Method of preparation of perovskite-type compounds
Assignee: Raytheon Co
•
Filing: 1985-06-11
•
Granted: 1987-01-13
•
Expires: 2005-06-11
Abstract
Abstract The present invention relates to a low temperature method of preparing a compound of the formula: ABO.sub.3 wherein A=Ba, Sr, Ca and Pb; and B=Ti, Zr and Hf, by (a) reacting a B-alkoxide, with a predetermined amount of aqueous A-hydroxide, (b) heating the reaction mixture to an initial temperature of 100° C.-250° C. at 1-40 atmospheres of pressure; (c) cooling the reaction mixture and thereafter, heating it to a subsequent temperature of approximately 40° C. to 60° C.; (d) dialyzing the cooled reaction product and recovering the tenate.
Inventors
- 👤 Ricardo C. Pastor
- 👤 Florentino V. Lee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 22:54
CPC Classifications
C; C01; C01G; C01G27/00; C01G23/00; C01G23/003; C01G23/006; C01G25/00; C01P; C01P2002/00; C01P2002/30; C01P2002/34; C01P2002/70; C01P2002/72; C01P2006/00; C01P2006/32; C01P2006/33; C01P2006/34; Y; Y10; Y10S; Y10S502/00; Y10S502/525
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
105 words
A low temperature method of preparing a compound of the formula: ABO.sub.3 wherein A=Ba, Sr, Ca and Pb; and B=Ti, Zr and Hf, comprising the steps of: (a) reacting a B-alkoxide with at least a stoichiometric amount of aqueous A-hydroxide; (b) heating the reaction mixture to an initial temperature of 100° C.-250° C. at 1-40 atmospheres of pressure to form a reaction product; (c) cooling the reaction product to a temperature below 40° C. and thereafter, heating it to a subsequent temperature of approximately 40° C. to 60° C.; (d) dialyzing the reaction product to form a dialyzate and a tenate and recovering the tenate.
Claim 2
Dependent Claim
105 words
A low temperature method of preparing a compound of the formula: ABO.sub.3 wherein A=Ba, Sr, Ca and Pb; and B=Ti, Zr and Hf, comprising the steps of: (a) reacting a B-alkoxide with at least a stoichiometric amount of aqueous A-hydroxide; (b) heating the reaction mixture to an initial temperature of 100° C.-250° C. at 1-40 atmospheres of pressure to form a reaction product; (c) cooling the reaction product to a temperature below 40° C. and thereafter, heating it to a subsequent temperature of approximately 40° C. to 60° C.; (d) dialyzing the reaction product to form a dialyzate and a tenate and recovering the tenate.
Claim 3
Dependent Claim
18 words
The method of claim 1 wherein the initial reaction temperature is 120° C. at 2 atmospheres of pressure.
Claim 4
Dependent Claim
16 words
The method of claim 2 wherein the initial heating step comprises heating in saturated steam pressure.
Claim 5
Dependent Claim
17 words
The method of claim 3 wherein the aqueous A-hydroxide is in 10% excess of the stoichiometric equivalent.
Claim 6
Dependent Claim
25 words
A low temperature method of preparing a perovskite-type compound of the formula: ABO.sub.3 according to claim 1 wherein A is barium and B is titanium.
Claim 7
Dependent Claim
18 words
The method of claim 5 wherein the initial reaction temperature is 120° C. at 2 atmospheres of pressure.
Claim 8
Dependent Claim
16 words
The method of claim 6 wherein the initial heating step comprises heating in saturated steam pressure.
Claim 9
Dependent Claim
18 words
The method of claim 7 wherein the aqueous barium hydroxide is in 10% excess of the stoichiometric equivalent.
Claim 10
Independent Claim
110 words
A method of producing barium titanate comprising the steps of: (a) reacting titanium iso-butoxide with at least a stoichiometric amount of aqueous barium hydroxide; (b) heating the reaction mixture to an initial temperature of 100° C.-250° C. at 1-40 atmospheres of pressure to form a reaction product; (c) cooling the reaction product to a temperature of below 40° C. and thereafter heating it to approximately 40° C. to 60° C.; (d) treating the reaction product with hydrochloric acid until a pH of 1-2 is attained; (e) dialyzing the reaction product into a dialyzate and tenate; (f) recovering the tenate and washing it with methylalcohol; and (g) drying the remaining residue.
Claim 11
Independent Claim
110 words
A method of producing barium titanate comprising the steps of: (a) reacting titanium iso-butoxide with at least a stoichiometric amount of aqueous barium hydroxide; (b) heating the reaction mixture to an initial temperature of 100° C.-250° C. at 1-40 atmospheres of pressure to form a reaction product; (c) cooling the reaction product to a temperature of below 40° C. and thereafter heating it to approximately 40° C. to 60° C.; (d) treating the reaction product with hydrochloric acid until a pH of 1-2 is attained; (e) dialyzing the reaction product into a dialyzate and tenate; (f) recovering the tenate and washing it with methylalcohol; and (g) drying the remaining residue.
Claim 12
Dependent Claim
18 words
The method of claim 9 wherein the initial reaction temperature is 120° C. at 2 atmospheres of pressure.
Claim 13
Dependent Claim
16 words
The method of claim 10 wherein the initial heating step comprises heating in saturated stem pressure.
Claim 14
Dependent Claim
18 words
The method of claim 11 wherein the aqueous barium hydroxide is in 10% excess of the stoichiometric equivalent.
References Cited (Backward Citations)
US4040983A
Cited
US4293534A
Cited
US4461844A
Cited
US4547355A
Cited
US4543341A
Cited
US4528613A
Cited
US4530031A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-01-12 | 1990-07-14 | 1991-01-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-01-12 | 1994-07-14 | 1995-01-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-01-12 | 1998-07-14 | 1999-01-13 | $7700.00 | Window Closed / Lapsed |