Method for forming a film of dielectric material on an electric component
Assignee: International Business Machines Corp
•
Filing: 1986-03-11
•
Granted: 1987-03-31
•
Expires: 2006-03-11
Abstract
Abstract Thin dielectric films are formed on an electronic component by in situ curing a polymerizable oligomer which is end capped with vinyl and/or acetylenic end groups. The polymerizable oligomers are comprised of polyamic acids, polyamic esters, polyisoimides, and mixtures thereof which can be crosslinked to form a three-dimensional network via sites at the vinyl or acetylenic end groups and sites at carbonyl groups contained within the polymeric chain. Use of these polymerizable oligomers permits utilization of low temperature methods of curing which reduce intrinsic and extrinsic stress within the cured dielectric film.
Inventors
- 👤 Constance J. Araps
- 👤 Steven M. Kandetzke
- 👤 Mark A. Takacs
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 12:16
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/63; H10P14/6326; H10P14/6342; H10P14/65; H10P14/6516; H10P14/6536; H10P14/68; H10P14/683
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
84 words
A method for forming a thin film of a dielectric material on an electronic component which comprises applying thereto a layer of a polymerizable oligomer selected from the group consisting of polyamic acids, the corresponding polyamic esters, the corresponding polyisoimides, or mixtures thereof, wherein the end groups of the polymerizable oligomer are end-capped with a vinyl or acetylenic end group; and curing the layer of polymerizable oligomer at temperatures below about 300° C., whereby the resulting cured polyimide exhibits low extrinsic and intrinsic stress.
Claim 2
Independent Claim
84 words
A method for forming a thin film of a dielectric material on an electronic component which comprises applying thereto a layer of a polymerizable oligomer selected from the group consisting of polyamic acids, the corresponding polyamic esters, the corresponding polyisoimides, or mixtures thereof, wherein the end groups of the polymerizable oligomer are end-capped with a vinyl or acetylenic end group; and curing the layer of polymerizable oligomer at temperatures below about 300° C., whereby the resulting cured polyimide exhibits low extrinsic and intrinsic stress.
Claim 3
Independent Claim
167 words
A method for forming superposed levels of metallurgy on an integrated circuit array comprising a semiconductor substrate, a dielectric layer on the substrate, a plurality of semiconductor devices integrated on the substrate, and a first electrical conductor pattern on the dielectric layer electrically connected to at least one of the semiconductor devices, comprising: (A) coating the substrate with a layer of a polymerizable oligomer selected from the group consisting of polyamic acids, polyamic esters thereof, polyisoimides, or mixtures thereof, wherein the end groups of the polymerizable oligomer are end capped with a vinyl or acetylenic end group; (B) lithographically forming openings in the coating in a pattern exposing a predetermined portion of the first electrical conductor or pattern; (C) curing the layer of polymerizable oligomer at temperatures below about 300° C. whereby the resulting cured polyimide exhibits low extrinsic and intrinsic stress; (D) forming a second electrical conductor pattern in electrical connection through the openings to the first conductor pattern; and (E) passivating the integrated circuit array.
Claim 4
Independent Claim
167 words
A method for forming superposed levels of metallurgy on an integrated circuit array comprising a semiconductor substrate, a dielectric layer on the substrate, a plurality of semiconductor devices integrated on the substrate, and a first electrical conductor pattern on the dielectric layer electrically connected to at least one of the semiconductor devices, comprising: (A) coating the substrate with a layer of a polymerizable oligomer selected from the group consisting of polyamic acids, polyamic esters thereof, polyisoimides, or mixtures thereof, wherein the end groups of the polymerizable oligomer are end capped with a vinyl or acetylenic end group; (B) lithographically forming openings in the coating in a pattern exposing a predetermined portion of the first electrical conductor or pattern; (C) curing the layer of polymerizable oligomer at temperatures below about 300° C. whereby the resulting cured polyimide exhibits low extrinsic and intrinsic stress; (D) forming a second electrical conductor pattern in electrical connection through the openings to the first conductor pattern; and (E) passivating the integrated circuit array.
