Cloth covered pinch welt and method for making same
Assignee: ALPHA PROFILES Inc
•
Filing: 1986-07-21
•
Granted: 1987-04-07
•
Expires: 2006-07-21
Abstract
Abstract The present invention teaches a cloth covered pinch welt comprising a flexible, thermoplastic polymeric substrate extruded about a reinforcing member having a layer of partially embedded open cell foam material bonded to the polymeric substrate and wherein a cloth covering is bonded to the foam material. In addition a method for manufacturing the cloth covered pinch welt disclosed herein is also taught.
Inventors
- 👤 Daniel W. Bowers
- 👤 Donald L. Wisser
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 11:35
CPC Classifications
B; B29; B29C; B29C48/00; B29C48/001; B29C48/0021; B32; B32B; B32B5/00; B32B5/22; B32B5/24; B32B5/245; B29C48/03; B29C48/07; B29C48/15; B29C48/154; B29C63/00; B29C63/02; B29C63/04; B29C63/044; B29C65/00; B29C65/48; B29C65/52; B32B27/00; B32B27/06; B32B27/065; B32B27/12; B32B5/18; B32B7/00; B32B7/04; B32B7/12; B60; B60J; B60J10/00; B60J10/15; B60J10/18; B60J10/30; B60J10/32; B60J10/33; C; C09; C09J; C09J5/00; C09J5/06; B29L; B29L2031/00; B29L2031/26; B32B2605/00; B32B2605/08; C09J2400/00; C09J2400/20; C09J2400/24; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/2419; Y10T428/24198; Y10T428/24215; Y10T428/24231; Y10T428/24777; Y10T428/24785; Y10T428/249921; Y10T428/249953; Y10T428/24996; Y10T428/249982; Y10T428/249984; Y10T428/249987; Y10T428/249991; Y10T428/249992
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
106 words
A method for manufacturing a cloth covered polymeric pinch welt comprising: a. hot extruding a thermoplastic polymeric material about a reinforcing member thereby forming a polymeric coated substrate; b. contacting said hot polymeric coated substrate, with a flexible open cell foam backed cloth material, wherein the foam is caused to embed into the surface of the polymeric substrate, thereby bonding said cloth material to said polymeric material forming a cloth covered polymeric substrate; c. cooling said bonded cloth covered polymeric substrate to below the melt temperature of the polymeric material to solidify the bond; d. forming said cooled, bonded cloth covered substrate to the desired shape.
Claim 2
Independent Claim
106 words
A method for manufacturing a cloth covered polymeric pinch welt comprising: a. hot extruding a thermoplastic polymeric material about a reinforcing member thereby forming a polymeric coated substrate; b. contacting said hot polymeric coated substrate, with a flexible open cell foam backed cloth material, wherein the foam is caused to embed into the surface of the polymeric substrate, thereby bonding said cloth material to said polymeric material forming a cloth covered polymeric substrate; c. cooling said bonded cloth covered polymeric substrate to below the melt temperature of the polymeric material to solidify the bond; d. forming said cooled, bonded cloth covered substrate to the desired shape.
Claim 3
Dependent Claim
14 words
The method of claim 1, wherein the polymeric material is a flexible polyvinyl chloride.
Claim 4
Dependent Claim
31 words
The method of claim 2 wherein the cloth is a brushed nylon knit or polyester fabric; having at least one surface coated with an open cell foam urethane polyester based material.
Claim 5
Dependent Claim
13 words
The method of claim 3 wherein the reinforcing member is a metal carrier.
Claim 6
Dependent Claim
36 words
The method of claim 4 wherein the bonded, cloth covered substrate is cooled to below 26.6° C. (80° F.) and is formed into its final shape by passing the coated article through a roll forming process.
Claim 7
Dependent Claim
38 words
A cloth covered pinch welt comprising a flexible, thermoplastic polymeric substrate extruded about a reinforcing member, a layer of flexible open cell foam material partially imbedded into the polymeric substrate, said foam covered with a layer of cloth.
Claim 8
Dependent Claim
38 words
A cloth covered pinch welt comprising a flexible, thermoplastic polymeric substrate extruded about a reinforcing member, a layer of flexible open cell foam material partially imbedded into the polymeric substrate, said foam covered with a layer of cloth.
