Chemical milling processes and etchants therefor
Assignee: Chem-Tronics Inc
•
Filing: 1984-05-01
•
Granted: 1986-05-13
•
Expires: 2004-05-01
Abstract
Abstract Aqueous chemical milling solutions for aluminum and aluminum alloys. These solutions contain a caustic; a nitrate or nitrite; and, optionally, a diol or polyol such as ethylene glycol or glycerin. Chemical milling processes which employ such solutions.
Inventors
- 👤 Donald W. Gross
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 06:31
CPC Classifications
C; C23; C23F; C23F1/00; C23F1/10; C23F1/14; C23F1/32; C23F1/36
Claims Analysis
Total Claims: 38
Claim 1
Independent Claim
60 words
A composition for chemically milling aluminum and aluminum alloys, said composition consisting of a solution of an alkali metal hydroxide or ammonium hydroxide and an ammonium nitrate or alkali metal nitrate in water, said solution containing from 80 to 120 grams of hydroxide and from 42 to 65 grams of nitrate per liter of solution calculated as the sodium salts.
Claim 2
Dependent Claim
60 words
A composition for chemically milling aluminum and aluminum alloys, said composition consisting of a solution of an alkali metal hydroxide or ammonium hydroxide and an ammonium nitrate or alkali metal nitrate in water, said solution containing from 80 to 120 grams of hydroxide and from 42 to 65 grams of nitrate per liter of solution calculated as the sodium salts.
Claim 3
Dependent Claim
27 words
A composition for chemically milling aluminum and aluminum alloys as defined in claim 1 wherein the hydroxide is sodium hydroxide and wherein the nitrate is sodium nitrate.
Claim 4
Dependent Claim
17 words
A composition as defined in claim 2 which contains about 100 grams per liter of sodium hydroxide.
Claim 5
Dependent Claim
17 words
A composition as defined in claim 2 which contains about 50 grams per liter of sodium nitrate.
Claim 6
Dependent Claim
81 words
A composition for chemically milling aluminum and aluminum alloys, said composition consisting of a solution of an alkali metal hydroxide or ammonium hydroxide and an ammonium nitrate or alkali metal nitrate in water and from six to eight percent of a surface smoothness enhancer, said solution containing from 80 to 120 grams of hydroxide and from 42 to 65 grams of nitrate per liter of solution calculated as the sodium salts and said surface smoothness enhancer being ethylene glycol or glycerin.
Claim 7
Dependent Claim
81 words
A composition for chemically milling aluminum and aluminum alloys, said composition consisting of a solution of an alkali metal hydroxide or ammonium hydroxide and an ammonium nitrate or alkali metal nitrate in water and from six to eight percent of a surface smoothness enhancer, said solution containing from 80 to 120 grams of hydroxide and from 42 to 65 grams of nitrate per liter of solution calculated as the sodium salts and said surface smoothness enhancer being ethylene glycol or glycerin.
Claim 8
Dependent Claim
14 words
A composition as defined in claim 5 in which the hydroxide is sodium hydroxide.
Claim 9
Dependent Claim
14 words
A composition as defined in claim 5 in which the nitrate is sodium nitrate.
Claim 10
Dependent Claim
74 words
A composition for chemically milling aluminum and aluminum alloys, said composition consisting of a solution of an alkali metal hydroxide or ammonium hydroxide and an alkali metal nitrate or ammonium nitrite in water, said solution containing from 80 to 120 grams of hydroxide calculated as the sodium salt and an amount of nitrite which is the equivalent of from 42 to 65 grams of nitrate per liter of solution calculated as the sodium salts.
Claim 11
Dependent Claim
74 words
A composition for chemically milling aluminum and aluminum alloys, said composition consisting of a solution of an alkali metal hydroxide or ammonium hydroxide and an alkali metal nitrate or ammonium nitrite in water, said solution containing from 80 to 120 grams of hydroxide calculated as the sodium salt and an amount of nitrite which is the equivalent of from 42 to 65 grams of nitrate per liter of solution calculated as the sodium salts.
Claim 12
Dependent Claim
13 words
A composition as defined in claim 8 wherein the hydroxide is sodium hydroxide.
Claim 13
Dependent Claim
13 words
A composition as defined in claim 8 wherein the nitrite is sodium nitrite.
