Dense shaped articles consisting of polycrystalline hexagonal boron nitride and process for their manufacture by isostatic hot-pressing
Abstract
Abstract The invention is a shaped article of boron nitride having a density of at least 95% of the theoretical density which consists of polycrystalline hexagonal boron nitride in the form of a homogeneous isotropic microstructure and which has been manufactured from pure boron nitride powder without the concomitant use of sintering aids by isostatic hot-pressing in a vacuum-tight casing at temperatures of from about 1200° to 1500° C. under a pressure of from about 50 to 300 MPa. Boron nitride powders having a free boric oxide content of not more than 1.0% by weight and having a specific surface area of from 5 to 30 m 2 /g are used as starting material. The powders either are filled into prefabricated casings consisting of steel or glass and densified by vibration or are preshaped to form green bodies having pores open to the surface and then placed in prefabricated casings or coated with a material which forms a vacuum-tight casing. The powders or the preshaped green bodies in the vacuum-tight casings are then subjected to an isostatic hot-pressing process in a high-pressure zone using an inert gas such as argon or nitrogen, as the pressure-transfer medium.
Inventors
- 👤 Klaus Hunold
- 👤 Alfred Lipp
- 👤 Klaus Reinmuth
Bibliographic Details
Claims Analysis
Total Claims: 3References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1990-01-05 | 1990-07-07 | 1991-01-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1994-01-05 | 1994-07-07 | 1995-01-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1998-01-05 | 1998-07-07 | 1999-01-06 | $7700.00 | Window Closed / Lapsed |