyladene fluoride and combinations thereof.

Claim 16

The process of claim 6 wherein the vinyl aromatic compound is selected from the group consisting of styrene, alpha-methylstyrene, p-methylstyrene, p-chlorostyrene, vinyl napthalene, o-methylstyrene, o-chlorostyrene, p-t-butylstyrene and combinations thereof.

Claim 17

The process of claim 6 wherein the ethylenically unsaturated compound is selected from the groups consisting of maleic acid anhydride, fumaric acid, maleic acid esters, fumaric acid esters, allylacrylate, allyl acetate, diallylphthalates, indene, methylindene, vinylcyclohexane, isobutylene, propylene, ethylene and combinations thereof.

Claim 18

The process of claim 1 wherein the coating composition bath has an operating temperature between about 15° C. to about 50° C.

Claim 19

The process of claim 1 wherein the coating composition bath has an operating temperature between about 20° C. and about 45° C.

Claim 20

The process of claim 1 wherein the metal substrate is immersed in the coating composition bath for about 5 seconds to about 10 minutes.

Claim 21

The process of claim 1 wherein the metal substrate is immersed in the coating composition bath for about 10 seconds to about 120 seconds.

Claim 22

The process of claim 1 wherein the coated metal substrate is rinsed in water for about 5 seconds to about 60 seconds.

Claim 23

The process of claim 2 wherein the coated metal substrate is dried at about 20° C. to about 260° C.

Claim 24

The process of claim 2 wherein the coated metal substrate is dried from about 22° C. to about 200° C.

Claim 25

The process of claim 1 wherein the duration of each immersion step is substantially identical.

Claim 26

The process of claim 1 wherein the duration of each immersion step is not substantially identical.

Claim 27

The process of claim 1 wherein the cycle of immersing and rinsing is repeated about 3 to about 7 times.

Claim 28

The process of claim 1 wherein the cycle of immersing and rinsing is repeated about 4 to about 5 times.

Claim 29

The process of claim 2 wherein the cycle of immersing, rinsing and drying is about 3 to about 7 times.

Claim 30

The process of claim 2 wherein the cycle of immersing, rinsing and drying is about 4 to about 5 times.

Claim 31

The process of claim 1 wherein the polymer coating is cured by baking at about 100° C. to about 200° C.

Claim 32

The process of claim 1 wherein the polymer coating is cured by baking at about 180° C. to about 230° C.

Claim 33

The process of claim 1 wherein the polymer coating is from about 0.05 to about 5 mil. thick.

Claim 34

The process of claim 1 wherein the polymer coating is from about 0.1 mil. to about 2 mil. thick.

Claim 35

A process for the autodeposition of a polymeric coating onto a metal substrate comprising: (a) immersing a metal substrate in an organic coating composition bath, capable of abstracting metal ions from said metal surface, comprising a curable film forming polymer which coagulates in the presence of said metal ions to deposit upon the immersed surface to form an organic coating, (b) withdrawing the coated metal surface from the bath, (c) rinsing the organic coating, (d) repeating steps (a) through (c) up to 10 times, and (e) curing the coating.

Claim 36

A process for the autodeposition of a polymeric coating onto a metal substrate comprising: (a) immersing a metal substrate in an organic coating composition bath, capable of abstracting metal ions from said metal surface, comprising a curable film forming polymer which coagulates in the presence of said metal ions to deposit upon the immersed surface to form an organic coating, (b) withdrawing the coated metal surface from the bath, (c) rinsing the organic coating, (d) repeating steps (a) through (c) up to 10 times, and (e) curing the coating.

Claim 37

A process for the autodeposition of a polymeric coating onto a metal substrate comprising: (a) immersing a metal substrate in a coating bath comprising a polymer derived from ethylenically unsaturated compounds, about 5 g/l to about 100 g/l of water, fluoride ions, about 5 g/l to about 10 g/l of an oxidant at a pH from about 1.0 to about 8.5, at a bath temperature of about 15° C. to about 50° C. for at least about 10 seconds, (b) withdrawing the coated metal substrate from the bath, (c) rinsing the organic coating, (d) repeating steps (a) through (c) up to about 10 times such that after drying the thickness of said coating is no more than about 120% the thickness of a dry single immersion coating, (e) curing the coating.

Claim 38

A process for the autodeposition of a polymeric coating onto a metal substrate comprising: (a) immersing a metal substrate in a coating bath comprising a polymer derived from ethylenically unsaturated compounds, about 5 g/l to about 100 g/l of water, fluoride ions, about 5 g/l to about 10 g/l of an oxidant at a pH from about 1.0 to about 8.5, at a bath temperature of about 15° C. to about 50° C. for at least about 10 seconds, (b) withdrawing the coated metal substrate from the bath, (c) rinsing the organic coating, (d) repeating steps (a) through (c) up to about 10 times such that after drying the thickness of said coating is no more than about 120% the thickness of a dry single immersion coating, (e) curing the coating.