Polypropylene blends having high impact strength and improved optical properties
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1976-08-16
•
Granted: 1978-05-02
•
Expires: 1996-08-16
Abstract
Abstract An impact polypropylene blend having an excellent balance of overall mechanical properties, particularly high impact strength, and significantly improved optical properties, comprising about 2 to about 22% by weight of an ethylene-propylene copolymer elastomer and about 1 to about 15% by weight of a low density polyethylene which are at least partially cured in the presence of polypropylene. The high impact polypropylene blends containing about 70 to about 95% by weight polypropylene have surprisingly good optical properties and are useful for making molded or extruded high clarity articles, such as containers, films, and the like.
Inventors
- 👤 Terrence Huff
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 09:13
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/02; C08L23/10; C08L23/12; C08K; C08K5/00; C08K5/04; C08K5/14; C08L2205/00; C08L2205/02; C08L2205/03; C08L2205/035; C08L23/04; C08L23/06; C08L23/16; C08L2310/00
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
103 words
A polypropylene blend having high impact strength and improved optical properties, comprising: about 70% to about 95% by weight of a polypropylene component, about 1% to about 15% by weight of a low density polyethylene component, said polyethylene having a density of no more than about 0.929 g/cc, and about 2% to about 22% by weight of an ethylene-propylene copolymer elastomer component having a combined ethylene content of at least 50 wt.%, based upon the weight of the elastomer component, the low density polyethylene and elastomer components being at least partially cured in the presence of at least a portion of the polyethylene.
Claim 2
Dependent Claim
103 words
A polypropylene blend having high impact strength and improved optical properties, comprising: about 70% to about 95% by weight of a polypropylene component, about 1% to about 15% by weight of a low density polyethylene component, said polyethylene having a density of no more than about 0.929 g/cc, and about 2% to about 22% by weight of an ethylene-propylene copolymer elastomer component having a combined ethylene content of at least 50 wt.%, based upon the weight of the elastomer component, the low density polyethylene and elastomer components being at least partially cured in the presence of at least a portion of the polyethylene.
Claim 3
Dependent Claim
36 words
The polypropylene blend of claim 1, wherein the polypropylene component is an isotactic polypropylene of greater than 90% hot heptane insolubles having a melt flow rate within the range of from about 0.5 to about 30.
Claim 4
Dependent Claim
60 words
The polypropylene blend of claim 1, wherein the ethylene-propylene copolymer elastomer component is selected from the group consisting of an ethylene-propylene binary copolymer, an ethylene-propylene-non-conjugated diene terpolymer elastomer and mixtures thereof having a combined ethylene content of from about 60 to about 80 wt.% and a Mooney viscosity of from about 20 to about 120 (M.L. 1+8' at 212° F.).
Claim 5
Dependent Claim
36 words
The polypropylene blend of claim 1, wherein the low density polyethylene component is a polyethylene having a density of about 0.915 to about 0.929 g/cc and a melt index of from about 2 to about 30.
Claim 6
Dependent Claim
53 words
The polypropylene blend of claim 1, wherein the low density polyethylene and ethylene-propylene copolymer elastomer components are cured with an organic peroxide, said organic peroxide being employed in an amount of from about 1/4 to a total amount required for substantially fully curing said components in the presence of said portion of polypropylene.
Claim 7
Dependent Claim
81 words
The blend of claim 1, wherein the portion of polypropylene cured in the presence of the low density polyethylene and ethylene-propylene copolymer elastomer components includes from about 0.1% to about 1.0% by weight, based upon the weight of said polypropylene portion, of a compound capable of preventing substantial degradation of the polypropylene with the elastomer and polyethylene being cured in the presence thereof, said compound being selected from the group consisting of sulfur, triallylcyanurate, triallylphosphate, tris (2,3-dibromopropyl) phosphate and mixtures thereof.
Claim 8
Dependent Claim
41 words
The polypropylene blend of claim 1, wherein the elastomer and low density polyethylene components are cured in the presence of from about 0.1 to about 0.5% by weight triallylcyanurate, based upon the weight of said elastomer and low density polyethylene components.
Claim 9
Independent Claim
127 words
A method for preparing a polypropylene blend having high impact strength and improved optical properties, said method comprising: mixing about 2 to about 22% by weight of an ethylene-propylene copolymer elastomer having a combined ethylene content of at least 50% by weight, based upon the weight of said elastomer, about 1 to about 15% by weight of a low density polyethylene having a density of no more than about 0.929 g/cc and an organic peroxide curing agent with about 70 to about 95% by weight of polypropylene; and subjecting the mixture to curing conditions, said organic peroxide curing agent being present in an amount of from about 1/4 to the total amount required to fully cure all of the elastomer and low density polyethylene in the mixture.
Claim 10
Independent Claim
127 words
A method for preparing a polypropylene blend having high impact strength and improved optical properties, said method comprising: mixing about 2 to about 22% by weight of an ethylene-propylene copolymer elastomer having a combined ethylene content of at least 50% by weight, based upon the weight of said elastomer, about 1 to about 15% by weight of a low density polyethylene having a density of no more than about 0.929 g/cc and an organic peroxide curing agent with about 70 to about 95% by weight of polypropylene; and subjecting the mixture to curing conditions, said organic peroxide curing agent being present in an amount of from about 1/4 to the total amount required to fully cure all of the elastomer and low density polyethylene in the mixture.
Claim 11
Dependent Claim
31 words
The method of claim 8, wherein the polypropylene is an isotactic polypropylene of greater than 90% hot heptane insolubles having a melt flow rate of from about 0.5 to about 30.
Claim 12
Dependent Claim
65 words
The method of claim 8, wherein the ethylene-propylene copolymer elastomer has a combined ethylene content of from about 60 to about 80 wt.%, based upon the weight of said elastomer and a Mooney viscosity of from about 20 to about 120 (M.L. 1+8' at 212° F.) and is selected from the group consisting of an ethylene-propylene binary copolymer, and ethylene-propylene-non-conjugated diene terpolymer and mixtures thereof.
Claim 13
Dependent Claim
32 words
The method of claim 8, wherein the low density polyethylene has a density of from about 0.915 to about 0.929 g/cc and a melt index of from about 2 to about 30.
Claim 14
Dependent Claim
58 words
The method of claim 8, wherein the elastomer, low density polyethylene and curing agent are initially mixed with about 3 to about 12 wt.% of the total amount of polypropylene of the blend and heated at said temperature for said period of time and then mixing the resulting mixture with the remainder of the polypropylene of the blend.
Claim 15
Dependent Claim
57 words
The method of claim 12, wherein the portion of polypropylene mixed with the elastomer, low density polyethylene and curing agent is initially mixed with from about 0.1 to about 1.0 wt.%, based upon the weight of said polypropylene portion, of a compound selected from the group consisting of sulfur, triallylcyanurate, triallylphosphate, tris (2,3-dibromopropyl) phosphate and mixtures thereof.
Claim 16
Dependent Claim
35 words
The method of claim 13, wherein the curing agent is present in an amount of from about 0.2 to about 0.3% by weight, based upon the weight of the elastomer and low density polyethylene present.
Claim 17
Dependent Claim
42 words
The method of claim 14, wherein about 0.1 to about 0.5 wt.% triallylcyanurate, based upon the weight of the elastomer and low density polyethylene present, is mixed therewith prior to subjecting the mixture to said elevated temperature for said period of time.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-05-01 | 1981-10-31 | 1982-05-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-05-01 | 1985-10-31 | 1986-05-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-05-01 | 1989-10-31 | 1990-05-02 | $7700.00 | Window Closed / Lapsed |