Use of immersion tin coating as etch resist
Assignee: Techno Instruments Investments 1983 Ltd
•
Filing: 1985-12-13
•
Granted: 1987-04-14
•
Expires: 2005-12-13
Abstract
Abstract A process is disclosed for manufacturing a circuit board having a metal layer in which a portion of the metal layer is removed by etching. A novel etch resist immersion tin composition is selectively applied to the metal layer to leave areas of coated and uncoated metal followed by etching the metal not coated with the resist. The immersion tin composition is applied as a substantially pore free coating at thicknesses of from about 0.08 to about 0.175 microns. The novel immersion tin composition contains a tin salt and both thiourea compounds and urea compounds.
Inventors
- 👤 Abraham M. Holtzman
- 👤 Joseph Relis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 09:22
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/22; H05K3/24; H05K3/244; C; C23; C23C; C23C18/00; C23C18/16; C23C18/1601; C23C18/1603; C23C18/1605; C23C18/18; C23C18/1803; C23C18/1824; C23C18/1827; C23C18/1831; C23C18/54; H05K3/38; H05K3/382; H05K3/384; H05K2203/00; H05K2203/07; H05K2203/0703; H05K2203/072; H05K3/46; H05K3/4611
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
69 words
A process for manufacturing a device having a metal surface in which a portion of said metal surface is removed by etching comprising selectively applying an etch resist immersion composition to said metal surface to leave areas of coated and uncoated metal followed by etching said metal not coated with said etch resist, said etch resist comprising: (a) a thiourea compound (b) a urea compound (c) a metal salt.
Claim 2
Dependent Claim
69 words
A process for manufacturing a device having a metal surface in which a portion of said metal surface is removed by etching comprising selectively applying an etch resist immersion composition to said metal surface to leave areas of coated and uncoated metal followed by etching said metal not coated with said etch resist, said etch resist comprising: (a) a thiourea compound (b) a urea compound (c) a metal salt.
Claim 3
Dependent Claim
23 words
The process of claim 1 where said etch resist composition further contains: (d) a chelating agent (e) a reducing agent (f) an acid.
Claim 4
Dependent Claim
52 words
The process of claim 1 where said metal salt comprises a tin salt and said composition optionally contains a member selected from the group consisting of a Group VIII metal salt, a Group IVA metal salt with the exception of tin, a Group IIB metal salt or a Group IB metal salt.
Claim 5
Dependent Claim
13 words
The process of claim 1 where said metal salt comprises a stannous salt.
Claim 6
Dependent Claim
14 words
The process of claim 2 where said reducing agent comprises an aldehyde reducing agent.
Claim 7
Dependent Claim
24 words
The process of claim 2 where said acid comprises a mineral acid and said tin salt comprises a stannous salt of a mineral acid.
Claim 8
Dependent Claim
30 words
The process of claim 1 where said thiourea compound and said urea compound comprise a thiourea nucleus and a urea nucleus with the same substituents on each of said nuclei.
Claim 9
Dependent Claim
17 words
The process of claim 7 where said thiourea compound comprises thiourea and said urea compound comprises urea.
Claim 10
Dependent Claim
51 words
The process of claim 4 where said etch resist further contains a compound selected from a member of the group consisting of a Group VIII metal salt, a Group IVA metal salt with the exception of tin, a Group IIB metal salt or a Group IB metal salt or mixtures thereof.
Claim 11
Dependent Claim
35 words
The process of claim 4 where said etch resist further contains a metal salt selected from a member of the group consisting of the salts of iron, cobalt, nickel, mercury or lead or mixtures thereof.
Claim 12
Dependent Claim
12 words
The process of claim 10 where said salt comprises a mercury salt.
Claim 13
Dependent Claim
11 words
The process of claim 4 further comprising a salt of lead.
Claim 14
Dependent Claim
13 words
The process of claim 1 or 2 or 9 further comprising a surfactant.
Claim 15
Dependent Claim
16 words
The process of claims 1 or 2 or 9 further comprising a polyoxyethylene nonyl phenol surfactant.
Claim 16
Dependent Claim
55 words
The process of claims 1 or 2 where the components of said composition are present in the following amounts on a molar basis: (a) about 10 to about 125 parts of a thiourea compound (b) about 10 to about 125 parts of urea compound (c) about 1 to about 15 parts of a metal salt.
Claim 17
Dependent Claim
46 words
The process of claim 15 further comprising the following components on a molar basis: (d) about 5 to about 40 parts of a chelating agent (e) about 5 to about 110 parts of a reducing agent (f) about 1 to about 30 parts of an acid.
Claim 18
Dependent Claim
13 words
The process of claim 15 where said metal salt comprises a tin salt.
Claim 19
Dependent Claim
75 words
The process of claim 17 where said etch resist further contains a compound selected from a member of the group consisting of a Group VIII metal salt, a Group IVA metal salt with the exception of tin, a Group IIB metal salt or a Group IB metal salt or mixtures thereof in an amount from about 2>10 -6 parts to about 55 parts on a molar basis and said metal salt comprises a stannous salt.
Claim 20
Dependent Claim
21 words
The process of claim 4 where said metal surface comprises a metal layer and said device comprises a printed circuit board.
Claim 21
Dependent Claim
14 words
The process of claim 19 where said printed circuit board comprises a multilayer board.
Claim 22
Dependent Claim
15 words
The process of claim 19 where said printed circuit board comprises a single layer board.
Claim 23
Dependent Claim
40 words
The process of claim 19 comprising applying said etch resist to said metal layer through a photoresist layer on said metal layer, a circuit image having been projected onto the said photoresist and developed to selectively expose said metal layer.
Claim 24
Dependent Claim
45 words
The process of claims 19 or 20 or 21 or 22 further comprising applying a solder mask over said coated metal remaining on said electrical device after said etching step, developing said solder mask, inserting circuit components into said circuit and soldering said electrical device.
Claim 25
Dependent Claim
16 words
The process of claim 4 where said etch resist further contains a Group IIB metal salt.
Claim 26
Dependent Claim
32 words
The process of claim 17 where said etch resist further contains a Group IIB metal salt in an amount from about 2×10 -6 parts to about 55 parts on a molar basis.
Claim 27
Dependent Claim
17 words
The process of claims 24 or 25 where said Group IIB salt comprises a salt of mercury.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-13 | 1990-10-13 | 1991-04-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-13 | 1994-10-13 | 1995-04-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-13 | 1998-10-13 | 1999-04-14 | $7700.00 | Window Closed / Lapsed |