Double layer photoresist technique for side-wall profile control in plasma etching processes
Assignee: Raytheon Co
•
Filing: 1985-04-29
•
Granted: 1987-02-24
•
Expires: 2005-04-29
Abstract
Abstract A photolithographic process useful for VLSI fabrication is disclosed for achieving side-wall profile control of poly lines, metal lines, contact and via openings. Layers of a first and second photoresist materials are formed on the poly, metal or oxide-covered substrate. The top layer is patterned by conventional processes to define the final device geometry. The bottom layer is exposed and over-developed to form an overhang structure about the line pattern or the contact/via opening. During the subsequent anisotropic plasma-assisted etching step, some ions or particles are passed obliquely over the overhang and bombard the opening corner, the side-wall and the under-cut area. The plasma-assisted etching step not only forms the poly or metal lines, or the contact or via opening, but also results in an opening with rounded corners and a smoothly tapered side-wall profile. The subsequent metal film deposition step results in a uniform film thickness around the edges of the opening. The process thus alleviates the problem of high contact resistance previously encountered as a result of dry etching the contact or via openings.
Inventors
- 👤 Kuan Y. Liao
- 👤 Kuang-Yeh Chang
- 👤 Hsing-Chien Ma
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 21:49
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/26; H10P50/264; H10P50/266; H10P50/267; H10P50/268; H10P50/28; H10P50/282; H10P50/283; H10P50/73
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
94 words
A process for forming a smoothly contoured via opening in protective surface layer used in semiconductor device fabrication including the steps of: (a) directing a beam of etchant particles normal to a predefined surface area of said protective surface layer, and (b) deflecting particles in the portion of said beam corresponding to the edge of said via opening to vary the amount and intensity of particles striking the protective sidewalls of said via opening, whereby said sidewalls are formed with a smoothly rounded contour to thereby receive smoothly contoured metal-over-insulator contacts at high yields.
Claim 2
Dependent Claim
94 words
A process for forming a smoothly contoured via opening in protective surface layer used in semiconductor device fabrication including the steps of: (a) directing a beam of etchant particles normal to a predefined surface area of said protective surface layer, and (b) deflecting particles in the portion of said beam corresponding to the edge of said via opening to vary the amount and intensity of particles striking the protective sidewalls of said via opening, whereby said sidewalls are formed with a smoothly rounded contour to thereby receive smoothly contoured metal-over-insulator contacts at high yields.
Claim 3
Dependent Claim
22 words
The process defined in claim 1 wherein said protective surface is formed initially on either a semiconductor substrate or a conductive layer.
Claim 4
Dependent Claim
45 words
The process defined in claims 1 or 2 wherein said beam of particles is deflected by extending a contoured mask into said beam of particles to provide a variation in amount and intensity of said beam proportional to the degree of contour of said mask.
Claim 5
Dependent Claim
104 words
An improved plasma-assisted etching process for use in integrated circuit fabrication for forming a pattern in a surface layer, comprising a sequence of the following steps: (i) forming a patterned masking layer on said surface layer, said masking layer having a predetermined pattern formed therein and arranged such that the masking layer comprises an overhang structure defining the periphery of said pattern; and (ii) etching said surface layer through the pattern in said masking layer by means of an anisotropic plasma-assisted etch to form sidewalls having a tapered profile in said surface layer in substantial correspondence with the pattern formed in the masking layer.
Claim 6
Dependent Claim
104 words
An improved plasma-assisted etching process for use in integrated circuit fabrication for forming a pattern in a surface layer, comprising a sequence of the following steps: (i) forming a patterned masking layer on said surface layer, said masking layer having a predetermined pattern formed therein and arranged such that the masking layer comprises an overhang structure defining the periphery of said pattern; and (ii) etching said surface layer through the pattern in said masking layer by means of an anisotropic plasma-assisted etch to form sidewalls having a tapered profile in said surface layer in substantial correspondence with the pattern formed in the masking layer.
Claim 7
Dependent Claim
30 words
The improved process of claim 4 wherein the step of forming the patterned masking layer comprises the step of applying a layer of first photoresist material to the substrate layer.
Claim 8
Dependent Claim
36 words
The improved process of claim 5 wherein the step of forming the patterned masking layer comprises the additional step of applying a layer of a second photoresist material to the layer of the first photoresist material.