Claim 5
Dependent Claim
21 words
The method of claim 2 which comprises repeating steps (A) through (D) until the desired levels of conductor patterns are obtained.
Claim 6
Independent Claim
94 words
A method of forming a thin film of a dielectric material on an electronic component comprising: (A) applying to the electronic component a layer comprising a polymerizable oligomer selected from the group consisting of polyamic acids, the corresponding polyamic esters, and the corresponding polyisoimides or mixtures thereof, wherein the end groups of the polymerizable oligomer are end capped with a vinyl or acetylenic end group; and (B) curing the layer of polymerizable oligomer upon said electronic component at temperatures below about 300° C., whereby the resulting crosslinked polyimide exhibits low extrinsic and intrinsic stress.
Claim 7
Independent Claim
94 words
A method of forming a thin film of a dielectric material on an electronic component comprising: (A) applying to the electronic component a layer comprising a polymerizable oligomer selected from the group consisting of polyamic acids, the corresponding polyamic esters, and the corresponding polyisoimides or mixtures thereof, wherein the end groups of the polymerizable oligomer are end capped with a vinyl or acetylenic end group; and (B) curing the layer of polymerizable oligomer upon said electronic component at temperatures below about 300° C., whereby the resulting crosslinked polyimide exhibits low extrinsic and intrinsic stress.
Claim 8
Dependent Claim
14 words
The method of claim 4 wherein said curing is accomplished using a catalytic technique.
Claim 9
Dependent Claim
24 words
The method of claim 5 wherein said curing is accomplished using a combined dry/cure cycle ranging between about 85° C. and about 300° C.
Claim 10
Dependent Claim
12 words
The method of claim 4 wherein said curing is accomplished using radiation.
Claim 11
Dependent Claim
14 words
The method of claim 4 wherein said polymerizable oligomer is comprised of said polyisoimide.
Claim 12
Dependent Claim
14 words
The method of claim 8 wherein said curing is accomplished using a catalytic technique.
Claim 13
Dependent Claim
12 words
The method of claim 9 wherein the catalyst utilized is a peroxide.
Claim 14
Dependent Claim
24 words
The method of claim 10 wherein said curing is accomplished using a combined dry/cure cycle ranging between about 85° C. and about 300° C.
Claim 15
Independent Claim
77 words
A method of forming a thin film of a dielectric material on an electronic component comprising: (A) applying to said electronic component a layer comprising a polymerizable oligomer selected from the group consisting of polyamic acids, the corresponding polyamic esters, and the corresponding polyisoimides or mixtures thereof, wherein the end groups of the polymerizable oligomer are end capped with a vinyl or acetylenic end group; and (B) curing said layer of polymerizable oligomer upon said electronic component.
Claim 16
Independent Claim
77 words
A method of forming a thin film of a dielectric material on an electronic component comprising: (A) applying to said electronic component a layer comprising a polymerizable oligomer selected from the group consisting of polyamic acids, the corresponding polyamic esters, and the corresponding polyisoimides or mixtures thereof, wherein the end groups of the polymerizable oligomer are end capped with a vinyl or acetylenic end group; and (B) curing said layer of polymerizable oligomer upon said electronic component.
Claim 17
Dependent Claim
20 words
The method of claim 12 wherein the combined dry/cure temperature cycle ranges from about 85° C. to about 400° C.
Claim 18
Dependent Claim
20 words
The method of claim 12 wherein said polyamic acid exhibits a molecular weight ranging from about 2,500 to about 3,000.
