High temperature membrane
Assignee: University of Cincinnati
•
Filing: 1985-03-18
•
Granted: 1987-02-03
•
Expires: 2005-03-18
Abstract
Abstract The present invention concerns a method of making a silica-based membrane comprising the steps of: (1) pyrolyzing the material made of one of the class comprising polysilicone rubber, polysilane and polysiloxane at a temperature range of about 500 DEG C. to about 1000 DEG C. for about 2 hours (minimum) in an inert atmosphere; and (2) oxidizing the pyrolyzed material at a sufficient temperature range of about 300 DEG C. to about 1000 DEG C. to crosslink the material with oxygen. The membrane typically has a B.E.T. surface-area measurement of about 220 m2/g which indicates a highly porous membrane-about 40 to 70% porosity. The present invention may also be characterized by producing a pyrolyzed membrane by the method described above, and coating the membrane with silicon material to fill in the large micropores, and repyrolyzing the coated membrane to produce a membrane having extremely small micropores to assure that such gases as hydrogen and helium can be separated by the membrane product of the present invention to a high level of selectivity.
Inventors
- 👤 Kew-Ho Lee
- 👤 Soon-Jai Khang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 00:45
CPC Classifications
B; B01; B01D; B01D67/00; B01D67/0039; B01D67/0067; B01D69/00; B01D69/04; B01D71/00; B01D71/02; B01D71/0213; C; C04; C04B; C04B35/00; C04B35/01; C04B35/14; C04B38/00; C04B38/0022; B01D2325/00; B01D2325/02; C04B2111/00; C04B2111/00474; C04B2111/00793; C04B2111/00801
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
133 words
A method of forming a membrane capable of withstanding high temperatures for separating gases comprising the steps of: (1) pyrolyzing a silicon-based material having hydrocarbons and SiO chains in its structure to drive off substantially all hydrocarbons, said pyrolyzed silicon-based material consisting essentially of loosely connected SiO chains, said pyrolyzing being conducted at a temperature range of from about 500° C. to about 1000° C., for a minimum duration of about 2 hours, in an inert gaseous atmosphere under positive pressure; and (2) oxidizing said pyrolyzed silicon-based material in an oxidizing atmosphere to crosslink said SiO radicals to form silica, said oxidizing being conducted at a temperature from about 300° C. to about 1000° C., for a minimum duration of about 2 hours, thereby forming a porous membrane capable of withstanding high temperatures.
Claim 2
Independent Claim
133 words
A method of forming a membrane capable of withstanding high temperatures for separating gases comprising the steps of: (1) pyrolyzing a silicon-based material having hydrocarbons and SiO chains in its structure to drive off substantially all hydrocarbons, said pyrolyzed silicon-based material consisting essentially of loosely connected SiO chains, said pyrolyzing being conducted at a temperature range of from about 500° C. to about 1000° C., for a minimum duration of about 2 hours, in an inert gaseous atmosphere under positive pressure; and (2) oxidizing said pyrolyzed silicon-based material in an oxidizing atmosphere to crosslink said SiO radicals to form silica, said oxidizing being conducted at a temperature from about 300° C. to about 1000° C., for a minimum duration of about 2 hours, thereby forming a porous membrane capable of withstanding high temperatures.
Claim 3
Dependent Claim
39 words
The method of claim 1, including the step of re-pyrolyzing said oxidized silica membrane in an inert gaseous atmosphere at a temperature range from about 500° C. to about 1000° C., for a minimum duration of about 2 hours.
Claim 4
Dependent Claim
50 words
The method of claim 2, wherein said re-pyrolyzed silica material is coated with a second silicon material to fill in the micropores, and further re-pyrolyzed in an inert gaseous atmosphere at a temperature range of from 500° C. to about 1000° C. for a minimum duration of about 2 hours.
Claim 5
Dependent Claim
49 words
The method of claim 1, wherein said pyrolyzed silica material is coated with a second silicon material to fill in the micropores, and re-pyrolyzed in an inert gaseous atmosphere at a temperature range of from 500° C. to about 1000° C. for a minimum duration of about 2 hours.
Claim 6
Dependent Claim
16 words
The method of claim 1, wherein said silicon-based material is one of polysilicone rubber, and polysiloxanes.
Claim 7
Dependent Claim
26 words
The method of claim 1, wherein said inert gaseous atmosphere is anyone of the class consisting of nitrogen, carbon dioxide, helium, argon, neon, and mixtures thereof.
Claim 8
Dependent Claim
22 words
The method of claim 1, wherein the pyrolyzation temperatures is about 850° C. and the duration of pyrolysis is about 4 hours.
Claim 9
Dependent Claim
13 words
The method of claim 1, wherein said silicon-based material is tubular in shape.
Claim 10
Dependent Claim
11 words
The method of claim 1, wherein said oxidizing atmosphere is air.
Claim 11
Dependent Claim
11 words
The method of claim 1, wherein the oxidizing atmosphere is oxygen.
Claim 12
Dependent Claim
19 words
The method of claim 1, wherein the said silica membrane has a porosity of about 40% to about 70%.
Claim 13
Dependent Claim
19 words
The method of claim 1, wherein the silica membrane has a B.E.T. surface-area measurement of 200 m 2 /g.
Claim 14
Dependent Claim
20 words
The method of claim 1, wherein said pyrolyzed silicon-based material does not shrink more than 10% in size during pyrolysis.
Claim 15
Dependent Claim
17 words
The method of claim 4, wherein said second silicon material contains silicone oil and a vulcanizing agent.
Claim 16
Dependent Claim
16 words
The method of claim 14, wherein said vulcanizing agent is an organic peroxide, zinc, or platinum.
Claim 17
Dependent Claim
26 words
The method of claim 15, wherein said vulcanizing agent is about 1% by weight of the total composition of said silicone oil and said vulcanizing agent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-02-02 | 1990-08-04 | 1991-02-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-02-02 | 1994-08-04 | 1995-02-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-02-02 | 1998-08-04 | 1999-02-03 | $7700.00 | Window Closed / Lapsed |