Terpolymers having the character of hydrogels
Assignee: Czech Academy of Sciences
•
Filing: 1986-01-28
•
Granted: 1987-04-07
•
Expires: 2006-01-28
Abstract
Abstract This invention relates to terpolymers which are capable of forming hydrogels having very good compatibility with living tissues and may be used as substitutes for damaged tissues, as in the form of implants and various prostheses. The terpolymers are comprised of an oligourethane having an average molecular weight from 1200 to 3000, 2-hydroxyethyl(meth)acrylate or 2-hydroxypropyl(meth)acrylate, and N-vinylpyrrolidone.
Inventors
- 👤 Slavko Hudecek
- 👤 Iva Hudeckova
- 👤 Jaroslava Otoupalova
- 👤 Pavel Cefelin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 04:13
CPC Classifications
C; C08; C08F; C08F226/00; C08F226/06; C08F226/10; A; A61; A61L; A61L27/00; A61L27/14; A61L27/16; C08F220/00; C08F220/02; C08F220/10; C08F220/20
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
131 words
A terpolymer capable of forming a hydrogel made by polymerizing (1) from about 5 to about 20 weight percent of an oligourethane having a terminal double bond and an average molecular weight of about 1200 to about 3000, of the general formula ##STR3## wherein R is a diol residue, R' is a diisocyanate residue, X is H or CH 3 , and n is an integer selected from the group consisting of those integers which result in a molecular weight for the oligourethane within the range of about 1200 to abut 3000; (2) from about 5 to about 60 weight percent of a monomer selected from the group consisting of 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl acrylate, and 2-hydroxypropyl methacrylate; and (3) from about 30 to about 90 weight percent of N-vinylpyrrolidone.
Claim 2
Dependent Claim
131 words
A terpolymer capable of forming a hydrogel made by polymerizing (1) from about 5 to about 20 weight percent of an oligourethane having a terminal double bond and an average molecular weight of about 1200 to about 3000, of the general formula ##STR3## wherein R is a diol residue, R' is a diisocyanate residue, X is H or CH 3 , and n is an integer selected from the group consisting of those integers which result in a molecular weight for the oligourethane within the range of about 1200 to abut 3000; (2) from about 5 to about 60 weight percent of a monomer selected from the group consisting of 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl acrylate, and 2-hydroxypropyl methacrylate; and (3) from about 30 to about 90 weight percent of N-vinylpyrrolidone.
Claim 3
Dependent Claim
27 words
A hydrogel comprising the terpolymer of claim 1 and from about 40 to about 85 weight percent of water, based on the total weight of the hydrogel.
Claim 4
Independent Claim
153 words
A method for preparing a terpolymer capable of forming a hydrogel comprising polymerizing under free-radical polymerization conditions, (1) from about 5 to about 20 weight percent of an oligourethane having a terminal double bond and an average molecular weight of about 1200 to about 3000, of the general formula ##STR4## wherein R is a diol residue, R' is a diisocyanate residue, X is H or CH 3 , and n is an integer selected from the group consisting of those integers which result in a molecular weight for the oligourethane within the range of about 1200 to about 3000; (2) from about 5 to about 60 weight percent of a monomer selected from the group consisting of 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl acrylate, and 2-hydroxypropyl methacrylate; and (3) from about 30 to about 90 weight percent of N-vinylpyrrolidone until at least about 70% by weight of the monomers have been converted into terpolymer.
Claim 5
Independent Claim
153 words
A method for preparing a terpolymer capable of forming a hydrogel comprising polymerizing under free-radical polymerization conditions, (1) from about 5 to about 20 weight percent of an oligourethane having a terminal double bond and an average molecular weight of about 1200 to about 3000, of the general formula ##STR4## wherein R is a diol residue, R' is a diisocyanate residue, X is H or CH 3 , and n is an integer selected from the group consisting of those integers which result in a molecular weight for the oligourethane within the range of about 1200 to about 3000; (2) from about 5 to about 60 weight percent of a monomer selected from the group consisting of 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl acrylate, and 2-hydroxypropyl methacrylate; and (3) from about 30 to about 90 weight percent of N-vinylpyrrolidone until at least about 70% by weight of the monomers have been converted into terpolymer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-06 | 1990-10-06 | 1991-04-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-06 | 1994-10-06 | 1995-04-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-06 | 1998-10-06 | 1999-04-07 | $7700.00 | Window Closed / Lapsed |