Unbonded PC steel strand
Assignee: KAWASAKI STEEL TECHNO-WIRE Corp A JAPANESE CORP
•
Filing: 1985-11-18
•
Granted: 1987-01-13
•
Expires: 2005-11-18
Abstract
Abstract An unbonded PC steel strand used for posttensioning concrete comprising a PC steel strand composed of a plurality of stranded wires, a zinc plated layer on the outer surface of the PC steel strand, a greaselike filler applied around the zinc plated layer, and a synthetic resin sheath covering the zinc and filler coated PC steel strand. A method of manufacturing the unbonded PC steel strand comprising steps of pickling and water washing the PC steel strand, coating the outer surface of the PC steel strand with flux, plating the outer surface of the PC steel strand with zinc, applying a greaselike corrosion inhibitor to the surface of the zinc plated layer and sheathing the PC steel strand with an outer synthetic resin sheath.
Inventors
- 👤 Masamitsu Takei
- 👤 Shigeo Shoji
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 13:40
CPC Classifications
D; D07; D07B; D07B1/00; D07B1/06; D07B1/0693; D07B1/14; D07B1/141; D07B1/144; D07B1/16; D07B1/162; E; E04; E04C; E04C5/00; E04C5/08; D07B2201/00; D07B2201/20; D07B2201/2015; D07B2201/2042; D07B2201/2043; D07B2201/2044; D07B2201/2045; D07B2501/00; D07B2501/20; D07B2501/2015; D07B2501/2023
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
101 words
An unbonded PC steel strand comprising a PC steel strand composed of a plurality of stranded wires, a zinc plated layer on the outer surface of the PC steel strand, said zinc plated layer having a thickness of 5-100 μm at the wire outer surface portion, and being breakable when the PC steel strand is subjected to the tension applied for posttensioning concrete, said thickness preventing breaking of said layer during manufacture, shipping, handling and storage, a greaselike or other anticorrosive lubricative filler covering the zinc plated layer, and a synthetic resin sheath covering the zinc plated, filler-covered PC steel strand.
Claim 2
Dependent Claim
101 words
An unbonded PC steel strand comprising a PC steel strand composed of a plurality of stranded wires, a zinc plated layer on the outer surface of the PC steel strand, said zinc plated layer having a thickness of 5-100 μm at the wire outer surface portion, and being breakable when the PC steel strand is subjected to the tension applied for posttensioning concrete, said thickness preventing breaking of said layer during manufacture, shipping, handling and storage, a greaselike or other anticorrosive lubricative filler covering the zinc plated layer, and a synthetic resin sheath covering the zinc plated, filler-covered PC steel strand.
Claim 3
Independent Claim
143 words
A method of manufacturing an unbonded PC steel strand comprising a PC steel strand composed of a plurality of stranded wires, a zinc layer plated on the outer surface of the PC steel strand, the plated layer having a thickness of 5-100 μm at the wire outer surface portion, a layer of greaselike or other anticorrosive lubricative filler applied on the outer surface of the zinc plated layer, and a synthetic resin sheath covering the zinc plated filler covered PC steel strand, which method comprises the steps of pickling and water washing the PC steel strand, coating the outer surface of the PC steel strand with flux, plating the outer surface of the PC steel strand with zinc, applying a greaselike corrosion inhibitor to the surface of the zinc plated layer, and sheathing the PC steel strand with an outer synthetic resin sheath.
Claim 4
Independent Claim
143 words
A method of manufacturing an unbonded PC steel strand comprising a PC steel strand composed of a plurality of stranded wires, a zinc layer plated on the outer surface of the PC steel strand, the plated layer having a thickness of 5-100 μm at the wire outer surface portion, a layer of greaselike or other anticorrosive lubricative filler applied on the outer surface of the zinc plated layer, and a synthetic resin sheath covering the zinc plated filler covered PC steel strand, which method comprises the steps of pickling and water washing the PC steel strand, coating the outer surface of the PC steel strand with flux, plating the outer surface of the PC steel strand with zinc, applying a greaselike corrosion inhibitor to the surface of the zinc plated layer, and sheathing the PC steel strand with an outer synthetic resin sheath.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-01-12 | 1990-07-14 | 1991-01-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-01-12 | 1994-07-14 | 1995-01-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-01-12 | 1998-07-14 | 1999-01-13 | $7700.00 | Window Closed / Lapsed |