Method for the formation of a titanium or zirconium compound coating
Assignee: Toshiba Corp
•
Filing: 1986-06-02
•
Granted: 1987-03-31
•
Expires: 2006-06-02
Abstract
Abstract A method for forming on the surface of a sintered article of silicon nitride type ceramic a coating film of a compound containing titanium or zirconium is disclosed. This metal compound coating is easily and inexpensively obtained by placing a metal-containing substance such as, for example, titanium dioxide in contact with a sintered article of silicon nitride type ceramic and sintering the resultant composite in a non-oxidative atmosphere.
Inventors
- 👤 Akio Sayano
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 20:59
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/22; C23C16/30; C04; C04B; C04B41/00; C04B41/009; C04B41/45; C04B41/50; C04B41/51; C04B41/5133; C04B41/80; C04B41/81; C04B41/85; C04B41/88
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
79 words
A method for the formation of a coating of a titanium or zirconium nitride on the surface of a sintered silicon nitride ceramic article, characterized by the steps of depositing a coating of titanium or zirconium or a substance containing titanium or zirconium on the surface of said sintered ceramic article and sintering the resultant composite in a non-oxidative atmosphere to produce a reaction between the surface and the coating to form said coating of titanium or zirconium nitride.
Claim 2
Independent Claim
79 words
A method for the formation of a coating of a titanium or zirconium nitride on the surface of a sintered silicon nitride ceramic article, characterized by the steps of depositing a coating of titanium or zirconium or a substance containing titanium or zirconium on the surface of said sintered ceramic article and sintering the resultant composite in a non-oxidative atmosphere to produce a reaction between the surface and the coating to form said coating of titanium or zirconium nitride.
Claim 3
Dependent Claim
23 words
A method according to claim 1, wherein said substance to be placed in contact with said sintered silicon nitride ceramic article contains titanium.
Claim 4
Dependent Claim
14 words
A method according to claim 2, wherein said substance containing titanium is titanium dioxide.
Claim 5
Independent Claim
24 words
A method according to any of claims 1-3, wherein said non-oxidative atmosphere is formed of a mixed gas of nitrogen or argon and hydrogen.
References Cited (Backward Citations)
US2715593A
Cited
US3394026A
Cited
US3510343A
Cited
US4159357A
Cited
US4346147A
Cited
JPS57106586A
Cited
US4462817A
Cited
US4462818A
Cited
US4462816A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-03-30 | 1990-09-29 | 1991-03-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-03-30 | 1994-09-29 | 1995-03-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-03-30 | 1998-09-29 | 1999-03-31 | $7700.00 | Window Closed / Lapsed |