Repair of a member having a projection
Assignee: General Electric Co
•
Filing: 1985-06-13
•
Granted: 1987-04-14
•
Expires: 2005-06-13
Abstract
Abstract Repair or replacement of a projection such as a labyrinth seal tooth of a metal having relatively poor weldability characteristics is accomplished by removing a portion or possibly all of the seal tooth down to a pedestal and then metallurgically bonding as by fusing to the pedestal a second metal characterized as having good weldability characteristics when diluted with the first metal, and age hardenable with an aging heat treatment with which the first metal also is age hardenable.
Inventors
- 👤 Bertrand G. Robins
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 03:10
CPC Classifications
B; B23; B23P; B23P6/00; B23P6/002; B23P6/007; B23K; B23K35/00; B23K35/22; B23K35/24; B23K35/30; B23K35/3033; B23K35/304; B23K9/00; B23K9/04; C; C22; C22F; C22F1/00; C22F1/10; E; E01; E01B; E01B5/00; F; F16; F16J; F16J15/00; F16J15/44; F16J15/447; F16J15/453; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49718; Y10T29/49721; Y10T29/49723; Y10T29/49725; Y10T29/49726; Y10T29/49732
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
226 words
In a method of repairing a metal article comprising a support and a projection of an operating height and shape projecting from a first surface of the support, the projection being of a first metal characterized as having relatively poor weldability and repair weldability characteristics, including poor weld flow and crack sensitivity, the method including removing at least a portion of the projection and replacing the removed portion with additional material, the steps of: mechanically removing at least a portion of the operating height of the projection to provide a projection pedestal having a base location extending in a range up to about 0.1" away from the first surface; providing an additional material of a second metal characterized as having good weldability and repair weldability characteristics when diluted with the first metal and age hardenable with an aging heat treatment with which the first metal also is age hardenable; metallurgically bonding the additional material directly to the base location, without prior melting of the base location, at a bond juncture zone to replace at least the removed portion, the additional material after bonding being in a condition which is substantially a solid solution, to provide a repair support/projection preform; subjecting the preform to the aging heat treatment; and then removing a portion of the additional material to regenerate the projection in the operating height and shape.
Claim 2
Dependent Claim
226 words
In a method of repairing a metal article comprising a support and a projection of an operating height and shape projecting from a first surface of the support, the projection being of a first metal characterized as having relatively poor weldability and repair weldability characteristics, including poor weld flow and crack sensitivity, the method including removing at least a portion of the projection and replacing the removed portion with additional material, the steps of: mechanically removing at least a portion of the operating height of the projection to provide a projection pedestal having a base location extending in a range up to about 0.1" away from the first surface; providing an additional material of a second metal characterized as having good weldability and repair weldability characteristics when diluted with the first metal and age hardenable with an aging heat treatment with which the first metal also is age hardenable; metallurgically bonding the additional material directly to the base location, without prior melting of the base location, at a bond juncture zone to replace at least the removed portion, the additional material after bonding being in a condition which is substantially a solid solution, to provide a repair support/projection preform; subjecting the preform to the aging heat treatment; and then removing a portion of the additional material to regenerate the projection in the operating height and shape.
Claim 3
Dependent Claim
13 words
The method of claim 1 in which the projection is a seal tooth.
Claim 4
Dependent Claim
20 words
The method of claim 2 in which the first metal is A286 Alloy, and the second metal is IN718 Alloy.
Claim 5
Dependent Claim
35 words
The method of claim 1 in which a portion of the first surface is removed adjacent to the projection pedestal, along with additional material, to position the bond juncture zone more remote from the support.
Claim 6
Dependent Claim
90 words
The method of claim 1 of repairing a metal article in which the projection is integral with and projecting from the support at a fillet with the first surface, the projection, and the support being of the first metal wherein: a major portion of the projection is removed to provide the projection pedestal; the additional material is provided in wire form; and the additional material is deposited by melting the wire and fusing the molten wire material with the base location and projection pedestal to provide the repair support/projection preform.
Claim 7
Dependent Claim
136 words
A labyrinth gas seal comprising a support and at least one seal tooth projecting from a surface of the support wherein: the tooth is a composite of a first metal in the form of a tooth pedestal integral with and projecting in a range of up to about 0.1" from a surface of the support and a second metal metallurgically bonded at a bond juncture zone directly to the tooth pedestal which exhibits no prior melting of the tooth pedestal at the bond juncture zone; the first metal is characterized as having relatively poor weldability and repair weldability characteristics and the second metal is characterized as having good weldability and repair weldability characteristics when diluted with the first metal and age hardenable with an aging heat treatment with which the first metal also is age hardenable.
Claim 8
Dependent Claim
136 words
A labyrinth gas seal comprising a support and at least one seal tooth projecting from a surface of the support wherein: the tooth is a composite of a first metal in the form of a tooth pedestal integral with and projecting in a range of up to about 0.1" from a surface of the support and a second metal metallurgically bonded at a bond juncture zone directly to the tooth pedestal which exhibits no prior melting of the tooth pedestal at the bond juncture zone; the first metal is characterized as having relatively poor weldability and repair weldability characteristics and the second metal is characterized as having good weldability and repair weldability characteristics when diluted with the first metal and age hardenable with an aging heat treatment with which the first metal also is age hardenable.
Claim 9
Dependent Claim
20 words
The seal of claim 6 in which the first metal is A286 Alloy, and the second metal is IN718 Alloy.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-13 | 1990-10-13 | 1991-04-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-13 | 1994-10-13 | 1995-04-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-13 | 1998-10-13 | 1999-04-14 | $7700.00 | Window Closed / Lapsed |