Claim 9
Dependent Claim
13 words
The article of claim 6 wherein the polymeric substrate is flexible polyvinyl chloride.
Claim 10
Dependent Claim
11 words
The article of claim 7 wherein the reinforcing member is metallic.
Claim 11
Dependent Claim
12 words
The article of claim 7 wherein the cloth covering is brushed nylon.
Claim 12
Dependent Claim
19 words
The article of claim 7 wherein the open cell foam is a flexible open cell urethane, polyester based material.
Claim 13
Independent Claim
104 words
A method for manufacturing a cloth covered polymeric pinch welt comprising: a. hot extruding a thermoplastic polymeric material about a reinforcing member thereby forming a polymeric substrate; b. contacting said hot polymeric substrate, with a flexible open cell foam backed cloth material, wherein the temperature of the substrate exceeds the melt temperature of the foam, thereby melting said foam and bonding said foam backed cloth to said polymeric material forming a cloth covered substrate; c. cooling said bonded cloth covered polymeric substrate to below the melt temperature of the foam urethane backing; d. forming said cooled, bonded cloth covered substrate to the desired shape.
Claim 14
Independent Claim
104 words
A method for manufacturing a cloth covered polymeric pinch welt comprising: a. hot extruding a thermoplastic polymeric material about a reinforcing member thereby forming a polymeric substrate; b. contacting said hot polymeric substrate, with a flexible open cell foam backed cloth material, wherein the temperature of the substrate exceeds the melt temperature of the foam, thereby melting said foam and bonding said foam backed cloth to said polymeric material forming a cloth covered substrate; c. cooling said bonded cloth covered polymeric substrate to below the melt temperature of the foam urethane backing; d. forming said cooled, bonded cloth covered substrate to the desired shape.
Claim 15
Dependent Claim
48 words
A cloth covered pinch welt comprising a flexible, thermoplastic polymeric substrate extruded about a reinforcing member, a layer of partially melted flexible open cell foam material covered with a layer of cloth wherein said melted foam acts as the adhesive to bond the cloth to the polymeric substrate.
Claim 16
Dependent Claim
48 words
A cloth covered pinch welt comprising a flexible, thermoplastic polymeric substrate extruded about a reinforcing member, a layer of partially melted flexible open cell foam material covered with a layer of cloth wherein said melted foam acts as the adhesive to bond the cloth to the polymeric substrate.
Claim 17
Independent Claim
112 words
A method for manufacturing a cloth covered polymeric pinch welt comprising a. hot extruding a thermoplastic polymeric material about a reinforcing member thereby forming a polymeric substrate; b. heating the flexible open cell foam backing of a foam backed cloth material to cause a portion of said foam material to melt; c. contacting said hot polymeric substrate with said heated partially melted surface of said foam backed cloth material, thereby bonding said cloth material to said polymeric material forming a cloth covered substrate; d. cooling said bonded cloth covered polymeric substrate to below the melt temperature of the foam backing; e. forming said cool bonded cloth covered substrate to the desired shape.
Claim 18
Independent Claim
112 words
A method for manufacturing a cloth covered polymeric pinch welt comprising a. hot extruding a thermoplastic polymeric material about a reinforcing member thereby forming a polymeric substrate; b. heating the flexible open cell foam backing of a foam backed cloth material to cause a portion of said foam material to melt; c. contacting said hot polymeric substrate with said heated partially melted surface of said foam backed cloth material, thereby bonding said cloth material to said polymeric material forming a cloth covered substrate; d. cooling said bonded cloth covered polymeric substrate to below the melt temperature of the foam backing; e. forming said cool bonded cloth covered substrate to the desired shape.
References Cited (Backward Citations)
US3535181A
Cited
US4003777A
Cited
US3849174A
Cited
US3989869A
Cited
US4104430A
Cited
US4221623A
Cited
US4378396A
Cited
US4370374A
Cited
US4381273A
Cited
US4493871A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-04-06 | 1990-10-06 | 1991-04-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-04-06 | 1994-10-06 | 1995-04-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-04-06 | 1998-10-06 | 1999-04-07 | $7700.00 | Window Closed / Lapsed |