Sealable, opaque polyolefinic multilayer film and process therefor
Assignee: Hoechst AG
•
Filing: 1985-12-05
•
Granted: 1987-03-24
•
Expires: 2005-12-05
Abstract
Abstract A sealable, opaque polyolefinic multilayer film composed of a polypropylene base layer, a non-sealable surface layer, and a sealable surface layer, and process therefor. The sealable surface layer has a low minimum sealing temperature and is made from a copolymer of propylene and ethylene or butene-1 units and/or a terpolymer of ethylene, propylene and butene-1 units. The non-sealable layer is a combination of a propylene homopolymer and a slip agent. The base layer contains an additive which is incompatible with polypropylene. The process includes stretching of the film, and during the stretching step, the polymer matrix is torn open around the additive particles to form vacuoles which give the base layer a degree of opacity.
Inventors
- 👤 Gunther Crass
- 👤 Siegfried Janocha
- 👤 Lothar Bothe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 10:15
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/32; B32B27/06; B32B27/08; B32B27/18; B32B38/00; B32B38/0008; C; C09; C09D; C09D123/00; C09D123/02; C09D123/10; C09D123/12; C09J; C09J123/00; C09J123/02; C09J123/10; C09J123/14; C09J123/142; B32B2250/00; B32B2250/24; B32B2250/242; B32B2307/00; B32B2307/40; B32B2307/41; B32B2307/50; B32B2307/514; B32B2307/518; B32B2307/70; B32B2307/75; B32B2310/00; B32B2310/14; B32B2323/00; B32B2323/10; C08; C08L; C08L2666/00; C08L2666/02; C08L2666/04; Y; Y10; Y10S; Y10S428/00; Y10S428/91; Y10T; Y10T428/00; Y10T428/26; Y10T428/266; Y10T428/28; Y10T428/2813; Y10T428/2817; Y10T428/2826; Y10T428/31504; Y10T428/31652; Y10T428/31663; Y10T428/31855; Y10T428/31909; Y10T428/31913
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
111 words
A sealable opaque polyolefinic multilayer film, comprising: a polypropylene base layer including an additive incompatible with said polypropylene; a sealable surface layer selected from the group consisting of a copolymer of propylene and ethylene, a copolymer of propylene and butene-1, a terpolymer of ethylene, propylene and butene-1, and combinations of the above; and a non-sealable surface layer comprising from about 97.5% to about 99.7% by weight of a propylene homopolymer, and from about 0.3% to about 2.5% by weight of a slip agent; wherein the density of said multilayer film is no greater than about 0.85 g/cm 3 , and wherein said sealable surface layer has a low minimum sealing temperature.
Claim 2
Dependent Claim
111 words
A sealable opaque polyolefinic multilayer film, comprising: a polypropylene base layer including an additive incompatible with said polypropylene; a sealable surface layer selected from the group consisting of a copolymer of propylene and ethylene, a copolymer of propylene and butene-1, a terpolymer of ethylene, propylene and butene-1, and combinations of the above; and a non-sealable surface layer comprising from about 97.5% to about 99.7% by weight of a propylene homopolymer, and from about 0.3% to about 2.5% by weight of a slip agent; wherein the density of said multilayer film is no greater than about 0.85 g/cm 3 , and wherein said sealable surface layer has a low minimum sealing temperature.
Claim 3
Dependent Claim
15 words
A multilayer film as claimed in claim 1, wherein said slip agent is a polydiorganosiloxane.
Claim 4
Dependent Claim
21 words
A multilayer film as claimed in claim 2, wherein said polydiorganosiloxane is selected from the group consisting of polydialkylsiloxane and polyalkylphenylsiloxane.
Claim 5
Dependent Claim
23 words
A multilayer film as claimed in claim 3, wherein said polydiorganosiloxane is selected from the group consisting of a polydimethylsiloxane and a polymethylphenylsiloxane.
Claim 6
Dependent Claim
28 words
A multilayer film as claimed in claim 4, wherein said polydiorganosiloxane has a kinematic viscosity of from about 10 3 to about 10 6 mm/s at 25° C.
Claim 7
Dependent Claim
28 words
A multilayer film as claimed in claim 4, wherein said polydiorganosiloxane has a kinematic viscosity of from about 20,000 to about 30,000 mm 2 /s at 25° C.
Claim 8
Dependent Claim
73 words
A multilayer film as claimed in claim 1, wherein said sealable surface layer further contains at least one additive selected from the group consisting of a low molecular weight resin and a propylene homopolymer, said resin being compatible with the copolymer or terpolymer of said sealable surface layer, each of said at least one additive present in an amount of from about 5% to about 15% by weight of said sealable surface layer.
Claim 9
Dependent Claim
57 words
A multilayer film as claimed in claim 1, wherein said sealable surface layer comprises an ethylene-propylene-butene-1 terpolymer and a propylene-butene-1 copolymer, corresponding to a content of from about 0.1% to about 7% by weight of ethylene, from about 53% to about 89.9% by weight of propylene and from about 10% to about 40% by weight of butene-1.
