Dielectric composition and laminated capacitor
Assignee: Kyocera Corp
•
Filing: 1986-01-09
•
Granted: 1986-12-09
•
Expires: 2006-01-09
Abstract
Abstract A dielectric ceramic composition prepared by adding 0.1 to 1.3% of B2O3, 1.0 to 3.0% of SiO2 and 0.5 to 3.0% of ZnO to a composition comprising 18.0 to 27.0% of BaTiO2, 31.6 to 36.3% of Nd2O3, 27.6 to 35.5% of TiO2, 2.5 to 8.1% of Bi2O3 and 5.6 to 9.0% of Pb3O4, all percentages being by weight. This dielectric composition has a high dielectric constant and a temperature coefficient controlled within a narrow range and can be fired at relatively low temperatures. Because of these properties, it is used as a multilayer ceramic capacitor in combination with an electrode composed of an Ag-Pd alloy containing a major amount of Ag.
Inventors
- 👤 Nobuo Yokoe
- 👤 Takashi Okawa
- 👤 Nobuyoshi Fujikawa
- 👤 Kazuyoshi Yamashita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 15:04
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/46; C04B35/462; H; H01; H01G; H01G4/00; H01G4/002; H01G4/018; H01G4/06; H01G4/08; H01G4/12; H01G4/1209; H01G4/1218
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
93 words
A dielectric ceramic composition prepared by adding 0.1 to 1.3% by weight of B 2 O 3 , 1.0 to 3.0% by weight of SiO 2 and 0.5 to 3.0% by weight of ZnO to a major proportion of a composition comprising 18.0 to 27.0% by weight of BaTiO 3 , 31.6 to 36.3% by weight of Nd 2 O 3 , 27.6 to 35.5% by weight of TiO 2 , 2.5 to 8.1% by weight of Bi 2 O 3 and 5.6 to 9.0% by weight of Pb 3 O 4 .
Claim 2
Dependent Claim
93 words
A dielectric ceramic composition prepared by adding 0.1 to 1.3% by weight of B 2 O 3 , 1.0 to 3.0% by weight of SiO 2 and 0.5 to 3.0% by weight of ZnO to a major proportion of a composition comprising 18.0 to 27.0% by weight of BaTiO 3 , 31.6 to 36.3% by weight of Nd 2 O 3 , 27.6 to 35.5% by weight of TiO 2 , 2.5 to 8.1% by weight of Bi 2 O 3 and 5.6 to 9.0% by weight of Pb 3 O 4 .
Claim 3
Dependent Claim
35 words
The composition of claim 1 wherein 0.3 to 0.9% by weight of B 2 O 3 , 1.5 to 2.5% by weight of SiO 2 and 1.0 to 2.5% by weight of ZnO are added.
Claim 4
Dependent Claim
225 words
A multilayer ceramic capacitor comprising (a) a laminated monolithic structure obtained by preparing a plurality of units each consisting of a thin layer of a dielectric ceramic composition and a thin layer of a metal paste formed as an internal electrode on the surface of the ceramic layer so that it reaches one end of the ceramic layer but does not reach the other end, stacking the units so that the metal pastereaching ends of the ceramic layers and the other ends are each alternately situated on the same side, pressbonding them, and sintering the entire assembly, and (b) external electrodes provided on both sides of the laminated structure; wherein said dielectric ceramic composition is a dielectric ceramic composition prepared by adding 0.1 to 1.3% by weight of B 2 O 3 , 1.0 to 3.0% by weight of SiO 2 and 0.5 to 3.0% by weight of ZnO to a major proportion of a composition comprising 18.0 to 27.0% by weight of BaTiO 3 , 31.6 to 36.3% by weight of Nd 2 O 3 , 27.6 to 35.5% of TiO 2 , 2.5 to 8.1% by weight of Bi 2 O 3 and 5.6 to 9.0% by weight of Pb 3 O 4 , and the internal electrode is made of a silver-palladium alloy in which silver is present in a major amount.
Claim 5
Dependent Claim
225 words
A multilayer ceramic capacitor comprising (a) a laminated monolithic structure obtained by preparing a plurality of units each consisting of a thin layer of a dielectric ceramic composition and a thin layer of a metal paste formed as an internal electrode on the surface of the ceramic layer so that it reaches one end of the ceramic layer but does not reach the other end, stacking the units so that the metal pastereaching ends of the ceramic layers and the other ends are each alternately situated on the same side, pressbonding them, and sintering the entire assembly, and (b) external electrodes provided on both sides of the laminated structure; wherein said dielectric ceramic composition is a dielectric ceramic composition prepared by adding 0.1 to 1.3% by weight of B 2 O 3 , 1.0 to 3.0% by weight of SiO 2 and 0.5 to 3.0% by weight of ZnO to a major proportion of a composition comprising 18.0 to 27.0% by weight of BaTiO 3 , 31.6 to 36.3% by weight of Nd 2 O 3 , 27.6 to 35.5% of TiO 2 , 2.5 to 8.1% by weight of Bi 2 O 3 and 5.6 to 9.0% by weight of Pb 3 O 4 , and the internal electrode is made of a silver-palladium alloy in which silver is present in a major amount.
Claim 6
Dependent Claim
25 words
The capacitor of claim 3 wherein the silver-palladium alloy contains 51 to 90% by weight of silver and 10 to 40% by weight of palladium.
Claim 7
Dependent Claim
20 words
The capacitor of claim 3 wherein the laminated assembly is sintered at a firing temperature of 1000° to 1050° C.
References Cited (Backward Citations)
US3760244A
Cited
US3757177A
Cited
US4097911A
Cited
US4335216A
Cited
US4485181A
Cited
US4536821A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-08 | 1990-06-09 | 1990-12-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-08 | 1994-06-09 | 1994-12-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-08 | 1998-06-09 | 1998-12-09 | $7700.00 | Window Closed / Lapsed |