Method for the application of a corrosion-protection layer containing protective-oxide-forming elements to the base body of a gas turbine blade and corrosion-protection layer on the base body of a gas turbine blade
Assignee: BBC Brown Boveri AG Switzerland
•
Filing: 1985-06-27
•
Granted: 1986-12-09
•
Expires: 2005-06-27
Abstract
Abstract Method for applying a corrosion-protection layer to the base body (1) of a gas turbine blade by embedding particles (3) of SiC in a metallic matrix by means of powder, paste or electrolytic/electrophoretic methods and compacting, welding or fusing and bonding the matrix-forming material to the base body (1) by means of hot-pressing, hot isostatic pressing or laser beam, electron beam or electric arc. Protective layers are formed which do not flake off and with high silicon content which is at least partially contained in the embedded, partly modified SiC particles (6) as a reservoir for the operation.
Inventors
- 👤 Mohamed Nazmy
- 👤 Robert Singer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 17:14
CPC Classifications
C; C23; C23C; C23C24/00; C23C24/08; C23C24/10; C23C24/103; B; B23; B23K; B23K35/00; B23K35/22; B23K35/24; B23K35/32; B23K35/327; F; F01; F01D; F01D5/00; F01D5/12; F01D5/28; F01D5/288; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12576; Y10T428/12771; Y10T428/12806; Y10T428/12826; Y10T428/12847; Y10T428/12854; Y10T428/12861; Y10T428/12931; Y10T428/12944; Y10T428/25; Y10T428/259; Y10T428/30
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
115 words
A method for applying a corrosion protection layer to a base body of a gas turbine blade, which comprises applying to said base body, silicon carbide particles together with a superalloy material in the form of particles or layers which forms a metallic matrix of the protective layer, compacting, pressing, and welding or fusing said matrix-forming material such that the protective layer matrix is firmly bonded to said base body, wherein silicon carbide particles are at least partially embedded in the form of fine particles which negligibly protrude above the surface of said protective layer matrix, and said silicon carbide particles partially react with said matrix-forming material so that some silicon migrates into said matrix.
Claim 2
Independent Claim
115 words
A method for applying a corrosion protection layer to a base body of a gas turbine blade, which comprises applying to said base body, silicon carbide particles together with a superalloy material in the form of particles or layers which forms a metallic matrix of the protective layer, compacting, pressing, and welding or fusing said matrix-forming material such that the protective layer matrix is firmly bonded to said base body, wherein silicon carbide particles are at least partially embedded in the form of fine particles which negligibly protrude above the surface of said protective layer matrix, and said silicon carbide particles partially react with said matrix-forming material so that some silicon migrates into said matrix.
Claim 3
Dependent Claim
43 words
Method according to claim 1, characterised in that the SiC and the material forming the metallic matrix of the protective layer are applied in the form of a powder mixture or a paste to the base body (1) of the gas turbine blade.
Claim 4
Dependent Claim
44 words
Method according to claim 1, characterised in that the SiC is deposited electrophoretically in particle form and the material forming the metallic matrix of the protective layer is simultaneously electrolytically deposited in layer form on the base body (1) of the gas turbine blade.
Claim 5
Dependent Claim
51 words
Method according to claim 1, characterised in that at least individual components of the material forming the metallic matrix of the protective layer are deposited electrolytically in a series of layers on the base body (1) of the gas turbine blade sequentially and alternately simultaneously with the electrophoretic deposition of SiC.
Claim 6
Dependent Claim
43 words
Method according to claim 1, characterised in that the superficial compacting, pressing and welding of the material forming the matrix take place by hot-pressing for 0.5 to 10 s at a temperature of 900° C. and a pressure of up to 500 Mpa.
Claim 7
Dependent Claim
97 words
Method according to claim 1, characterised in that the base body (1) of the gas turbine blade is subjected to a coarse-grain annealing before it is coated with a corrosion-protection layer and that the superficial compacting, pressing and welding of the material forming the matrix take place by hot-isostatic pressing of a powder mixture for 1/2-3 h at a temperature of 1200° C. and a pressure of 100-150 Mpa loaded into a soft-iron sheet body sealed on all sides and that the soft-iron sheet body is removed mechanically or chemically after the powder has been hot-isostatically pressed.
Claim 8
Dependent Claim
34 words
Method according to claim 1, characterised in that the said fusing of the material forming the matrix is accomplished by a laser beam (9) or an electron beam (10) or an electric arc (11).
Claim 9
Dependent Claim
63 words
Corrosion-protection layer on the base body of a gas turbine blade consisting of a metallic matrix and particles of protective-oxide-forming elements embedded in the latter, characterized in that the protective-oxide-forming element is silicon, which is present in the form of discretely embedded, partially modified SiC particles, wherein said SiC particles partially react with said matrix so that some silicon migrates into said matrix.
Claim 10
Dependent Claim
63 words
Corrosion-protection layer on the base body of a gas turbine blade consisting of a metallic matrix and particles of protective-oxide-forming elements embedded in the latter, characterized in that the protective-oxide-forming element is silicon, which is present in the form of discretely embedded, partially modified SiC particles, wherein said SiC particles partially react with said matrix so that some silicon migrates into said matrix.
Claim 11
Dependent Claim
27 words
Corrosion-protection layer according to claim 8, characterised in that the metallic matrix has approximately the same composition as the base body (1) of the gas turbine blade.
Claim 12
Dependent Claim
22 words
Corrosion-protection layer according to claim 8, characterised in that the metallic matrix consists of nickel or a nickel/chromium alloy or of cobalt.
References Cited (Backward Citations)
US3296693A
Cited
US3929590A
Cited
US3981062A
Cited
US4079552A
Cited
US4288495A
Cited
US4218494A
Cited
US4241135A
Cited
US4302300A
Cited
US4447466A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-08 | 1990-06-09 | 1990-12-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-08 | 1994-06-09 | 1994-12-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-08 | 1998-06-09 | 1998-12-09 | $7700.00 | Window Closed / Lapsed |