Process for the intercalation of graphitic carbon employing sulfur trioxide
Assignee: Celanese Corp
•
Filing: 1985-05-28
•
Granted: 1986-12-30
•
Expires: 2005-05-28
Abstract
Abstract An improved procedure is provided for increasing the electrical conductivity of graphite via intercalation. It has been found that sulfur trioxide has the ability to substantially aid the intercalation of graphite by previously known intercalants such as (a) fluorosulfonic acid, chlorosulfonic acid, or mixtures thereof, (b) a boron trihalide, a tetrahalide of a Group IV element, a pentahalide of a Group V element, or mixtures thereof, and (c) mixtures of (a) and (b). Such presence of sulfur trioxide during the graphite intercalation reaction has been found to expedite the rate at which intercalation takes place and possibly enables the achievement of a greater electrical conductivity than would have otherwise been obtained. In a preferred embodiment the graphitic carbon is present within a carbonaceous fibrous material at the time of its intercalation and the resulting product is substantially electrically oriented along the axis of the fiber.
Inventors
- 👤 Ilmar L. Kalnin
- 👤 Harris A. Goldberg
- 👤 George J. Breckenridge, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 06:53
CPC Classifications
H; H01; H01B; H01B1/00; H01B1/04; C; C01; C01B; C01B32/00; C01B32/20; C01B32/21; C01B32/22
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
197 words
In a process for forming an intercalated electrically conducting composition comprising reacting graphite in a reaction zone under anhydrous conditions with a reactant selected from the group consistng of: (a) a sulfur-containing reactant selected from the group consisting of fluorosulfonic acid, chlorosulfonic acid, and mixtures thereof, (b) a halide reactant selected from the group consisting of boron trihalide, a tetrahalide of a Group IV element, a pentahalide of a Group V element, and mixtures thereof, and (c) mixtures of (a) and (b); the improvement of additionally providing in said reaction zone during at least a portion of said reaction while at a temperature of approximately 20° to 90° C. a sulfur trioxide reactant which is capable of aiding the increase in the electrical conductivity of the graphite with the proviso that when reactant (a) is present with said sulfur trioxide as a binary mixture the molar ratio is approximately 5:1 to 50:1, when reactant (b) is present with said sulfur trioxide as a binary mixture the molar ratio is approximately 0.05:1 to 1:1, and when reactants (a) and (b) are present with said sulfur trioxide as a ternary mixture the molar ratios are approximately 10:1:1 to 100:0.1:1.
Claim 2
Dependent Claim
197 words
In a process for forming an intercalated electrically conducting composition comprising reacting graphite in a reaction zone under anhydrous conditions with a reactant selected from the group consistng of: (a) a sulfur-containing reactant selected from the group consisting of fluorosulfonic acid, chlorosulfonic acid, and mixtures thereof, (b) a halide reactant selected from the group consisting of boron trihalide, a tetrahalide of a Group IV element, a pentahalide of a Group V element, and mixtures thereof, and (c) mixtures of (a) and (b); the improvement of additionally providing in said reaction zone during at least a portion of said reaction while at a temperature of approximately 20° to 90° C. a sulfur trioxide reactant which is capable of aiding the increase in the electrical conductivity of the graphite with the proviso that when reactant (a) is present with said sulfur trioxide as a binary mixture the molar ratio is approximately 5:1 to 50:1, when reactant (b) is present with said sulfur trioxide as a binary mixture the molar ratio is approximately 0.05:1 to 1:1, and when reactants (a) and (b) are present with said sulfur trioxide as a ternary mixture the molar ratios are approximately 10:1:1 to 100:0.1:1.
Claim 3
Dependent Claim
36 words
A process for forming an intercalated electrically conducting composition according to claim 1 wherein said graphite is in the form of a fiber and the resulting intercalated electrically conducting composition is electrically oriented along it axis.
Claim 4
Dependent Claim
22 words
An improved process for forming an intercalated electrically conducting composition according to claim 1 wherein said sulfur-containing reactant (a) is fluorosulfonic acid.
Claim 5
Dependent Claim
22 words
An improved process for forming an intercalated electrically conducting composition according to claim 1 wherein said halide reactant (b) is a fluoride.
Claim 6
Dependent Claim
43 words
An improved process for forming an intercalated electrically conducting composition according to claim 1 wherein said halide reactant (b) is a Group IV element tetrahalide selected from the group consisting of SiF 4 , HfF 4 , TiF 4 and ZrF 4 .
Claim 7
Dependent Claim
46 words
An improved process for forming an intercalated electrically conducting composition according to claim 1 wherein said halide reactant (b) is a Group V element pentahalide selected from the group consisting of PF 5 , NbF 5 , TaF 5 , AsF 5 and SbF 5 .
Claim 8
Dependent Claim
22 words
An improved process for forming an intercalated electrically conducting composition according to claim 1 wherein said halide reactant (b) is antimony pentafluoride.
