Composite metal articles
Assignee: Vida Weld Pty Ltd
•
Filing: 1984-06-19
•
Granted: 1987-01-13
•
Expires: 2004-06-19
Abstract
Abstract PCT No. PCT/AU84/00123 Sec. 371 Date Feb. 27, 1985 Sec. 102(e) Date Feb. 27, 1985 PCT Filed Jun. 19, 1984 PCT Pub. No. WO85/00308 PCT Pub. Date Jan. 31, 1985.A method of forming a composite article having a first and a second metal components, and a resultant composite metal article, wherein a flux coating is applied over at least a substantially oxide-free bond surface of the first component, the first component with said flux coating is preheated and, with said first component positioned in a mould to fill a portion of a cavity of the mould, a melt for providing the second component is poured into the mould so as to flow over said bond surface; the first component being preheated to a first temperature and the melt being poured at a second temperature such that, on flowing over the bond surface, the melt displaces said flux coating and wets said bond surface, and that such initial temperature equilibration between said surface and the melt results in an interface temperature therebetween at least equal to the liquidus temperature of the melt, thereby resulting on solidification of the melt in attainment of a bond between the components.
Inventors
- 👤 Ian R. Sare
- 👤 Ian D. Henderson
- 👤 Teunis Heijkoop
- 👤 Michael R. Bosworth
- 👤 Ronald E. Aspin
- 👤 Brian K. Arnold
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 18:29
CPC Classifications
B; B22; B22D; B22D19/00; B22D19/16; B22D19/08
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
202 words
A method of forming a composite article having first and second metal components, wherein said first component is a ferrous metal and said second component is a ferrous metal or cobalt base alloy comprising the steps of: (a) applying a flux coating over a substantially oxide-free bond surface of said first component; (b) preheating said first component in a mould in which said first component is positioned to a preheat temperature of about 350° C. to about 800° C.; and (c) pouring a melt of said second metal to provide said second component, said melt being poured at a superheated temperature and such that said melt flows over said bond surface to thereby displace said flux coating from said bond surface and wet said bond surface, said superheat temperature being substantially in excess of said preheat temperature, whereby said melt raises the temperature of said bond surface to achieve an initial temperature equilibrium between said surface and the melt, and a substantially instantaneous interface temperature therebetween which is at least equal to the liquidus temperature of the melt, such that on solidification of the melt a bond between the components is attained substantially in the absence of fusion of said bond surface.
Claim 2
Independent Claim
202 words
A method of forming a composite article having first and second metal components, wherein said first component is a ferrous metal and said second component is a ferrous metal or cobalt base alloy comprising the steps of: (a) applying a flux coating over a substantially oxide-free bond surface of said first component; (b) preheating said first component in a mould in which said first component is positioned to a preheat temperature of about 350° C. to about 800° C.; and (c) pouring a melt of said second metal to provide said second component, said melt being poured at a superheated temperature and such that said melt flows over said bond surface to thereby displace said flux coating from said bond surface and wet said bond surface, said superheat temperature being substantially in excess of said preheat temperature, whereby said melt raises the temperature of said bond surface to achieve an initial temperature equilibrium between said surface and the melt, and a substantially instantaneous interface temperature therebetween which is at least equal to the liquidus temperature of the melt, such that on solidification of the melt a bond between the components is attained substantially in the absence of fusion of said bond surface.
Claim 3
Dependent Claim
25 words
A method as defined in claim 1, wherein said first component comprises a ferrous metal selected from mild seel, low alloy steels and stainless steels.
Claim 4
Dependent Claim
26 words
A method as defined in claim 1, wherein said second component is selected from the group consisting of white cast irons, stainless steel, and cobalt-base alloys.
Claim 5
Dependent Claim
56 words
A method as defined in claim 3, wherein said first component is selected from the group consisting of mild steels, alloy steels, including stainless steels, and cast irons including chromium white cast iron, and wherein said second component is a white cast iron having from 2.0 to 5.0 wt.% carbon and chromium up to 30 wt.%.
Claim 6
Dependent Claim
23 words
A method as defined in claim 4, wherein chromium is present in excess of 14 wt.%, such as from 25 to 30 wt.%.
