Electrical contacts and methods of making contacts by electrodeposition
Assignee: BJA SYSTEMS Inc
•
Filing: 1985-09-11
•
Granted: 1986-12-09
•
Expires: 2005-09-11
Abstract
Abstract Methods for increasing the ductility and reducing the porosity and cracking tendency of a palladium or palladium-silver electrodeposit which comprises providing an underlayer of a palladium/nickel or palladium/cobalt alloy electrodeposit. Also dual layer composite electroplated deposits and their use in electrical contacts or connectors.
Inventors
- 👤 Fred I. Nobel
- 👤 James L. Martin
- 👤 Michael P. Toben
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 22:09
CPC Classifications
H; H01; H01H; H01H11/00; H01H11/04; H01H11/041; C; C25; C25D; C25D3/00; C25D3/02; C25D3/56; C25D3/567; C25D5/00; C25D5/10; C25D5/60; C25D5/623; H01H1/00; H01H1/02; H01H1/021; H01H1/023; H01H2011/046; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12583; Y10T428/1259; Y10T428/12771; Y10T428/12861; Y10T428/12868; Y10T428/12875; Y10T428/12896; Y10T428/12903; Y10T428/12944
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
126 words
A method for increasing the ductility and reducing the porosity or tendency for cracking in a dual layer palladium alloy electrodeposit upon a substrate which comprises: electrodepositing a first layer of a palladium/nickel or palladium/cobalt alloy comprising between about 20 and 95 weight percent palladium and between about 5 and 80 weight percent nickel or cobalt upon the substrate in a thickness of at least about 0.5 microinches to increase the ductility and reduce the porosity and tendency for cracking of the dual layer electrodeposit; and electrodepositing a second layer of palladium or a palladium/silver alloy upon said first layer in a thickness of greater than about 5 microinches for use as an electrical contact, said second layer having a thickness greater than said first layer.
Claim 2
Independent Claim
126 words
A method for increasing the ductility and reducing the porosity or tendency for cracking in a dual layer palladium alloy electrodeposit upon a substrate which comprises: electrodepositing a first layer of a palladium/nickel or palladium/cobalt alloy comprising between about 20 and 95 weight percent palladium and between about 5 and 80 weight percent nickel or cobalt upon the substrate in a thickness of at least about 0.5 microinches to increase the ductility and reduce the porosity and tendency for cracking of the dual layer electrodeposit; and electrodepositing a second layer of palladium or a palladium/silver alloy upon said first layer in a thickness of greater than about 5 microinches for use as an electrical contact, said second layer having a thickness greater than said first layer.
Claim 3
Dependent Claim
17 words
An article comprising a substrate and the dual layer electrodeposit produced by the method of claim 1.
Claim 4
Dependent Claim
17 words
The article of claim 2 wherein the metal substrate comprises copper, nickel, or one of their alloys.
Claim 5
Dependent Claim
84 words
A palladium or palladium/silver electrical contact comprising a substrate and a dual layer electrodeposit comprising at least about 0.5 microinches of a first layer of a palladium/nickel or palladium/cobalt alloy comprising between about 20 and 95 weight percent palladium and between about 5 and 80 weight percent nickel or cobalt and greater than about 5 microinches of a second layer of palladium or a palladium/silver alloy; said second layer being thicker than said frist layer and providing the electrical characteristics of the electrical contact.
Claim 6
Dependent Claim
84 words
A palladium or palladium/silver electrical contact comprising a substrate and a dual layer electrodeposit comprising at least about 0.5 microinches of a first layer of a palladium/nickel or palladium/cobalt alloy comprising between about 20 and 95 weight percent palladium and between about 5 and 80 weight percent nickel or cobalt and greater than about 5 microinches of a second layer of palladium or a palladium/silver alloy; said second layer being thicker than said frist layer and providing the electrical characteristics of the electrical contact.
Claim 7
Dependent Claim
22 words
The electrical contact of claim 4 wherein the first layer of the electrodeposit has a thickness of greater than about 5 microinches.
