Dielectric ceramic composition and method of producing same, and a monolithic capacitor

Claim 2

A dielectric, ceramic material having a composition: (Ba.sub.1-x Sr.sub.x O).sub.a Ti.sub.1-y Zr.sub.y O.sub.2 +α((1-z)MnO+zCoO)+β((1-t)A.sub.2 O.sub.5 +tL.sub.2 O.sub.3)+wSiO.sub.2, wherein: A=Nb, Ta, V; L=Y or a rare earth element; 0.002≦x+y+1.7αz≦0.250; 0.000≦z≦0.980; 0.990≦a≦1.020; 0.010≦α≦15.00 (mol %); 0.01≦β/α≦0.55; 0.000≦t≦0.980; and 0.002≦w≦1.00 (wt %).

Claim 3

A monolithic capacitor comprising: a plurality of layers of dielectric ceramic composition (Ba 1-x Sr x O) a Ti 1-y Zr y O 2 +α((1-z)MnO+zCoO)+β((1-t)A 2 O 5 +tL 2 O 3 )+wSiO 2 , wherein: A=Nb, Ta, V; L=Y or a rare earth element; 0.002≦x+y+1.7αz≦0.250; 0.000≦z≦0.980; 0.990≦a≦1.020; 0.010≦α≦15.00 (mol %); 0.01≦β/α≦0.55; 0.000≦t≦0.980; and, 0.002≦w≦1.00 (wt %); a plurality of layers of base metal electrodes, each layer being bonded between a pair of the dielectric ceramic compositions; and, a pair of external electrodes electrically and selectively connected to the base metal electrodes.

Claim 4

A monolithic capacitor comprising: a plurality of layers of dielectric ceramic composition (Ba 1-x Sr x O) a Ti 1-y Zr y O 2 +α((1-z)MnO+zCoO)+β((1-t)A 2 O 5 +tL 2 O 3 )+wSiO 2 , wherein: A=Nb, Ta, V; L=Y or a rare earth element; 0.002≦x+y+1.7αz≦0.250; 0.000≦z≦0.980; 0.990≦a≦1.020; 0.010≦α≦15.00 (mol %); 0.01≦β/α≦0.55; 0.000≦t≦0.980; and, 0.002≦w≦1.00 (wt %); a plurality of layers of base metal electrodes, each layer being bonded between a pair of the dielectric ceramic compositions; and, a pair of external electrodes electrically and selectively connected to the base metal electrodes.

Claim 5

A monolithic capacitor according to claim 2, wherein said base metal electrodes consist essentially of at least one metal selected from the group consisting of Ni, Fe, Co, Cr, W and Mo.

Claim 6

A monolithic capacitor according to claim 3, wherein said base metal electrodes consist essentially of Ni.

Claim 7

A monolithic capacitor according to claim 3, wherein a thickness of each of said base metal electrodes is from 2 to 5 microns.

Claim 8

A monolithic capacitor according to claim 2, wherein a thickness of layers of dielectric material is from 20 to 40 microns.

Claim 9

A monolithic capacitor according to claim 3 or 6, wherein said monolithic capacitor is produced by firing monolithic materials capable of yielding said dielectric ceramic composition and base metal in a reducing or non-oxidizing atmosphere.

Claim 10

A monolithic capacitor according to claim 7, wherein the firing is carried out at a temperature of from 1180° to 1300° C.