Claim 7
Dependent Claim
221 words
A method as defined in claim 4, wherein said white cast iron has a composition selected from the group consisting of: (a) 2.4 to 3.6 wt.% carbon, 0.5 to 1.5 wt.% manganese, 1.0 wt.% maximum silicon, 14 to 17 wt.% chromium and 1.5 to 3.5 wt.% molybdenum, the balance apart from incidental impurities being iron; (b) 2.3 to 3.0 wt.% carbon, 0.5 to 1.5 wt.% manganese, 1.0 wt.% maximum silicon, 23 to 30 wt.% chromium, and 1.5 wt.% maximum molybdenum, the balance apart from incidental impurities being iron; (c) 2.5 to 4.5 wt.% carbon, 2.5 to 3.5 wt.% manganese, 1.0 wt.% maximum silicon, 25 to 29 wt.% chromium, and 0.5 to 1.5 wt.% molybdenum, the balance apart from incidental impurities being iron; (d) 4.0 to 5.0 wt.% carbon, 1.0 wt.% maximum manganese, 0.5 to 1.5 wt.% silicon, 18 to 25 wt.% chromium, 5.0 to 7.0 wt.% molybdenum, 0.5 to 1.5 wt.% vanadium, 5.0 to 10.0 wt.% niobium, and 1.0 to 5.0 wt.% tungsten, the balance apart from incidental impurities being iron; and (e) 3.5 to 4.5 wt.% carbon, 1.0 wt.% maximum manganese, 0.5 to 1.5 wt.% silicon, 23 to 30 wt.% chromium, 0.7 to 1.1 wt.% molybdenum, 0.3 to 0.5 wt.% vanadium, 7.0 to 9.0 wt.% niobium, and 0.2 to 0.5 wt.% nickel, the balance apart from incidental impurities being iron.
Claim 8
Dependent Claim
99 words
A method as defined in claim 3, wherein said first component is selected from the group consisting of mild steel and alloy steels including stainless steels and wherein said second component is an austenitic stainless steel having a composition selected from the group consisting of: (a) 0.08 wt.% maximum carbon, 18 to 21 wt.% chromium, 10 to 12 wt.% nickel, 2 to 3 wt.% molybdenum and, apart from incidental impurities, a balance of iron; and (b) 0.08 wt.% maximum carbon, 18 to 21 wt.% chromium, 8 to 11 wt.% nickel and, part from incidental impurities, a balance of iron.
Claim 9
Dependent Claim
136 words
A method as defined in claim 3, wherein said first component is selected from the group consisting of mild steel and alloy steels, and wherein said second component is a cobalt-base alloy having (Co, Cr) 7 C 3 carbides in an eutectic structure and a work hardenable matrix, obtained with a composition selected from the group consisting of: (a) 28 to 31 wt.% chromium, 3.5 to 5.5 wt.% tungsten, a maximum of 3.0 wt.% for each of iron and nickel, a maximum of 2.0 wt.% for each of manganese and silicon, 1.5 wt.% maximum molybdenum, 0.9 to 1.4 wt.% carbon and, apart from incidental impurities, a balance of cobalt; and (b) substantially 29 wt.% chromium, 6.3 wt.% tungsten, 2.9 wt.% iron, 9.0 wt.% nickel, 1.0 wt.% carbon and, apart from incidental impurities, a balance of cobalt.
Claim 10
Dependent Claim
35 words
A method as defined in claim 1 wherein said first component is preheated at least in part by flame heating applied within the mould cavity, and maintained until after pouring of the melt is complete.
Claim 11
Dependent Claim
27 words
A method as defined in claim 9, wherein said flame heating provides reducing conditions within the mould cavity at least until pouring of the melt is complete.
Claim 12
Dependent Claim
57 words
A method as defined in claim 1, wherein said first component is preheated at least in part by flame heating applied thereto in a drag component of the mould, prior to positioning of a cope portion of the mould, and said flame heating is terminated prior to positioning of said cope portion and pouring of the metal.
Claim 13
Dependent Claim
19 words
A method as defined in claim 1 wherein said flux is applied to said first component as a slurry.
Claim 14
Dependent Claim
19 words
A method as defined in claim 1 wherein said flux is applied to said first component as a powder.
Claim 15
Dependent Claim
32 words
A method as defined in claim 1, wherein said flux acts both to prevent oxidation of said surface of the first component and also to clean said surface of any oxide contamination.
Claim 16
Dependent Claim
35 words
A method as defined in claim 1, wherein the metal of the first component has a melting range which commences at a temperature equal to or in excess of the liquidus temperature of the melt.
Claim 17
Dependent Claim
33 words
A method as defined in claim 1, wherein the metal of the first component has a melting range substantially the same as that of the metal for the melt providing the second component.
References Cited (Backward Citations)
US39531A
Cited
GB1053913A
Cited
US2235199A
Cited
US2881491A
Cited
DE1290306B
Cited
GB888404A
Cited
GB928928A
Cited
GB977207A
Cited
GB1152370A
Cited
GB1247197A
Cited
SU558754A1
Cited
SU745592A1
Cited
GB2044646A
Cited
SU980952A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-01-12 | 1990-07-14 | 1991-01-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-01-12 | 1994-07-14 | 1995-01-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-01-12 | 1998-07-14 | 1999-01-13 | $7700.00 | Window Closed / Lapsed |