Claim 14
Independent Claim
99 words
A method of chemically milling an aluminum or aluminum alloy workpiece to impart a selected shape thereto which comprises the steps of: cleaning said workpiece and masking any portions thereof in which the removal of metal is not wanted and thereafter immersing the workpiece for an extended period of time in a chemical milling solution consisting of an alkali metal hydroxide or ammonium hydroxide, an alkali metal nitrate or ammonium nitrate, and water, there being from 80 to 120 grams of hydroxide and from 42 to 65 grams of nitrate calculated as the sodium salts per liter of solution.
Claim 15
Independent Claim
99 words
A method of chemically milling an aluminum or aluminum alloy workpiece to impart a selected shape thereto which comprises the steps of: cleaning said workpiece and masking any portions thereof in which the removal of metal is not wanted and thereafter immersing the workpiece for an extended period of time in a chemical milling solution consisting of an alkali metal hydroxide or ammonium hydroxide, an alkali metal nitrate or ammonium nitrate, and water, there being from 80 to 120 grams of hydroxide and from 42 to 65 grams of nitrate calculated as the sodium salts per liter of solution.
Claim 16
Dependent Claim
31 words
A method of chemically milling an aluminum or aluminum alloy workpiece as defined in claim 11 in which the hydroxide is sodium hydroxide and in which the nitrate is sodium nitrate.
Claim 17
Dependent Claim
22 words
A method as defined in claim 12 in which the chemical milling solution contains about 100 grams per liter of sodium hydroxide.
Claim 18
Dependent Claim
24 words
A method as defined in claim 12 or 13 in which the chemical milling solution contains about 50 grams per liter of sodium nitrate.
Claim 19
Dependent Claim
23 words
A method as defined in claim 11 or in claim 12 in which the workpiece is a copper or zinc containing aluminum alloy.
Claim 20
Dependent Claim
20 words
A method as defined in claim 15 in which the aluminum alloy is an alloy having the nominal composition 6.3Cu-0.3Mn-0.18Zr-0.10V-0.06Ti-Al.
Claim 21
Independent Claim
137 words
A method of chemically milling of an aluminum alloy having the nominal composition 6.3Cu-0.3Mn-0.18Zr-0.10V-0.06Ti-Al extrusion or forging to impart a selected shape thereto which comprises the steps of: cleaning said workpiece and masking any portions thereof in which the removal of metal is not wanted and thereafter immersing the workpiece for an extended period of time in a chemical milling solution consisting of an alkali metal hydroxide or ammonium hydroxide, an alkali metal nitrate or ammonium nitrate, a surface smmothness enhancer, and water, there being from 80 to 120 grams of hydroxide and from 42 to 65 grams of nitrate calculated as the sodium salts per liter of solution and said surface smoothness enhancer being ethylene glycol or glycerin and being present in an amount of six to eight percent based on the volume of the solution.
Claim 22
Independent Claim
137 words
A method of chemically milling of an aluminum alloy having the nominal composition 6.3Cu-0.3Mn-0.18Zr-0.10V-0.06Ti-Al extrusion or forging to impart a selected shape thereto which comprises the steps of: cleaning said workpiece and masking any portions thereof in which the removal of metal is not wanted and thereafter immersing the workpiece for an extended period of time in a chemical milling solution consisting of an alkali metal hydroxide or ammonium hydroxide, an alkali metal nitrate or ammonium nitrate, a surface smmothness enhancer, and water, there being from 80 to 120 grams of hydroxide and from 42 to 65 grams of nitrate calculated as the sodium salts per liter of solution and said surface smoothness enhancer being ethylene glycol or glycerin and being present in an amount of six to eight percent based on the volume of the solution.
Claim 23
Dependent Claim
36 words
A process as defined in claim 11 or in claim 17 in which the chemical milling solution is maintained at a temperature in the range of 190° to 200° F. while the workpiece is immersed therein.
Claim 24
Dependent Claim
24 words
A method as defined in claim 11 or in claim 17 wherein the workpiece has at least one weld or other heat affected zone.
Claim 25
Dependent Claim
31 words
A method as defined in claim 17 in which the workpiece is an extruded Al 2219 aluminum alloy with the aforesaid nominal composition and the surface smoothness enhancer is ethylene glycol.
Claim 26
Independent Claim
113 words
A method of chemically milling an aluminum or aluminum alloy workpiece to impart a selected shape thereto which comprises the steps of: cleaning said workpiece and masking any portions thereof in which the removal of metal is not wanted and thereafter immersing the workpiece for an extended period of time in a chemical milling solution consisting of an alkali metal hydroxide or ammonium hydroxide, an alkali metal nitrite or ammonium nitrite, and water, there being from 80 to 120 grams of hydroxide calculated as the sodium salt and an amount of nitrite which is the equivalent of from 42 to 65 grams of nitrate calculated as the sodium salts per liter of solution.