Claim 19
Independent Claim
161 words
A method for forming superposed levels of metallurgy on an integrated circuit array comprising a semiconductor substrate, a dielectric layer on the substrate, a plurality of semiconductor devices integrated on the substrate, and a first electrical conductor pattern on the dielectric layer electrically connected to at least one of the semiconductor devices, comprising: (A) coating the substrate with a layer of a polymerizable oligomer selected from the group consisting of polyamic acids, the corresponding polyamic esters, the corresponding polyisoimides or mixtures thereof, wherein the end groups of the polymerizable oligomer are end capped with a vinyl or acetylenic end group; (B) lithographically forming openings in the coating in a pattern exposing a predetermined portion of the first electrical conductor pattern; (C) curing the layer of polymerizable oligomer using cure temperatures as high as about 400° C.; (D) forming a second electrical conductor pattern in electrical connection through the openings to the first conductor pattern; and (E) passivating the integrated circuit array.
Claim 20
Independent Claim
161 words
A method for forming superposed levels of metallurgy on an integrated circuit array comprising a semiconductor substrate, a dielectric layer on the substrate, a plurality of semiconductor devices integrated on the substrate, and a first electrical conductor pattern on the dielectric layer electrically connected to at least one of the semiconductor devices, comprising: (A) coating the substrate with a layer of a polymerizable oligomer selected from the group consisting of polyamic acids, the corresponding polyamic esters, the corresponding polyisoimides or mixtures thereof, wherein the end groups of the polymerizable oligomer are end capped with a vinyl or acetylenic end group; (B) lithographically forming openings in the coating in a pattern exposing a predetermined portion of the first electrical conductor pattern; (C) curing the layer of polymerizable oligomer using cure temperatures as high as about 400° C.; (D) forming a second electrical conductor pattern in electrical connection through the openings to the first conductor pattern; and (E) passivating the integrated circuit array.
Claim 21
Independent Claim
144 words
A method of forming a multilayer structure wherein at least one polymeric insulating layer separates at least portions of other layers, and wherein at least one of the other layers comprises conductors comprising: (A) applying a polymeric material, which is comprised of a polymerizable oligomer selected from the group consisting of polyamic acids, polyamic esters, polyisoimides or mixtures thereof, wherein the end groups of the polymerizable oligomer are end capped with a vinyl or acetylenic end group, to a surface of the multilayer structure; (B) curing the polymerizable oligomer using a combined dry/cure cycle ranging between about 85° C. and about 300° C. to provide a polymeric insulating material; and (C) applying a layer of metallurgy or other conventional material as is used in the semiconductor arts to at least a portion of the surface of the cured polymeric insulating material of step (B).
Claim 22
Independent Claim
144 words
A method of forming a multilayer structure wherein at least one polymeric insulating layer separates at least portions of other layers, and wherein at least one of the other layers comprises conductors comprising: (A) applying a polymeric material, which is comprised of a polymerizable oligomer selected from the group consisting of polyamic acids, polyamic esters, polyisoimides or mixtures thereof, wherein the end groups of the polymerizable oligomer are end capped with a vinyl or acetylenic end group, to a surface of the multilayer structure; (B) curing the polymerizable oligomer using a combined dry/cure cycle ranging between about 85° C. and about 300° C. to provide a polymeric insulating material; and (C) applying a layer of metallurgy or other conventional material as is used in the semiconductor arts to at least a portion of the surface of the cured polymeric insulating material of step (B).
Claim 23
Independent Claim
154 words
A method of forming a multilayer structure wherein at least one polymeric insulating layer separates at least portions of other layers, and wherein at least one of the other layers comprises conductors, comprising: (A) applying a polymeric material, which is comprised of a polymerizable oligomer selected from the group consisting of polyamic acids, polyamic esters, polyisoimides or mixtures thereof, wherein the end groups of the polymerizable oligomer are end capped with a vinyl or acetylenic end group, to a surface of the multilayer structure; (B) curing the polymerizable oligomer using a combined dry/cure cycle ranging between about 85° C. and about 300° C. to provide a polymeric insulating material; (C) lithographically forming openings in the cured polymeric insulating material; and (D) applying a layer of metallurgy or other conventional material as is used in the semiconductor arts to at least a portion of the surface of the cured polymeric insulating material of step (C).
