Surface-treated tire curing bladder, treatment composition therefore and method for curing tires
Assignee: Goodyear Tire and Rubber Co
•
Filing: 1985-08-06
•
Granted: 1987-01-13
•
Expires: 2005-08-06
Abstract
Abstract Lubricant composition comprised of clay, two polydimethylsiloxanes, poly(ethylene glycol and/or propylene glycol) and surfactant(s); tire cure bladder coated therewith; and a method of molding a rubber tire utilizing such a coated cure bladder.
Inventors
- 👤 Louis F. Comper
- 👤 Robert F. Scheiderich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 09:55
CPC Classifications
C; C10; C10M; C10M3/00; B; B29; B29C; B29C33/00; B29C33/56; B29C33/60; B29C33/62; B29C33/64; B29C43/00; B29C43/02; B29C43/10; B29C43/102; B29C43/104; C08; C08L; C08L83/00; C08L83/04; B29L; B29L2030/00; C08G; C08G77/00; C08G77/04; C08G77/12; C08G77/14; C08G77/16; C10M2201/00; C10M2201/02; C10M2207/00; C10M2207/10; C10M2207/12; C10M2207/121; C10M2207/122; C10M2207/125; C10M2207/129; C10M2227/00; C10M2227/04; C10M2229/00; C10M2229/04; C10M2229/041; C10N; C10N2010/00; C10N2010/04; C10N2010/14; C10N2010/16; C10N2020/00; C10N2020/01
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
210 words
A method of treating a cured rubber, expandable toroidal shaped, pneumatic tire cure bladder for a pneumatic or semi-pneumatic tire which comprises coating the outer, exposed surface of the bladder, optionally in about 80 to about 150 percent of its tire cure expanded position with a composition and drying said composition, wherein said composition comprises an aqueous mixture of the product of the mixture of (A) about 20 to about 40 parts by weight hydroxyl capped polydimethylsiloxane characterized by having a viscosity in the range of about 12 million to about 28 million centistokes at 25° C.; (B) about 35 to about 70 parts by weight of at least one silane selected from (i) a methyl hydrogen silane, characterized by having a viscosity in the range of about 20 to about 40 centistokes at 25° C., (ii) dimethyl hydrogen silane characterized by having a viscosity in the range of about 80 to about 120 centistokes at 25° C., (iii) methyl trimethoxy silane; (C) optionally, about 3 to about 12 parts by weight of a metal salt of an organic acid selected from at least one of zinc, magnesium, manganese and cobalt as acetates, stearates, propionates, glutionates and octoates thereof; and (D) about 10 to about 25 parts by weight surfactant.
Claim 2
Independent Claim
210 words
A method of treating a cured rubber, expandable toroidal shaped, pneumatic tire cure bladder for a pneumatic or semi-pneumatic tire which comprises coating the outer, exposed surface of the bladder, optionally in about 80 to about 150 percent of its tire cure expanded position with a composition and drying said composition, wherein said composition comprises an aqueous mixture of the product of the mixture of (A) about 20 to about 40 parts by weight hydroxyl capped polydimethylsiloxane characterized by having a viscosity in the range of about 12 million to about 28 million centistokes at 25° C.; (B) about 35 to about 70 parts by weight of at least one silane selected from (i) a methyl hydrogen silane, characterized by having a viscosity in the range of about 20 to about 40 centistokes at 25° C., (ii) dimethyl hydrogen silane characterized by having a viscosity in the range of about 80 to about 120 centistokes at 25° C., (iii) methyl trimethoxy silane; (C) optionally, about 3 to about 12 parts by weight of a metal salt of an organic acid selected from at least one of zinc, magnesium, manganese and cobalt as acetates, stearates, propionates, glutionates and octoates thereof; and (D) about 10 to about 25 parts by weight surfactant.
Claim 3
Dependent Claim
43 words
The method of claim 1 where the bladder is of the butyl-type of rubber and where, in said composition, the silane of (B) is methyl hydrogen silane and/or dimethyl hydrogen silane and the metal salt of (C) is zinc acetate and/or zinc stearate.
References Cited (Backward Citations)
US4554122A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-01-12 | 1990-07-14 | 1991-01-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-01-12 | 1994-07-14 | 1995-01-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-01-12 | 1998-07-14 | 1999-01-13 | $7700.00 | Window Closed / Lapsed |