Claim 8
Dependent Claim
22 words
The electrical contact of claim 4 wherein the second layer of the electrodeposit has a thickness of greater than about 20 microinches.
Claim 9
Independent Claim
88 words
A method for reducing corrosion of a copper, nickel or copper/nickel alloy basis metal substrate during electroplating of palladium/silver alloys from an acidic, high chloride electroplating bath which comprises electroplating at least 0.5 microinches of a first layer of a palladium/nickel or palladium/cobalt alloy comprising between about 20 and 95 weight percent palladium and between about 5 and 80 weight percent nickel or cobalt upon the substrate prior to electroplating the palladium/silver alloy to reduce or prevent corrosion of the basis metal during electroplating of the palladium/silver alloy.
Claim 10
Independent Claim
88 words
A method for reducing corrosion of a copper, nickel or copper/nickel alloy basis metal substrate during electroplating of palladium/silver alloys from an acidic, high chloride electroplating bath which comprises electroplating at least 0.5 microinches of a first layer of a palladium/nickel or palladium/cobalt alloy comprising between about 20 and 95 weight percent palladium and between about 5 and 80 weight percent nickel or cobalt upon the substrate prior to electroplating the palladium/silver alloy to reduce or prevent corrosion of the basis metal during electroplating of the palladium/silver alloy.
Claim 11
Dependent Claim
20 words
The method of claim 7 wherein the thickness of the palladium/nickel or palladium/cobalt layer is at least about 10 microinches.
Claim 12
Independent Claim
133 words
A method for electroplating a dual layer palladium alloy deposit which comprises: electrodepositing a first layer of a palladium/nickel or palladium/cobalt alloy comprising between about 20 and 95 weight percent palladium and between about 5 and 80 weight percent nickel or cobalt upon a substrate in a thickness greater than about 0.5 microinches to increase the ductility and reduce the porosity and tendency for cracking in the dual layer electrodeposit; and electrodepositing a second layer of palladium or a palladium/silver alloy comprising between about 20 and 95 weight percent palladium and between about 5 and 80 weight percent silver upon said first layer in a thickness of at least about 5 microinches for use as an electrical contact; the thickness of said second layer being greater than the thickness of said first layer.
Claim 13
Independent Claim
133 words
A method for electroplating a dual layer palladium alloy deposit which comprises: electrodepositing a first layer of a palladium/nickel or palladium/cobalt alloy comprising between about 20 and 95 weight percent palladium and between about 5 and 80 weight percent nickel or cobalt upon a substrate in a thickness greater than about 0.5 microinches to increase the ductility and reduce the porosity and tendency for cracking in the dual layer electrodeposit; and electrodepositing a second layer of palladium or a palladium/silver alloy comprising between about 20 and 95 weight percent palladium and between about 5 and 80 weight percent silver upon said first layer in a thickness of at least about 5 microinches for use as an electrical contact; the thickness of said second layer being greater than the thickness of said first layer.
Claim 14
Dependent Claim
17 words
An article comprising a substrate and the dual layer electrodeposit produced by the method of claim 9.
Claim 15
Dependent Claim
86 words
A palladium/silver electrical contact comprising a substrate and a composite electrodeposit comprising greater than about 0.5 microinches of a first layer of a palladium/nickel or palladium/cobalt alloy comprising between about 20 and 95 weight percent palladium and between about 5 and 80 weight percent nickel or cobalt upon said substrate and at least about 5 microinches of a second layer of a palladium/silver alloy comprising between about 20 and 95 weight percent palladium and between about 5 and 80 weight percent silver upon said first layer.
Claim 16
Dependent Claim
86 words
A palladium/silver electrical contact comprising a substrate and a composite electrodeposit comprising greater than about 0.5 microinches of a first layer of a palladium/nickel or palladium/cobalt alloy comprising between about 20 and 95 weight percent palladium and between about 5 and 80 weight percent nickel or cobalt upon said substrate and at least about 5 microinches of a second layer of a palladium/silver alloy comprising between about 20 and 95 weight percent palladium and between about 5 and 80 weight percent silver upon said first layer.