Claim 9
Dependent Claim
31 words
An improved process for forming an intercalated electrically conducting composition according to claim 1 wherein said sulfur-containing reactant (a) is fluorosulfonic acid and said halide reactant (b) is SbF 5 .
Claim 10
Dependent Claim
51 words
An improved process for forming an intercalated electrically conducting composition according to claim 1 wherein said reactants (a) and (b) are present with said sulfur trioxide as a ternary mixture and wherein the molar ratios of reactant (a), reactant (b), and sulfur trioxide, provided in the reaction zone are approximately 50:0.5:1.
Claim 11
Dependent Claim
38 words
An improved process for forming an intercalated electrically conducting composition according to claim 1 wherein the contents of said reaction zone are provided at a temperature of approximately 25° to 35° C. during the course of said reaction.
Claim 12
Dependent Claim
143 words
An improved process for forming an intercalated electrically conducting fiber which is electrically oriented along its axis comprising reacting in an reaction zone while at a temperature of approximately 20° to 90° C. under anhydrous conditions a carbonaceous fibrous material comprising graphitic carbon with the following reactants: (a) a sulfur-containing reactant selected from the group consisting of fluorosulfonic acid, chlorosulfonic acid, and mixtures thereof, (b) a halide reactant selected from the group consisting of boron trihalide, a tetrahalide of a Group IV element, a pentahalide of a Group V element, and mixtures thereof, and (c) a sulfur trioxide, wherein the molar ratios of reactants (a), (b), and (c) provided in the reaction zone are approximately 10:1:1 to 100:0.1:1 and wherein the sulfur trioxide reactant is capable of substantially aiding the increase in the electrical conductivity of the carbonaceous fibrous material comprising graphitic carbon.
Claim 13
Dependent Claim
143 words
An improved process for forming an intercalated electrically conducting fiber which is electrically oriented along its axis comprising reacting in an reaction zone while at a temperature of approximately 20° to 90° C. under anhydrous conditions a carbonaceous fibrous material comprising graphitic carbon with the following reactants: (a) a sulfur-containing reactant selected from the group consisting of fluorosulfonic acid, chlorosulfonic acid, and mixtures thereof, (b) a halide reactant selected from the group consisting of boron trihalide, a tetrahalide of a Group IV element, a pentahalide of a Group V element, and mixtures thereof, and (c) a sulfur trioxide, wherein the molar ratios of reactants (a), (b), and (c) provided in the reaction zone are approximately 10:1:1 to 100:0.1:1 and wherein the sulfur trioxide reactant is capable of substantially aiding the increase in the electrical conductivity of the carbonaceous fibrous material comprising graphitic carbon.
Claim 14
Dependent Claim
27 words
An improved process for forming an intercalated electrically conducting carbonaceous fibrous material comprising graphitic carbon according to claim 11 wherein said sulfur-containing reactant (a) is fluorosulfonic acid.
Claim 15
Dependent Claim
27 words
An improved process for forming an intercalated electrically conducting carbonaceous fibrous material according to claim 11 comprising graphitic carbon wherein said halide reactant (b) is a fluoride.
Claim 16
Dependent Claim
44 words
An improved process for forming an intercalated electrically conducting carbonaceous fibrous material according to claim 11 wherein said reactant (b) is a Group IV element tetrahalide selected from the group consisting of SiF 4 , HfF 4 , TiF 4 and ZrF 4 .
Claim 17
Dependent Claim
47 words
An improved process for forming an intercalated electrically conducting carbonaceous fibrous material according to claim 11 wherein said reactant (b) is a Group V element pentahalide selected from the group consisting of PF 5 , NbF 5 , TaF 5 , AsF 5 and SbF 5 .
Claim 18
Dependent Claim
23 words
An improved process for forming an intercalated electrically conducting carbonaceous fibrous material according to claim 11 wherein said reactant (b) is antimony pentafluoride.
Claim 19
Dependent Claim
33 words
An improved process for forming an intercalated electrically conducting carbonaceous fibrous material according to claim 11 wherein said sulfur-containing reactant (a) is fluorosulfonic acid and the halide reactant (b) is SbF 5 .
Claim 20
Dependent Claim
34 words
An improved process for forming an intercalated electrically conducting carbonaceous fibrous material according to claim 11 where the molar ratios of reactants (a), (b) and (c) provided in the reaction zone are approximately 50:0.5:1.
Claim 21
Dependent Claim
38 words
An improved process for forming an intercalated electrically conducting composition according to claim 11 wherein the contents of said reaction zone are provided at a temperature of approximately 25° to 35° C. during the course of said reaction.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-29 | 1990-06-30 | 1990-12-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-29 | 1994-06-30 | 1994-12-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-29 | 1998-06-30 | 1998-12-30 | $7700.00 | Window Closed / Lapsed |