Method for applying material to a substrate

Claim 2

A process for brazing refractory particles onto a substrate, which process comprises applying to the substrate a brazing material, a particulate refractory material to be brazed onto the substrate and a binder composition; and connecting the substrate to a source of an electric current to cause the current to flow through the substrate whereby the substrate is heated to sufficient temperature to cause the brazing material to fuse.

Claim 3

A process as claimed in claim 1 wherein after brazing the refractory material onto the substrate the substrate is re-heated to cause thermal tempering thereof by passing an electric current through the substrate.

Claim 4

A process as claimed in claim 1 wherein the particulate refractory material is selected from the carbides, nitrides, borides and silicides of nickel and tungsten and has a mass median particle size in the range 0.01 to 1.5 mms.

Claim 5

A process as claimed in claim 1 wherein the brazing material is selected from a cobalt-based and a nickel-based alloy.

Claim 6

A process as claimed in claim 1 wherein the binder composition comprises a material selected from a volatile material and a thermally decomposable material which is substantially eliminated from the coating on the substrate during the brazing process.

Claim 7

A process as claimed in claim 5 wherein the binder comprises an acrylic polymer.

Claim 8

A process as claimed in claim 1 wherein the coated substrate is heated by passing a current of from 50 to 250 amps at a voltage of 10 to 50 volts AC or DC through it.

Claim 9

A process as claimed in claim 1 wherein the coated substrate is heated in a protective atmosphere or under vacuum.

Claim 10

A process as claimed in claim 8 wherein the protective atmosphere is provided at least in part by the products of volatilisation and/or decomposition of the binder composition.

Claim 11

A process as claimed in claim 1 wherein the overall coating applied to the substrate comprises 5 to 10 parts of tungsten carbide refractory grit, 1 to 2 parts of a cobalt or nickel based brazing powder, from 2 to 5 parts of the binder and, optionally, from 1 to 2 parts of a flux, all parts being by dry weight.

Claim 12

A process for brazing refractory particles onto a steel tool blank substrate so as to form a grit cutting edge thereon, which process comprises: (a) applying to the substrate a brazing material selected from a cobalt-based and a nickel-based alloy; a particulate refractory material selected from the carbides, nitrides, borides and silicides of nickel and tungsten and having a mass median particle size in the range 0.01 to 6 mms; a binder composition comprising an acrylic polymeric material; and optionally a flux material selected from fluoride based fluxes and borax/boric acid mixtures; said materials being used in proportions of from 5 to 10 parts of refractory material, 1 to 2 parts of brazing material, from 2 to 5 parts of binder composition and, optionally, from 1 to 2 parts of flux, all parts being by dry weight; (b) connecting the substrate to a source of an electric current to cause a current of from 50 to 250 amps at from 10 to 50 volts to flow through the substrate whereby the substrate is heated to sufficient temperature to cause the brazing material to fuse in a protective atmosphere at part of which is provided by volatilisation and decomposition products from the binder composition; and (c) optionally re-heating the brazed substrate to cause thermal tempering thereof by passing a further electric current therethrough during cooling of the substrate following brazing.

Claim 13

A process for brazing refractory particles onto a steel tool blank substrate so as to form a grit cutting edge thereon, which process comprises: (a) applying to the substrate a brazing material selected from a cobalt-based and a nickel-based alloy; a particulate refractory material selected from the carbides, nitrides, borides and silicides of nickel and tungsten and having a mass median particle size in the range 0.01 to 6 mms; a binder composition comprising an acrylic polymeric material; and optionally a flux material selected from fluoride based fluxes and borax/boric acid mixtures; said materials being used in proportions of from 5 to 10 parts of refractory material, 1 to 2 parts of brazing material, from 2 to 5 parts of binder composition and, optionally, from 1 to 2 parts of flux, all parts being by dry weight; (b) connecting the substrate to a source of an electric current to cause a current of from 50 to 250 amps at from 10 to 50 volts to flow through the substrate whereby the substrate is heated to sufficient temperature to cause the brazing material to fuse in a protective atmosphere at part of which is provided by volatilisation and decomposition products from the binder composition; and (c) optionally re-heating the brazed substrate to cause thermal tempering thereof by passing a further electric current therethrough during cooling of the substrate following brazing.