Abstract
Abstract Heat shrinkable thermoplastic compositions are prepared by blending an ethylene copolymer resin with a rubber and dynamically vulcanizing the rubber. The ethylene copolymer resin is a copolymer of ethylene with an alkyl ester of an alpha, beta monoethylenically unsaturated monocarboxylic acid as well as copolymers of ethylene with the acid per se. The preferred copolymer is ethylene-vinyl-acetate copolymer. The preferred rubber is halogenated butyl rubber. Uncured rubber can be included in the composition.
Inventors
- 👤 Donald R. Hazelton
- 👤 Robert C. Puydak
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 13:49
CPC Classifications
C; C08; C08L; C08L21/00; B; B29; B29C; B29C61/00; B29C61/003; C08L23/00; C08L23/02; C08L23/04; C08L23/08; C08L23/0846; C08L23/0853; C08L23/26; C08L23/28; C08L23/283; B29K; B29K2021/00; B29K2023/00; B29K2023/04; B29K2023/06; B29K2023/08; B29K2023/083
Claims Analysis
Total Claims: 35
Claim 1
Independent Claim
101 words
A heat shrinkable, thermoplastic elastomeric composition comprising a polyolefin resin wherein the polyolefin resin comprises an ethylene copolymer resin and a butyl or halogenated butyl rubber wherein at least a part of the rubber is dynamically vulcanized to a fully cured state in the presence of the polyolefin resin except that the use of peroxide cure systems are specifically excluded and wherein said ethylene copolymer resin is selected from the group consisting of copolymers of ethylene and vinyl acetate, copolymers of ethylene with an alkyl ester of an alpha, beta monoethylenically unsaturated monocarboxylic acid and copolymers of ethylene with said acid.
Claim 2
Dependent Claim
101 words
A heat shrinkable, thermoplastic elastomeric composition comprising a polyolefin resin wherein the polyolefin resin comprises an ethylene copolymer resin and a butyl or halogenated butyl rubber wherein at least a part of the rubber is dynamically vulcanized to a fully cured state in the presence of the polyolefin resin except that the use of peroxide cure systems are specifically excluded and wherein said ethylene copolymer resin is selected from the group consisting of copolymers of ethylene and vinyl acetate, copolymers of ethylene with an alkyl ester of an alpha, beta monoethylenically unsaturated monocarboxylic acid and copolymers of ethylene with said acid.
Claim 3
Dependent Claim
44 words
The composition according to claim 1 wherein the ethylene copolymer resin comprises about 25 to 100 wt% of the polyolefin resin and an additional resin having a melting point of less than 126° C. comprises 0 to about 75 wt% of the polyolefin resin.
Claim 4
Dependent Claim
23 words
The composition of claim 1 wherein the polyolefin resin comprises about 20 to about 90 wt% of the resin/rubber component of the composition.
Claim 5
Dependent Claim
23 words
The composition of claim 1 wherein the vulcanized rubber comprises about 10 to about 40 wt% of the resin/rubber component of the composition.
Claim 6
Dependent Claim
21 words
The composition according to claim 2 wherein the additional resin is selected from the group consisting of LDPE, LLDPE and polybutylene.
Claim 7
Dependent Claim
23 words
The composition according to claim 1 wherein the rubber comprises about 20 to about 75 wt% of the resin/rubber component of the composition.
Claim 8
Dependent Claim
20 words
The composition according to claim 6 wherein the rubber comprises about 40 to about 60 wt% of the resin/rubber component.
Claim 9
Dependent Claim
14 words
The composition according to claim 1 wherein the rubber is a halogenated butyl rubber.
Claim 10
Dependent Claim
15 words
The composition according to claim 8 wherein the halogenated butyl rubber is chlorinated butyl rubber.
Claim 11
Dependent Claim
15 words
The composition according to claim 8 wherein the halogenated butyl rubber is brominated butyl rubber.
Claim 12
Dependent Claim
21 words
The composition according to claim 8 wherein a vulcanizing agent comprising ZnO is utilized in the dynamic vulcanization of the rubber.
Claim 13
Dependent Claim
13 words
The composition according to claim 1 wherein an inorganic filler is incorporated therein.
Claim 14
Dependent Claim
15 words
The composition according to claim 12 wherein the organic filler is calcium carbonate or clay.
Claim 15
Dependent Claim
14 words
The composition according to claim 1 wherein the polyolefin resin is an ethylene-vinylacetate copolymer.
Claim 16
Dependent Claim
20 words
The composition according to claim 14 wherein the vinylacetate content of the copolymer is about 2 to about 30 wt%.
Claim 17
Dependent Claim
20 words
The composition according to claim 15 wherein the vinylacetate content of the copolymer is about 9 to about 27 wt%.
Claim 18
Dependent Claim
14 words
The composition according to claim 1 wherein the ethylene copolymer is an ethylene-methylacrylate copolymer.