Claim 11

In a method for producing a monolithic ceramic body comprising a plurality of dielectric ceramic layers and a plurality of electrodes, each of which is bonded between a pair of the ceramic layers, comprising the steps of: mixing finely divided compounds to obtain a predetermined composition which yields a barium titanate-based ceramic after firing; rendering said predetermined composition into a moldable state; forming sheets of said predetermined composition, for providing said plurality of dielectric ceramic layers, after the firing; forming a predetermined pattern of material on said sheets, which material is capable of forming a base metal electrode, after the firing; laminating said sheets having the predetermined pattern of material to each other, thereby sandwiching each of the predetermined patterns of material between a pair of said sheets; and, firing the laminated sheets and material in a reducing or non-oxidizing atmosphere, an improvement comprises: separately preparing compounds expressed by BaTiO 3 , SrTiO 3 , BaZrO 3 , and SrZrO 3 , respectively, and finely dividing said compounds; adding an Mn-oxide-bearing material, a Co oxide-bearing material, a material bearing an oxide of at least one element selected from the first group consisting of Nb, Ta, and V, and a material bearing an oxide of at least one element selected from the second group consisting of Y and a rare earth element, to said separately prepared compounds; and mixing them so as to obtain a barium titanate-based composition having a formula (Ba.sub.1-x Sr.sub.x O).sub.a Ti.sub.1-y Zr.sub.y O.sub.2 +α((1-z)MnO+zCoO)+β((1-t)A.sub.2 O.sub.5 +tL.sub.2 O.sub.3)+wSiO.sub.2, wherein: A=Nb, Ta, V; L=Y or a rare earth element; 0.002≦x+y+1.7αz≦0.250; 0.000≦z≦0.980; 0.990≦a≦1.020; 0.010≦α≦15.00 (mol %); 0.01≦β/α≦0.55; 0.000≦t≦0.980; and, 0.002≦w≦1.00 (wt %).

Claim 12

In a method for producing a monolithic ceramic body comprising a plurality of dielectric ceramic layers and a plurality of electrodes, each of which is bonded between a pair of the ceramic layers, comprising the steps of: mixing finely divided compounds to obtain a predetermined composition which yields a barium titanate-based ceramic after firing; rendering said predetermined composition into a moldable state; forming sheets of said predetermined composition, for providing said plurality of dielectric ceramic layers, after the firing; forming a predetermined pattern of material on said sheets, which material is capable of forming a base metal electrode, after the firing; laminating said sheets having the predetermined pattern of material to each other, thereby sandwiching each of the predetermined patterns of material between a pair of said sheets; and, firing the laminated sheets and material in a reducing or non-oxidizing atmosphere, an improvement comprises: separately preparing compounds expressed by BaTiO 3 , SrTiO 3 , BaZrO 3 , and SrZrO 3 , respectively, and finely dividing said compounds; adding an Mn-oxide-bearing material, a Co oxide-bearing material, a material bearing an oxide of at least one element selected from the first group consisting of Nb, Ta, and V, and a material bearing an oxide of at least one element selected from the second group consisting of Y and a rare earth element, to said separately prepared compounds; and mixing them so as to obtain a barium titanate-based composition having a formula (Ba.sub.1-x Sr.sub.x O).sub.a Ti.sub.1-y Zr.sub.y O.sub.2 +α((1-z)MnO+zCoO)+β((1-t)A.sub.2 O.sub.5 +tL.sub.2 O.sub.3)+wSiO.sub.2, wherein: A=Nb, Ta, V; L=Y or a rare earth element; 0.002≦x+y+1.7αz≦0.250; 0.000≦z≦0.980; 0.990≦a≦1.020; 0.010≦α≦15.00 (mol %); 0.01≦β/α≦0.55; 0.000≦t≦0.980; and, 0.002≦w≦1.00 (wt %).

Claim 13

A method according to claim 9, wherein the firing is carried out at a temperature of from 1180° to 1300° C.

Claim 14

A method according to claim 9, wherein said preparation step comprises: forming BaTiO 3 , SrTiO 3 , BaZrO 3 , and SrZrO 3 by pre-firing at a temperature of from 1000° to 1240° C.

Claim 15

A method according to claim 11, wherein said Mn-oxide bearing material is MnCO 3 , said Co-oxide bearing material is Co 3 O 4 , said material bearing an oxide of at least one element selected from the first group consisting of Nb, Ta, and V is Nb 2 O 5 , Ta 2 O 5 or V 2 O 5 , and said material bearing an oxide of at least one element selected from the second group consisting of Y and a rare earth element is Y 2 O 3 or an oxide of the rare earth element.