Heat-resistant high impact styrene resin, process for production thereof, and resin composition comprising said styrene resin
Assignee: DIC Corp
•
Filing: 1985-09-12
•
Granted: 1986-12-23
•
Expires: 2005-09-12
Abstract
Abstract This invention provides a styrene copolymer resin having heat resistance and impact resistance. The resin is a moldable thermoplastic resin obtained by copolymerizing 3 to 70% by weight of a rubbery polymer and 97 to 30% by weight in total of styrene and methacrylic acid, provided that the proportions of styrene and methacrylic acid are 97 to 65% by weight and 3 to 35% by weight, respectively. The styrene and methacrylic acid are partly grafted to the rubbery polymer.
Inventors
- 👤 Atsushi Hosoda
- 👤 Yoshikiyo Miura
- 👤 Takehisa Mizuno
- 👤 Tsuyoshi Morita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 04:52
CPC Classifications
C; C08; C08F; C08F279/00; C08F279/02; C08L; C08L51/00; C08L51/04
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
251 words
A moldable, thermoplastic rubber-modified styrene copolymer resin composition having heat resistance and impact strength, said composition comprising (1) a mixture composed of (i) a rubber-modified styrene copolymer resin obtained by copolymerizing 3 to 70% by weight of a rubbery polymer and 97 to 30% by weight in total of styrene, methacrylic acid and optionally another vinyl monomer copolymerizable with styrene and methacrylic acid, the proportions of styrene, methacrylic acid and the optional other vinyl monomer being 3 to 35% by weight of methacrylic acid and correspondingly from 97 to 65% by weight in total of styrene and the optional other vinyl monomer with the proviso that when a mixture of both styrene and the other vinyl monomer is used more than 50% by weight of the mixture is styrene, said styrene, methacrylic acid and the optional other vinyl monomer being partly grafted to the rubbery polymer, and (ii) a styrene/methacrylic acid copolymer resin composed of 97 to 65% by weight of styrene or a mixture of styrene and another vinyl monomer copolymerizable with styrene and methacrylic acid with the proviso that when said mixture is used the majority of said mixture is comprised of styrene, and 3 to 35% by weight of methacrylic acid, said composition containing 1 to 50% by weight of the rubbery polymer as dispersed particles having an average particle diameter of 0.1 to 0.8 micrometer, and 3 to 35% by weight of the methacrylic acid, and (2) 0.001 to 0.2% by weight, as silicon, of an organopolysiloxane.
Claim 2
Dependent Claim
251 words
A moldable, thermoplastic rubber-modified styrene copolymer resin composition having heat resistance and impact strength, said composition comprising (1) a mixture composed of (i) a rubber-modified styrene copolymer resin obtained by copolymerizing 3 to 70% by weight of a rubbery polymer and 97 to 30% by weight in total of styrene, methacrylic acid and optionally another vinyl monomer copolymerizable with styrene and methacrylic acid, the proportions of styrene, methacrylic acid and the optional other vinyl monomer being 3 to 35% by weight of methacrylic acid and correspondingly from 97 to 65% by weight in total of styrene and the optional other vinyl monomer with the proviso that when a mixture of both styrene and the other vinyl monomer is used more than 50% by weight of the mixture is styrene, said styrene, methacrylic acid and the optional other vinyl monomer being partly grafted to the rubbery polymer, and (ii) a styrene/methacrylic acid copolymer resin composed of 97 to 65% by weight of styrene or a mixture of styrene and another vinyl monomer copolymerizable with styrene and methacrylic acid with the proviso that when said mixture is used the majority of said mixture is comprised of styrene, and 3 to 35% by weight of methacrylic acid, said composition containing 1 to 50% by weight of the rubbery polymer as dispersed particles having an average particle diameter of 0.1 to 0.8 micrometer, and 3 to 35% by weight of the methacrylic acid, and (2) 0.001 to 0.2% by weight, as silicon, of an organopolysiloxane.
Claim 3
Dependent Claim
29 words
The resin composition of claim 1 wherein the grafting ratio of styrene, methacrylic acid and the optional other vinyl monomer grafted to the rubbery copolymer is 3 to 300%.
Claim 4
Dependent Claim
29 words
The resin composition of claim 1 wherein the rubber-modified styrene copolymer resin is obtained by emulsion polymerization of styrene and methacrylic acid in the presence of a polybutadiene latex.
Claim 5
Dependent Claim
38 words
The resin composition of claim 1 wherein the rubber-modified styrene copolymer resin is obtained by emulsion polymerization of styrene and methacrylic acid in the presence of a styrene/butadiene copolymer latex containing at least 60% by weight of butadiene.
Claim 6
Dependent Claim
102 words
The resin composition of claim 1 wherein the rubber-modified styrene copolymer resin (i) is obtained by copolymerizing 3 to 70% by weight of the rubbery polymer and 97 to 30% by weight in total of styrene, methacrylic acid, and another vinyl monomer copolymerizable with styrene and methacrylic acid, the proportions of styrene, methacrylic acid and the other vinyl monomer being 3 to 35% by weight of methacrylic acid and correspondingly from 97 to 65% by weight in total of styrene and the other vinyl monomer with the other vinyl monomer constituting from 1 to 20% by weight of the weight of styrene.
Claim 7
Dependent Claim
32 words
The resin composition of claim 5 wherein the other copolymerizable vinyl monomer is selected from the group consisting of alpha-methylstyrene, t-butylstyrene, halogen-substituted styrene, vinyltoluene, acrylonitrile, methacrylonitrile, alpha-chloroacrylonitrile, acrylic esters and methacrylic esters.
Claim 8
Dependent Claim
51 words
The resin composition of claim 1 wherein the organopolysiloxane (2) comprises a polymer having structural units represented by the following formula (III): ##STR2## wherein R 1 and R 2 are identical or different and represent alkyl, aryl or aralkyl groups, which may be substituted by hydroxyl, alkoxy, hydroxyalkyl or polyhydroxyalkylene groups.
Claim 9
Dependent Claim
17 words
The resin composition of claim 7 wherein the organopolysiloxane comprises dimethylpolysiloxane, methylphenylpolysiloxane diphenylpolysiloxane, methylbenzylpolysiloxane or mixtures thereof.
Claim 10
Dependent Claim
18 words
The resin composition of claim 7 wherein the organopolysiloxane has a viscosity of from 15 to 50,000 centistokes.
Claim 11
Dependent Claim
19 words
The resin composition of claim 1 which comprises from 0.002 to 0.8% by weight, as silicon, of said organopolysiloxane.
Claim 12
Dependent Claim
18 words
The resin composition of claim 1 which comprises 0.002 to 0.05% by weight, as silicon, of said organopolysiloxane.
Claim 13
Dependent Claim
32 words
The resin composition of claim 1 wherein the rubbery polymer of the rubber-modified styrene copolymer resin is selected from the group consisting of polybutadiene rubber, styrene/butadiene rubber, acrylonitrile/butadiene rubber, and ethylene/propylene/polyene rubber.
Claim 14
Dependent Claim
33 words
The resin composition of claim 1 wherein the weight ratio of the rubber-modified styrene copolymer resin (i) to the styrene/methacrylic acid copolymer resin (ii) in the mixture (1) is from 20:80 to 70:30.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-22 | 1990-06-23 | 1990-12-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-22 | 1994-06-23 | 1994-12-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-22 | 1998-06-23 | 1998-12-23 | $7700.00 | Window Closed / Lapsed |