Claim 19
Dependent Claim
22 words
The composition according to claim 1 having incorporated therein 0 to about 25 wt%, based on total rubber, of an uncured rubber.
Claim 20
Dependent Claim
24 words
The composition according to claim 18 wherein the uncured rubber comprises about 5 to bout 20 wt% of the total rubber in the composition.
Claim 21
Dependent Claim
16 words
The composition according to claim 18 wherein the uncured rubber is an EPM, polyisobutylene or EPDM.
Claim 22
Dependent Claim
21 words
The composition according to claim 18 wherein the vulcanized rubber is a halogenated rubber and the uncured rubber is an EPM.
Claim 23
Dependent Claim
18 words
The composition according to claim 21 wherein the halogenated rubber is chlorinated butyl rubber or brominated butyl rubber.
Claim 24
Dependent Claim
124 words
A process for preparing a composition comprising a polyolefin resin, where the polyolefin resin is an ethylene copolymer resin, wherein said ethylene copolymer resin is selected from the group consisting of copolymers of ethylene and vinyl acetate, copolymers of ethylene with an alkyl ester of an alpha, beta monoethylenically unsaturated monocarboxylic acid and copolymers of ethylene with said acid and a fully vulcanized butyl or halogenated butyl rubber which comprises (a) blending the resin and rubber to be vulcanized at a temperature above the melting point of the resin; (b) adding a vulcanizing agent for the rubber, excluding a peroxide vulcanizing agent, to the resin/rubber blend; and (c) vulcanizing the rubber under dynamic vulcanization conditions for a time sufficient to fully vulcanize the rubber.
Claim 25
Dependent Claim
124 words
A process for preparing a composition comprising a polyolefin resin, where the polyolefin resin is an ethylene copolymer resin, wherein said ethylene copolymer resin is selected from the group consisting of copolymers of ethylene and vinyl acetate, copolymers of ethylene with an alkyl ester of an alpha, beta monoethylenically unsaturated monocarboxylic acid and copolymers of ethylene with said acid and a fully vulcanized butyl or halogenated butyl rubber which comprises (a) blending the resin and rubber to be vulcanized at a temperature above the melting point of the resin; (b) adding a vulcanizing agent for the rubber, excluding a peroxide vulcanizing agent, to the resin/rubber blend; and (c) vulcanizing the rubber under dynamic vulcanization conditions for a time sufficient to fully vulcanize the rubber.
Claim 26
Dependent Claim
18 words
The process according to claim 23 wherein an additional rubber not vulcanizable by the vulcanizing agent is incorporated.
Claim 27
Dependent Claim
25 words
The process according to claim 24 wherein the additional rubber is introduced during the blending of the resin and rubber and prior to dynamic vulcanization.
Claim 28
Dependent Claim
36 words
The process according to claim 24 wherein the additional rubber is added after the rubber to be vulcanized is fully vulcanized, blending being continued until the additional rubber is uniformly dispersed in the resin/vulcanized rubber blend.
Claim 29
Dependent Claim
58 words
The process according to claim 23 wherein an additional rubber is added to the composition after the rubber to be vulcanized is fully vulcanized; said additional rubber being vulcanizable by the vulcanization agent; provided, however, that the vulcanizing agent is fully consumed during the dynamic vulcanization step and is unavailable to vulcanize any part of the additional rubber.
Claim 30
Dependent Claim
57 words
The process according to claim 23 wherein an additional rubber which is vulcanizable by the vulcanizing agent is added to the rubber/resin blend after the rubber to be vulcanized is fully vulcanized; said vulcanizing agent being present in an amount sufficient to at least partially cure the additional rubber, but insufficient to fully vulcanize the additional rubber.
Claim 31
Dependent Claim
14 words
The process according to claim 24 wherein the additional rubber is EPM or polyisobutylene.
Claim 32
Dependent Claim
25 words
The process according to claim 27 wherein the rubber to be fully vulcanized is a halogenated rubber and the additional rubber is a halogenated rubber.
Claim 33
Dependent Claim
15 words
The process according to claim 30 wherein the halogenated rubbers are each chlorinated butyl rubber.
Claim 34
Dependent Claim
25 words
The process according to claim 28 wherein the rubber to be fully vulcanized is a halogenated rubber and the additional rubber is a halogenated rubber.
Claim 35
Dependent Claim
14 words
The process according to claim 32 wherein the rubbers are each chlorinated butyl rubber.
References Cited (Backward Citations)
US3037954A
Cited
US3592881A
Cited
US3758643A
Cited
US3904470A
Cited
US4104210A
Cited
US4087485A
Cited
US4130534A
Cited
US4212787A
Cited
US4350795A
Cited
US4202801A
Cited
US4348266A
Cited
JPS58145741A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-01-26 | 1990-07-28 | 1991-01-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-01-26 | 1994-07-28 | 1995-01-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-01-26 | 1998-07-28 | 1999-01-27 | $7700.00 | Window Closed / Lapsed |