Process for producing a cutting base

Claim 2

Process for producing a sound recording cutting base, comprising: precipitating a cuttable copper layer on a substrate from an electroplating bath, the copper layer having an initial grain size and having recrystallizing characteristics as a result of the bath's composition, convection and current density, characterized in that in order to extend recrystallization time, substances are added to the bath which, by their incorporation in the copper layer, stabilize the latter in such a manner that recrystallization is prevented or delayed, said substances including leveling agents added in effective amounts to prevent formation of large-grain crystals of copper having a grain size which substantially exceeds the initial grain-size.

Claim 3

Process according to claim 1, wherein the leveling agents added to the bath are organic substances which, by their incorporation in the copper layer, influence predominantly recrystallization behavior and not copper layer hardness.

Claim 4

Process according to claim 1, wherein the substances added to the bath further include inorganic substances having precipitation potentials adapted to that for copper in such a way that substantially smaller quantities of these inorganic substances are precipitated compared to the quantity of copper.

Claim 5

Process according to claim 1, wherein the substances added to the bath further include one or more of arsenic, bismuth, and antimony.

Claim 6

Process according to claim 1, wherein said leveling agents are added to the bath in amounts ranging from an amount effective to extend the recrystallization time to an amount sufficiently small to effectively prevent hardening of the copper layer under the conditions of the process.

Claim 7

Process according to claim 1, wherein said leveling agents are added to the bath in amounts ranging from 0.15 to 1.5 milliliters per liter of bath.

Claim 8

Process according to claim 1, wherein said leveling agents comprise from 0.05 to 0.5 milliliters per liter of bath of N,N-phenylmethylcarbamide methylene diethyl dithiocarbamine and from 0.1 to 1 milliliters per liter of bath of dyestuffs containing cationic N compounds.

Claim 9

In a process for producing copper cutting plates having a characteristic cuttability time for sound recording including the steps of providing an electroplatable substrate and a copper electroplating bath, the bath having a composition, a convection characteristic, and a current density; and electrolytically precipitating a cuttable copper layer onto the substrate, the copper layer having recrystallization characteristics which are a function of the composition, the convection characteristic, and the current density of the bath, which recrystallization characteristics include a recrystallization time during which the copper layer recrystallizes from an initial, newly precipitated state having an initial crystal grain size to a second state having a second crystal grain size, which second grain size is substantially larger than the initial grain size, the improvement comprising: adding organic leveling agents to the bath, which organic leveling agents are incorporated into the copper layer during the electrolytic precipitation thereof, in amounts effective to extend the recrystallization time by at least delaying recrystallization to the second state whereby the characteristic cuttability time of the copper cutting plates is increased.

Claim 10

In a process for producing copper cutting plates having a characteristic cuttability time for sound recording including the steps of providing an electroplatable substrate and a copper electroplating bath, the bath having a composition, a convection characteristic, and a current density; and electrolytically precipitating a cuttable copper layer onto the substrate, the copper layer having recrystallization characteristics which are a function of the composition, the convection characteristic, and the current density of the bath, which recrystallization characteristics include a recrystallization time during which the copper layer recrystallizes from an initial, newly precipitated state having an initial crystal grain size to a second state having a second crystal grain size, which second grain size is substantially larger than the initial grain size, the improvement comprising: adding organic leveling agents to the bath, which organic leveling agents are incorporated into the copper layer during the electrolytic precipitation thereof, in amounts effective to extend the recrystallization time by at least delaying recrystallization to the second state whereby the characteristic cuttability time of the copper cutting plates is increased.

Claim 11

The process according to claim 8, wherein said leveling agents are added to the bath in amounts ranging from 0.15 to 1.5 milliliters per liter of bath.

Claim 12

The process according to claim 8, wherein said leveling agents are added to the bath in amounts ranging from 0.05 to 0.5 milliliters per liter of bath of N,N-phenylmethylcarbamide methylene diethyl dithiocarbamine and from 0.1 to 1 milliliters per liter of bath of dyestuffs containing cationic N compounds.

Claim 13

The process according to claim 8, wherein inorganic substances are additionally added to the bath, the inorganic substances having precipitation potentials adapted to that for copper so that a substantially smaller quantity of same are precipitated compared to the quantity of copper during the electrolytic precipitation step.

Claim 14

The process according to claim 11, wherein the inorganic substances added to the bath are selected from among arsenic, bismuth, antimony, and mixtures thereof.

Claim 15

The process according to claim 8, wherein the organic leveling agents are added to the bath in amounts effective to at least delay recrystallization to the second state without substantially hardening the copper layer.

Claim 16

The process according to claim 8, wherein the organic leveling agents are added to the bath in amounts ranging from an amount effective to extend the recrystallization time to an amount sufficiently small to effectively prevent hardening of the copper layer.

Claim 17

The process according to claim 8, wherein the bath further comprises from 50 to 200 milligrams per liter of antimony fluoride.