Process for making a selective absorber for a solar collector and selective absorber obtained
Assignee: Bpifrance Financement SA
•
Filing: 1982-07-02
•
Granted: 1984-04-24
•
Expires: 2002-07-02
Abstract
Abstract The invention concerns a fabrication process for a selective absorber of a solar collector to achieve a solar-radiation collection-surface with high absorptivity and low emissivity. The collector surface is made of an iron alloy containing chrome and is immersed in an acid bath containing oxygen atoms and at least one metalloid substance based on sulfur, selenium and/or tellurium; beforehand, the state of the collector surface is adjusted for activation.
Inventors
- 👤 Lucien Aries
- 👤 Jean-Pierre Traverse
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 21:51
CPC Classifications
C; C23; C23C; C23C22/00; C23C22/05; C23C22/06; C23C22/48; C23C22/50; F; F24; F24S; F24S70/00; F24S70/20; F24S70/225; F24S70/25; Y; Y02; Y02E; Y02E10/00; Y02E10/40; Y10; Y10S; Y10S126/00; Y10S126/907; Y10S126/908; Y10S128/00; Y10S128/901
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
149 words
A process for making a selective absorber for a solar collector for obtaining a collector surface for solar radiation having high absorptivity and low emissivity comprising providing a collector surface of iron containing chromium alloyed therewith, providing an acid bath containing oxygen atoms and at least one metalloid substance based on sulfur, selenium and/or tellurium dissolved in said bath, adjusting the state of the collector surface so that the natural corrosion potential of the collector surface in the presence of said bath is less than the primary passivation potential for raising the surface to the active state, and contacting said collector surface with said bath so as to cause migration of the metal atoms from the collector and to cause migration of the metalloid atoms from the bath and to thereby bring about interface reactions between said metal atoms and said metalloid atoms at the surface of said collector.
Claim 2
Dependent Claim
149 words
A process for making a selective absorber for a solar collector for obtaining a collector surface for solar radiation having high absorptivity and low emissivity comprising providing a collector surface of iron containing chromium alloyed therewith, providing an acid bath containing oxygen atoms and at least one metalloid substance based on sulfur, selenium and/or tellurium dissolved in said bath, adjusting the state of the collector surface so that the natural corrosion potential of the collector surface in the presence of said bath is less than the primary passivation potential for raising the surface to the active state, and contacting said collector surface with said bath so as to cause migration of the metal atoms from the collector and to cause migration of the metalloid atoms from the bath and to thereby bring about interface reactions between said metal atoms and said metalloid atoms at the surface of said collector.
Claim 3
Dependent Claim
26 words
A process according to claim 1, and including adding to said bath a corrosion inhibitor specific to the alloy and the bath containing the metalloid substance.
Claim 4
Dependent Claim
27 words
A process according to claim 2, and wherein said corrosion inhibitor added to the bath is selected from the group consisting of acetylenic alcohols and ethylenic alcohols.
Claim 5
Dependent Claim
92 words
A process as in one of claims 1, 2 or 3, and including adjusting the natural corrosion potential of the alloy by measuring said natural corrosion potential using a test circuit comprising an electrode comprising the collector surface and a reference electrode immersed in the bath, and carrying out a cathode activation by immersing an anode into the bath and setting up a current between said anode and the collector surface as the cathode, and repeating said cathode activation until the measured natural corrosion potential is less than the primary passivation potential.
Claim 6
Dependent Claim
32 words
A process according to claim 4 and including adjusting the natural corrosion potential of the alloy by previously pickling and/or abrading and/or degreasing the collector surface before prior to said cathode activation.
Claim 7
Dependent Claim
18 words
A process according to claim 1, 2 or 3 characterized in that said bath comprises an aqueous bath.
Claim 8
Dependent Claim
28 words
A process according to claim 1, 2 or 3 characterized in that the metalloid substance comprises a sulfur-based substance selected from the group consisting of sulfur or thiosulfate.
Claim 9
Dependent Claim
30 words
A process according to claim 1, 2 or 3 characterized in that the metalloid substance comprises a selenium-based substance selected from the group consisting of selenium dioxide and selenous acid.
Claim 10
Dependent Claim
23 words
A process according to claim 1, 2 or 3 characterized in that said acid bath contains at least 0.1% by weight of acid.
Claim 11
Dependent Claim
27 words
A process according to claim 1, 2 or 3 characterized in that the collector surface comprises a ferrite steel containing chromium and stabilized by niobium or titanium.
Claim 12
Dependent Claim
22 words
A process according to claim 1, 2 or 3 characterized in that the collector surface comprises austenite steel containing chromium and nickel.
References Cited (Backward Citations)
JPS5334651A
Cited
JPS5337151A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-04-24 | 1987-10-24 | 1988-04-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-04-24 | 1991-10-24 | 1992-04-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-04-24 | 1995-10-24 | 1996-04-24 | $7700.00 | Window Closed / Lapsed |