Claim 27
Independent Claim
113 words
A method of chemically milling an aluminum or aluminum alloy workpiece to impart a selected shape thereto which comprises the steps of: cleaning said workpiece and masking any portions thereof in which the removal of metal is not wanted and thereafter immersing the workpiece for an extended period of time in a chemical milling solution consisting of an alkali metal hydroxide or ammonium hydroxide, an alkali metal nitrite or ammonium nitrite, and water, there being from 80 to 120 grams of hydroxide calculated as the sodium salt and an amount of nitrite which is the equivalent of from 42 to 65 grams of nitrate calculated as the sodium salts per liter of solution.
Claim 28
Dependent Claim
30 words
A method as defined in claim 21 in which the workpiece is a forging of an aluminum alloy having the nominal composition 6.3Cu-0.3Mn-0.18Zr-0.10V-0.06Ti-Al and the surface smoothness enhancer is glycerin.
Claim 29
Dependent Claim
44 words
A process of chem-milling aluminum and aluminum alloys comprising the steps of adding from 45 to 65 g/1 of sodium nitrate to a chem-milling composition which contains sodium hydroxide and continuing the chem-milling until the concentration of dissolved aluminum in the solution is increased.
Claim 30
Dependent Claim
44 words
A process of chem-milling aluminum and aluminum alloys comprising the steps of adding from 45 to 65 g/1 of sodium nitrate to a chem-milling composition which contains sodium hydroxide and continuing the chem-milling until the concentration of dissolved aluminum in the solution is increased.
Claim 31
Dependent Claim
37 words
In a chem-milling composition comprising sodium hydroxide as the principal active ingredient and a diol or triol, the improvement which comprises the addition of from 45 to 65 g/1 of sodium nitrate per liter of chem-milling solution.
Claim 32
Dependent Claim
37 words
In a chem-milling composition comprising sodium hydroxide as the principal active ingredient and a diol or triol, the improvement which comprises the addition of from 45 to 65 g/1 of sodium nitrate per liter of chem-milling solution.
Claim 33
Dependent Claim
35 words
The composition of claim 24 wherein the etching rate of the chem-milling composition is increased and the tank life of the composition is increased as compared to a similar composition not containing the sodium nitrate.
Claim 34
Dependent Claim
20 words
A composition as defined in claim 5 in which the surface smoothness enhancer constitutes from 7.1 to 10 volume percent.
Claim 35
Dependent Claim
20 words
A composition as defined in claim 5 in which the surface smoothness enhancer constitutes from 6 to 8 volume percent.
Claim 36
Dependent Claim
36 words
A method of chemically milling an aluminum or aluminum alloy workpiece as defined in claim 11 wherein the workpiece is fabricated of an aluminum alloy having a nominal composition of: 6.3Cu-0.3Mn-0.18Zr-0.10V-0.06Ti-Al, 4.4Cu-0.6Mn-1.5Mg-Al, 1.6Cu-2.5Mg-5.6Zn-0.23Cr-AI, 0.6Cu-3.3Mg-0.18Cr-4.3Zn-0.20Mn-Al, or 0.30Cu-0.6Si-1.OMg-0.20Cr-Al.
Claim 37
Dependent Claim
34 words
A method as defined in claim 11 wherein the temperature of said chemical milling solution is maintained in the range of 190°-200° F. during the period in which metal is removed from said workpiece.
Claim 38
Dependent Claim
19 words
A composition as defined in claim 24 in which the diol is ethylene glycol and the triol is glycerin.
References Cited (Backward Citations)
US2472304A
Cited
US2671717A
Cited
US2673143A
Cited
US2795491A
Cited
US3039909A
Cited
US2942955A
Cited
US3039910A
Cited
US3061494A
Cited
US3134702A
Cited
US3356550A
Cited
US3300349A
Cited
US3557000A
Cited
US3690949A
Cited
JPS4828541A
Cited
US3802973A
Cited
US3957553A
Cited
DE2439202A1
Cited
US4113549A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-05-12 | 1989-11-11 | 1990-05-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-05-12 | 1993-11-11 | 1994-05-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-05-12 | 1997-11-11 | 1998-05-13 | $7700.00 | Window Closed / Lapsed |