Claim 10
Dependent Claim
57 words
A multilayer film as claimed in claim 7, wherein said sealable surface layer comprises an ethylene-propylene-butene-1 terpolymer and a propylene-butene-1 copolymer, corresponding to a content of from about 0.1% to about 7% by weight of ethylene, from about 53% to about 89.9% by weight of propylene and from about 10% to about 40% by weight of butene-1.
Claim 11
Dependent Claim
44 words
A multilayer film as claimed in claim 7, wherein said low molecular weight resin has a softening point of from about 60° C. to about 180° C., and wherein said sealable surface layer has a sealing temperature of no greater than about 100° C.
Claim 12
Dependent Claim
19 words
A multilayer film as claimed in claim 1, wherein said non-sealable surface layer is corona-treated to improve its printability.
Claim 13
Dependent Claim
18 words
A multilayer film as claimed in claim 1, wherein said film is oriented by a biaxial stretching process.
Claim 14
Dependent Claim
26 words
A multilayer film as claimed in claim 1, wherein said incompatible additive is present in an amount of from about 5% to about 30% by weight.
Claim 15
Dependent Claim
30 words
A multilayer film as claimed in claim 1, wherein said incompatible additive is selected from the group consisting of calcium carbonate, silicon dioxide, a Na-Al-silicate, and combinations of the above.
Claim 16
Dependent Claim
31 words
A multilayer film as claimed in claim 1, wherein said incompatible additive is selected from the group consisting of polystyrene, polymethylmethacrylate, polytetrafluoroethylene, and copolymers of two or more of the above.
Claim 17
Dependent Claim
25 words
A multilayer film as claimed in claim 1, wherein said incompatible additive has an average particle diameter of from about 2 to about 8 μm.
Claim 18
Dependent Claim
24 words
A packaging film produced from the multilayer film of claim 1, wherein said surface layers have a thickness of less than about 3 μm.
Claim 19
Dependent Claim
182 words
A process for preparing a sealable, opaque polyolefinic multilayer film, comprising the steps of: coextruding a base layer and a separate surface layer on each side of said base layer to form the multilayer film, one of said surface layers being sealable and the other of said surface layers being non-sealable; biaxially stretching said multilayer film in longitudinal and transverse directions; and subjecting said non-sealable surface layer to a corona-discharge treatment; wherein said base layer is a polypropylene, and includes an additive which is incompatible with said polypropylene, said sealable surface layer is selected from the group consisting of a copolymer of propylene and ethylene, a copolymer of propylene and butene-1, a terpolymer of ethylene, propylene and butene-1, and combinations of the above, and said non-sealable surface layer comprises from about 97.5% to about 99.7% by weight of a propylene homopolymer, and from about 0.3% to about 2.5% by weight of a slip agent; wherein the density of said multilayer film is no greater than about 0.85 g/cm 3 , and wherein said sealable surface layer has a low minimum sealing temperature.
Claim 20
Dependent Claim
182 words
A process for preparing a sealable, opaque polyolefinic multilayer film, comprising the steps of: coextruding a base layer and a separate surface layer on each side of said base layer to form the multilayer film, one of said surface layers being sealable and the other of said surface layers being non-sealable; biaxially stretching said multilayer film in longitudinal and transverse directions; and subjecting said non-sealable surface layer to a corona-discharge treatment; wherein said base layer is a polypropylene, and includes an additive which is incompatible with said polypropylene, said sealable surface layer is selected from the group consisting of a copolymer of propylene and ethylene, a copolymer of propylene and butene-1, a terpolymer of ethylene, propylene and butene-1, and combinations of the above, and said non-sealable surface layer comprises from about 97.5% to about 99.7% by weight of a propylene homopolymer, and from about 0.3% to about 2.5% by weight of a slip agent; wherein the density of said multilayer film is no greater than about 0.85 g/cm 3 , and wherein said sealable surface layer has a low minimum sealing temperature.
Claim 21
Dependent Claim
40 words
A process as claimed in claim 13, wherein said corona-discharge treatment is performed at an intensity sufficient to obtain a surface tension equivalent to between about 36 and about 40 mN/m in a comparable surface layer lacking said slip agent.
Claim 22
Dependent Claim
24 words
A process as claimed in claim 13, wherein said biaxially stretched film has a thickness of from about 15 μm to about 60 μm.
References Cited (Backward Citations)
US4230767A
Cited
US4303708A
Cited
US4293608A
Cited
US4340641A
Cited
US4348457A
Cited
US4502263A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-03-23 | 1990-09-22 | 1991-03-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-03-23 | 1994-09-22 | 1995-03-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-03-23 | 1998-09-22 | 1999-03-24 | $7700.00 | Window Closed / Lapsed |