Claim 9
Dependent Claim
70 words
The improved process of claim 6 wherein the step of forming the patterned masking layer comprises the additional steps of: (i) exposing the first photoresist material through a mask bearing the predetermined opening pattern; (ii) developing the second photoresist to define the predetermined opening pattern therein; (iii) exposing and thereafter developing the first photoresist material through the opening pattern formed in the first photoresist material to form the overhang structure.
Claim 10
Dependent Claim
15 words
The improved process of claim 7 further comprising the step of removing the overhang structure.
Claim 11
Dependent Claim
54 words
The improved process of claim 8 wherein the step of removing the overhang structure comprises: (i) immersing the substrate in a solution adapted to dissolve the layer of the first photoresist; and (ii) subjecting the immersed wafer to ultrasonic vibration, whereby the layer of the second photoresist material is lifted away from the substrate.
Claim 12
Dependent Claim
21 words
The improved process of claim 4 wherein said suface layer comprises a poly layer and the layer pattern comprises poly lines.
Claim 13
Dependent Claim
21 words
The improved process of claim 4 wherein said surface layer comprises a metal layer and the layer pattern comprises metal lines.
Claim 14
Dependent Claim
15 words
The improved process of claim 4 wherein said layer pattern comprises a contact opening pattern.
Claim 15
Dependent Claim
143 words
An improved plasma-assisted etching process for use in integrated circuit fabrication for etching a pattern in a surface layer on a wafer, comprising a sequence of the following steps: (i) applying a first layer of a first photoresist material on the surface layer; (ii) applying a second layer of a second photoresist material to said first layer to form a double layer of photoresist materials; (iii) employing a mask to selectively expose the second layer of photoresist material and thereafter developing the second layer to provide a predetermined pattern in the second layer; (iv) selectively exposing and thereafter developing the first photoresist layer through the pattern formed in the second photoresist layer to form a photoresist overhang structure; (v) conducting a plasma-assisted etch to selectively etch the surface layer through the photoresist overhang structure; and (vi) stripping the photoresist materials from the substrate.
Claim 16
Dependent Claim
143 words
An improved plasma-assisted etching process for use in integrated circuit fabrication for etching a pattern in a surface layer on a wafer, comprising a sequence of the following steps: (i) applying a first layer of a first photoresist material on the surface layer; (ii) applying a second layer of a second photoresist material to said first layer to form a double layer of photoresist materials; (iii) employing a mask to selectively expose the second layer of photoresist material and thereafter developing the second layer to provide a predetermined pattern in the second layer; (iv) selectively exposing and thereafter developing the first photoresist layer through the pattern formed in the second photoresist layer to form a photoresist overhang structure; (v) conducting a plasma-assisted etch to selectively etch the surface layer through the photoresist overhang structure; and (vi) stripping the photoresist materials from the substrate.
Claim 17
Dependent Claim
15 words
The invention of claim 13 wherein said plasma-assisted etch step comprises an anisotropic plasma etch.
Claim 18
Dependent Claim
20 words
The invention of claim 13 further comprising the step of depositing a layer of metal over the etched surface layer.
Claim 19
Dependent Claim
22 words
The invention of claim 13 wherein said mask employed to selectively expose the second layer of photoresist material comprises a contact mask.
Claim 20
Dependent Claim
57 words
The invention of claim 13 wherein the step of stripping the photoresist materials from the surface layer comprises: (i) immersing the wafer in a solution adapted to dissolve the first photoresist material; and (ii) subjecting the immersed wafer to ultrasonic vibration, whereby the second layer of the second photoresist material is lifted away from the surface layer.
Claim 21
Dependent Claim
98 words
An improved process for providing metal contacts on a wafer during VLSI fabrication, comprising a sequence of the following steps: (i) forming a patterned masking layer on the wafer, the masking layer having a predetermined pattern formed therein such that the masking layer comprises an overhang structure defining the pattern; (ii) etching said wafer through said opening pattern in the masking layer by means of an anisotropic plasma-assisted etch to form an etched pattern is said wafer having a tapered sidewall profile; (iii) removing the masking layer from the wafer; and (iv)depositing a metal layer over the wafer.
