Process for producing chalcogenide semiconductors

Claim 2

A process for producing a chalcogenide semiconductor material for use in photovoltaic semiconductor devices, said process comprising: a. forming a solution containing ions from at least one chalcogen and providing said solution with a pH in a range of 1-2 so as to provide said semiconductor material with suitable performance characteristics when used as said photovoltaic semiconductor device; b. forming a metal base layer containing a sufficient number of metal elements to form at least a ternary chalcogenide semiconductor material upon being chalcogenized with said solution; and c. contacting said metal base layer with said solution at about ambient temperature so as to chalcogenize said metal base layer and form said at least ternary chalcogenide semiconductor material.

Claim 3

The process as claimed in claim 1, wherein said chalcogen is selected from one or more of the Group VIa elements.

Claim 4

The process as claimed in claim 2, wherein said chalcogen is selected from the group consisting of selenium, tellurium, and sulfur.

Claim 5

The process as claimed in claim 1, wherein said metal base layer comprises an alloy of one or more elements selected from the group consisting of Group Ib, Group IIb, Group IIIa, and Group IVa elements.

Claim 6

The process as claimed in claim 1, wherein said metal base layer is formed on a conducting substrate prior to contacting said layer with said solution.

Claim 7

The process as claimed in claim 5, wherein said conducting substrate is in the form of a thin layer and is selected from the group consisting of Mo, ITO, SnO 2 , Ti, and stainless steel.

Claim 8

The process as claimed in claim 1, wherein said chalcogenide semiconductor material comprises a ternary chalcogenide, wherein said metal base comprises a binary alloy compound having elements selected from the group consisting of Group Ib, Group IIb, Group IIIa, and Group IVa elements, and wherein said chalcogen is selected from Goup VIa elements.

Claim 9

The process as claimed in claim 1, wherein said chalcogenide semiconductor material comprises a quaternary chalcogenide, wherein said metal base comprises a ternary compound having elements selected from the group consisting of Group Ib, Group IIb, Group IIIa, and Group IVa elements, and wherein said chalcogen is selected from Group VIa elements.

Claim 10

The process as claimed in claim 21, wherein said chalcogenide semiconductor material comprises CuInSe 2 , said metal base layer comprises the alloy CuIn, and said solution contains Se +4 ions.

Claim 11

The process as claimed in claim 21, wherein said chalcogenide semiconductor material comprises p-type material for use in solar cells and other photovoltaic cells.

Claim 12

A process for chalcogenizing metal base layer films to form a photosensitive semiconductor material, said process comprising: a. forming a solution containing ions from at least one chalcogen selected from group VIa elements and providing said solution with a pH in a range of 1-2 so as to provide the photosensitive semiconductor material with suitable performance characteristics for use in photovoltaic applications; b. forming a metal base layer containing a sufficient number of metal elements to form at least a ternary chalcogenide photosensitive semiconductor material when put in contact with said solution; and c. contacting said metal base layer with said solution at about ambient temperature so as to chalcogenize said metal base layer and form said at least ternary chalcogenide photosensitive semiconductor material.

Claim 13

A process for chalcogenizing metal base layer films to form a photosensitive semiconductor material, said process comprising: a. forming a solution containing ions from at least one chalcogen selected from group VIa elements and providing said solution with a pH in a range of 1-2 so as to provide the photosensitive semiconductor material with suitable performance characteristics for use in photovoltaic applications; b. forming a metal base layer containing a sufficient number of metal elements to form at least a ternary chalcogenide photosensitive semiconductor material when put in contact with said solution; and c. contacting said metal base layer with said solution at about ambient temperature so as to chalcogenize said metal base layer and form said at least ternary chalcogenide photosensitive semiconductor material.

Claim 14

The process as claimed in claim 22, wherein said solution contains a chalcogen ion concentration of at least about 0.001 M.

Claim 15

The process as claimed in claim 22, wherein said metal base layer comprises an alloy of one or more elements selected from the group consisting of Group Ib, Group IIb, Group IIIa, and Group IVa elements.

Claim 16

The process as claimed in claim 22, wherein said chalcogen is selected from the group consisting of selenium, tellurium and sulfur.

Claim 17

The process as claimed in claim 11, wherein said chalcogenide semiconductor material comprises p-type photovoltaic material.

Claim 18

The process as claimed in claim 11, wherein said metal base layer film is first deposited onto a conducting substrate surface.

Claim 19

The process as claimed in claim 11, wherein said photovoltaic material comprises ternary semiconductor material, and wherein said metal base layer film comprises a binary alloy.

Claim 20

The process as claimed in claim 11, wherein said photovoltaic material comprises a quaternary semiconductor material, and wherein said metal base layer film comprises a ternary alloy.