Claim 17
Dependent Claim
24 words
The electrical contact of claim 11 wherein the palladium/nickel or palladium/cobalt layer of the electrodeposit has a thickness of at least about 10 microinches.
Claim 18
Dependent Claim
20 words
The electrical contact of claim 11 wherein the palladium/silver layer of the electrodeposit has a thickness of about 25-60 microinches.
Claim 19
Dependent Claim
24 words
The electrical contact of claim 11 wherein the palladium/silver alloy of the electrodeposit comprises between about 40 and 80 weight percent palladium, balance silver.
Claim 20
Dependent Claim
28 words
The electrical contact of claim 11 wherein the palladium/nickel or palladium/cobalt alloy of the electrodeposit comprises between about 50 and 95 weight percent palladium, balance nickel or cobalt.
Claim 21
Independent Claim
124 words
A method for making an electrical contact having a contact surface of palladium which comprises initially electrodepositing a first layer of a palladium/nickel or palladium/cobalt alloy comprising between about 20 and 95 weight percent palladium and between about 5 and 80 weight percent nickel or cobalt upon a substrate in a thickness of greater than 0.5 microinches before electroplating the palladium layer to increase the ductility and reduce the porosity and tendency for cracking in the dual layer electrodeposit; and electrodepositing a second layer of palladium upon said first layer in a thickness of at least about 5 microinches; the thickness of said second layer being greater than the thickness of said first layer, said second layer providing the electrical characteristics of the contact.
Claim 22
Independent Claim
124 words
A method for making an electrical contact having a contact surface of palladium which comprises initially electrodepositing a first layer of a palladium/nickel or palladium/cobalt alloy comprising between about 20 and 95 weight percent palladium and between about 5 and 80 weight percent nickel or cobalt upon a substrate in a thickness of greater than 0.5 microinches before electroplating the palladium layer to increase the ductility and reduce the porosity and tendency for cracking in the dual layer electrodeposit; and electrodepositing a second layer of palladium upon said first layer in a thickness of at least about 5 microinches; the thickness of said second layer being greater than the thickness of said first layer, said second layer providing the electrical characteristics of the contact.
Claim 23
Dependent Claim
17 words
An article comprising a substrate and the dual layer electrodeposit produced by the method of claim 16.
Claim 24
Dependent Claim
79 words
A palladium electrical contact comprising a substrate and a composite electrodeposit comprising a first layer of greater than 5 microinches of a palladium/nickel or palladium/cobalt alloy comprising between about 20 and 95 weight percent palladium and between about 5 and 80 weight percent nickel or cobalt and greate than 20 microinches and a second layer of palladium; the thickness of the second layer being greater than that of the first layer and providing the electrical characteristics of the contact.
Claim 25
Dependent Claim
79 words
A palladium electrical contact comprising a substrate and a composite electrodeposit comprising a first layer of greater than 5 microinches of a palladium/nickel or palladium/cobalt alloy comprising between about 20 and 95 weight percent palladium and between about 5 and 80 weight percent nickel or cobalt and greate than 20 microinches and a second layer of palladium; the thickness of the second layer being greater than that of the first layer and providing the electrical characteristics of the contact.
Claim 26
Dependent Claim
22 words
The electrical contact of claim 18 wherein the palladium/nickel layer of the electrodeposit has a thickness of at least about 10 microinches.
Claim 27
Dependent Claim
23 words
The electrical contact of claim 18 wherein the palladium layer of the electrodeposit has a thickness of between about 25 and 60 microinches.
Claim 28
Dependent Claim
24 words
The electrical contact of claim 18 wherein the palladium/nickel alloy of the electrodeposit comprises between about 50 and 95 weight percent palladium, balance nickel.
References Cited (Backward Citations)
CA440591A
Cited
US3053741A
Cited
US4100039A
Cited
JPS55154013A
Cited
US4269671A
Cited
US4465563A
Cited
US4478692A
Cited
US4529667A
Cited
US4463060A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-08 | 1990-06-09 | 1990-12-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-08 | 1994-06-09 | 1994-12-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-08 | 1998-06-09 | 1998-12-09 | $7700.00 | Window Closed / Lapsed |