Claim 24
Independent Claim
154 words
A method of forming a multilayer structure wherein at least one polymeric insulating layer separates at least portions of other layers, and wherein at least one of the other layers comprises conductors, comprising: (A) applying a polymeric material, which is comprised of a polymerizable oligomer selected from the group consisting of polyamic acids, polyamic esters, polyisoimides or mixtures thereof, wherein the end groups of the polymerizable oligomer are end capped with a vinyl or acetylenic end group, to a surface of the multilayer structure; (B) curing the polymerizable oligomer using a combined dry/cure cycle ranging between about 85° C. and about 300° C. to provide a polymeric insulating material; (C) lithographically forming openings in the cured polymeric insulating material; and (D) applying a layer of metallurgy or other conventional material as is used in the semiconductor arts to at least a portion of the surface of the cured polymeric insulating material of step (C).
Claim 25
Independent Claim
138 words
A method of forming a multilayer structure wherein at least one polymeric insulating layer separates at least portions of other layers, and wherein at least one of the other layers comprises conductors, comprising: (A) applying a polymeric material, which is comprised of a polymerizable oligomer selected from the group consisting of polyamic acids, polyamic esters, polyisoimides or mixtures thereof, wherein the end groups of the polymerizable oligomer are end capped with a vinyl or acetylenic end group, to a surface of the multilayer structure; (B) curing the polymerizable oligomer at temperatures as high as about 400° C. to form a polymeric insulating material; and (C) applying a layer of metallurgy or other conventional material as is used in the semiconductor arts to at least a portion of the surface of the cured polymeric insulating material of step (B).
Claim 26
Independent Claim
138 words
A method of forming a multilayer structure wherein at least one polymeric insulating layer separates at least portions of other layers, and wherein at least one of the other layers comprises conductors, comprising: (A) applying a polymeric material, which is comprised of a polymerizable oligomer selected from the group consisting of polyamic acids, polyamic esters, polyisoimides or mixtures thereof, wherein the end groups of the polymerizable oligomer are end capped with a vinyl or acetylenic end group, to a surface of the multilayer structure; (B) curing the polymerizable oligomer at temperatures as high as about 400° C. to form a polymeric insulating material; and (C) applying a layer of metallurgy or other conventional material as is used in the semiconductor arts to at least a portion of the surface of the cured polymeric insulating material of step (B).
Claim 27
Independent Claim
149 words
A method of forming a multilayer structure wherein at least one polymeric insulating layer separates at least portions of other layers, and wherein at least one of the other layers comprises conductors, comprising: (A) applying a polymeric material which is comprised of a polymerizable oligomer selected from the group consisting of polyamic acids, polyamic esters, polyisoimides or mixtures thereof, wherein the end groups of the polymerizable oligomer are end capped with a vinyl or acetylenic end group, to a surface of the multilayer structure; (B) curing the polymerizable oligomer at temperatures as high as about 400° C. to form a polymeric insulating material; (C) lithographically forming openings in the polymeric insulating material; and (D) applying a layer of material of metallurgy or other conventional material as is used in the semiconductor arts to at least a portion of the surface of the cured polymeric insulating material of step C.
Claim 28
Independent Claim
149 words
A method of forming a multilayer structure wherein at least one polymeric insulating layer separates at least portions of other layers, and wherein at least one of the other layers comprises conductors, comprising: (A) applying a polymeric material which is comprised of a polymerizable oligomer selected from the group consisting of polyamic acids, polyamic esters, polyisoimides or mixtures thereof, wherein the end groups of the polymerizable oligomer are end capped with a vinyl or acetylenic end group, to a surface of the multilayer structure; (B) curing the polymerizable oligomer at temperatures as high as about 400° C. to form a polymeric insulating material; (C) lithographically forming openings in the polymeric insulating material; and (D) applying a layer of material of metallurgy or other conventional material as is used in the semiconductor arts to at least a portion of the surface of the cured polymeric insulating material of step C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-03-30 | 1990-09-29 | 1991-03-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-03-30 | 1994-09-29 | 1995-03-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-03-30 | 1998-09-29 | 1999-03-31 | $7700.00 | Window Closed / Lapsed |