Claim 22
Dependent Claim
98 words
An improved process for providing metal contacts on a wafer during VLSI fabrication, comprising a sequence of the following steps: (i) forming a patterned masking layer on the wafer, the masking layer having a predetermined pattern formed therein such that the masking layer comprises an overhang structure defining the pattern; (ii) etching said wafer through said opening pattern in the masking layer by means of an anisotropic plasma-assisted etch to form an etched pattern is said wafer having a tapered sidewall profile; (iii) removing the masking layer from the wafer; and (iv)depositing a metal layer over the wafer.
Claim 23
Dependent Claim
28 words
The invention of claim 18 wherein the step of forming a masking layer comprises the application of respective lower and upper layers of first and second photoresist layers.
Claim 24
Dependent Claim
95 words
The invention of claim 17 wherein the step of forming a masking layer further comprises: (i) exposing the top layer of photoresist material through a mask; (ii) developing the top layer of photoresist material to form a pattern in the top layer; (iii) exposing the bottom layer of photoresist material through the contact pattern in the top layer; and (iv) developing the bottom photoresist layer through the opening pattern formed in the top layer so that the the top layer overhangs the bottom layer around the periphery of the opening formed in the top layer.
Claim 25
Dependent Claim
21 words
The improved process of claim 13 wherein said surface layer comprises a poly layer and the layer pattern comprises poly lines.
Claim 26
Dependent Claim
15 words
The improved process of claim 13 wherein said layer pattern comprises a contact opening pattern.
Claim 27
Dependent Claim
21 words
The improved process of claim 22 further comprising the step of depositing metal over said patterned layer to form metal contacts.
Claim 28
Dependent Claim
84 words
A process for forming a smoothly contoured opening pattern in a protective surface layer used in semiconductor device fabrication, including the steps of: (a) directing a beam of etchant particles at a predefined surface area of said protective surface layer, and (b) deflecting particles in the portion of said beam corresponding to the edges of said opening pattern to vary the amount and intensity of particles striking the protective sidewalls of said opening pattern, whereby said sidewalls are formed with a smoothly rounded contour.
Claim 29
Dependent Claim
84 words
A process for forming a smoothly contoured opening pattern in a protective surface layer used in semiconductor device fabrication, including the steps of: (a) directing a beam of etchant particles at a predefined surface area of said protective surface layer, and (b) deflecting particles in the portion of said beam corresponding to the edges of said opening pattern to vary the amount and intensity of particles striking the protective sidewalls of said opening pattern, whereby said sidewalls are formed with a smoothly rounded contour.
Claim 30
Dependent Claim
127 words
A process for forming a smoothly contoured opening pattern in a protective surface layer used in semiconductor device fabrication, including the steps of: (i) forming a patterned masking layer over said protective surface layer, the masking layer having a predetermined pattern formed therein such that the masking layer comprises an overhang structure defining the pattern; (ii) directing a beam of anisotropic etchant particles at a predefined surface area of said protective surface layer through said patterned masking layer; and (iii) deflecting particles from the edges of the openings patterned in said masking layer to vary the amount and intensity of particles striking said protective surface layer adjacent to the edges thereof, whereby said opening is formed in said protective surface layer sidewalls with a smoothly rounded contour.
Claim 31
Dependent Claim
127 words
A process for forming a smoothly contoured opening pattern in a protective surface layer used in semiconductor device fabrication, including the steps of: (i) forming a patterned masking layer over said protective surface layer, the masking layer having a predetermined pattern formed therein such that the masking layer comprises an overhang structure defining the pattern; (ii) directing a beam of anisotropic etchant particles at a predefined surface area of said protective surface layer through said patterned masking layer; and (iii) deflecting particles from the edges of the openings patterned in said masking layer to vary the amount and intensity of particles striking said protective surface layer adjacent to the edges thereof, whereby said opening is formed in said protective surface layer sidewalls with a smoothly rounded contour.
References Cited (Backward Citations)
JPS547871A
Cited
JPS5569264A
Cited
US4354897A
Cited
JPS56130925A
Cited
JPS5783034A
Cited
DE3215411A1
Cited
US4461672A
Cited
US4484978A
Cited
US4523976A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-02-23 | 1990-08-25 | 1991-02-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-02-23 | 1994-08-25 | 1995-02-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-02-23 | 1998-08-25 | 1999-02-24 | $7700.00 | Window Closed / Lapsed |