US4626198A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method and apparatus for producing dead burnt materials
Assignee: Fuller Co
•
Filing: 1985-09-20
•
Granted: 1986-12-02
•
Expires: 2005-09-20
Abstract
Abstract An improved process and apparatus for producing sintered material such as dead burned clay, dolomite, magnesite or periclase with the highest particle specific gravity capable from each material. A grinding mill produces raw material which is 100% minus 20 mesh. The ground raw material is supplied to a suspension type preheater and then to a stationary flash calcining system where the material is soft burned at temperatures in the range of 1000° to 1200° C. From the calcining system, the calcined material is immediately supplied to hot briquetting machine where briquettes or nodules are formed. The hot nodules at a temperature of approximately 800° C. are then immediately supplied to a rotary kiln which serves as a sintering furnace where the soft burned material is dead burnt at a temperature in the range of 1650° to 1850° C. Hot spent combustion gas from the sintering furnace is supplied to the calcining furnace to serve as preheated secondary air for combustion. The spent hot gas from the calcining furnace is used in the suspension preheater to preheat the raw material.
Inventors
- 👤 Sidney M. Cohen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 06:07
CPC Classifications
F; F27; F27B; F27B7/00; F27B7/20; F27B7/2016; F27B7/2025; F27B7/2033; C; C04; C04B; C04B2/00; C04B2/10; C04B2/102; Y; Y02; Y02P; Y02P40/00; Y02P40/40
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
79 words
An improved process for producing sintered materials such as dead burnt clay, dolomite, magnesite or periclase with a desired particle specific gravity comprising the steps of calcining raw materials while in suspension in a calcining furnace at a temperature in the range of approximately 1000° to 1200° C.; forming the calcined materials into nodules; supplying the thus formed nodules to a sintering furnace; and sintering the nodules at a temperature in the range of approximately 1650° to 1850° C.
Claim 2
Dependent Claim
79 words
An improved process for producing sintered materials such as dead burnt clay, dolomite, magnesite or periclase with a desired particle specific gravity comprising the steps of calcining raw materials while in suspension in a calcining furnace at a temperature in the range of approximately 1000° to 1200° C.; forming the calcined materials into nodules; supplying the thus formed nodules to a sintering furnace; and sintering the nodules at a temperature in the range of approximately 1650° to 1850° C.
Claim 3
Dependent Claim
27 words
An improved process of producing sintered materials according to claim 1 further comprising the step of supplying exhaust gases from the sintering furnace to the calcining furnace.
Claim 4
Dependent Claim
31 words
An improved process of producing sintered materials according to claim 2 further comprising the step of preheating the raw materials while in suspension in exhaust gases discharged from the calcining furnace.
Claim 5
Dependent Claim
31 words
An improved process of producing sintered materials according to claim 1 wherein the step of forming the calcined material into nodules is performed substantially immediately after the raw material is calcined.
Claim 6
Dependent Claim
42 words
An improved process or producing sintered materials according to claim 4 wherein the step of supplying the nodules to a sintered furnace is performed substantially immediately after the nodules are formed whereby the nodules are at a temperature of approximately 800° C.
Claim 7
Dependent Claim
26 words
An improved process of producing sintered material according to claim 5 further comprising the step of cooling the sintered material by direct contact with cooling air.
Claim 8
Dependent Claim
24 words
A process of producing sintered materials according to claim 6 further comprising the step of grinding the raw material to 100% minus 20 mesh.
Claim 9
Dependent Claim
173 words
Apparatus for producing dead burnt materials such as dolomite, magnesite or periclase comprising: a stationary calcining furnace having an inlet for raw material to be sintered, an inlet for fuel for combustion therein, an inlet for gas for combustion, and an outlet for spent combustion gas and entrained calcined material; a gas-solids separator having an inlet for spent combustion gas and entrained calcined material flow connected to the outlet of the calcining furnace, an outlet for spent combustion gas and an outlet for calcined material; means for forming said calcined material into nodules having an inlet flow connected to the outlet for calcined material of said gas-solids separator and an outlet for nodules of calcined material whereby the calcined material is nodulized while at a high temperature; and a sintering furnace having an inlet for fuel, an inlet for air for combustion, an inlet for nodules of calcined material flow connected to the outlet for nodules of said last named means, an outlet for dead burnt material and an outlet for combustion gas.
Claim 10
Dependent Claim
173 words
Apparatus for producing dead burnt materials such as dolomite, magnesite or periclase comprising: a stationary calcining furnace having an inlet for raw material to be sintered, an inlet for fuel for combustion therein, an inlet for gas for combustion, and an outlet for spent combustion gas and entrained calcined material; a gas-solids separator having an inlet for spent combustion gas and entrained calcined material flow connected to the outlet of the calcining furnace, an outlet for spent combustion gas and an outlet for calcined material; means for forming said calcined material into nodules having an inlet flow connected to the outlet for calcined material of said gas-solids separator and an outlet for nodules of calcined material whereby the calcined material is nodulized while at a high temperature; and a sintering furnace having an inlet for fuel, an inlet for air for combustion, an inlet for nodules of calcined material flow connected to the outlet for nodules of said last named means, an outlet for dead burnt material and an outlet for combustion gas.
Claim 11
Dependent Claim
36 words
Apparatus for producing dead burnt materials according to claim 8 further comprising duct means flow connecting the outlet for combustion gas of the sintering furnace to the inlet for gas for combustion of the calcining furnace.
Claim 12
Dependent Claim
88 words
Apparatus for producing dead burnt materials according to claim 9 further comprising preheater means having an inlet for fine ground raw material and an inlet for hot gases flow connected to the outlet for spent combustion gas of said gas-solids separator and an outlet for preheated raw material whereby the raw material and hot gases are in countercurrent contact with each other to thereby preheat the raw material and said outlet for preheated raw material is flow connected to the inlet for raw material of the calcining furnace.
Claim 13
Dependent Claim
79 words
Apparatus for producing dead burnt materials according claim 10 further comprising a cooler flow connected to the outlet for dead burnt material of the sintering furnace including means for supplying cooling air for direct heat exchange contact with hot dead burned material whereby the dead burnt material is cooled and the cooling air is heated and means for supplying at least some of the thus heated cooling air to the inlet for air for combustion of the sintering furnace.
Claim 14
Dependent Claim
23 words
Apparatus for producing dead burnt materials according to claim 11 further comprising means for grinding the raw material to 100% minus 20 mesh.
Claim 15
Dependent Claim
25 words
Apparatus for producing dead burnt materials according to claim 12 wherein said means for forming the calcined material into nodules is a hot briquetting machine.
Claim 16
Dependent Claim
43 words
An improved process for producing sintered material comprising the steps of calcining raw materials to be sintered in a calcining furnace; immediately forming the hot calcined materials into nodules; immediately supplying the thus formed nodules to a sintering furnace; and sintering the nodules.
Claim 17
Dependent Claim
43 words
An improved process for producing sintered material comprising the steps of calcining raw materials to be sintered in a calcining furnace; immediately forming the hot calcined materials into nodules; immediately supplying the thus formed nodules to a sintering furnace; and sintering the nodules.
References Cited (Backward Citations)
US1912894A
Cited
US3304188A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-12-01 | 1990-06-02 | 1990-12-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-12-01 | 1994-06-02 | 1994-12-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-12-01 | 1998-06-02 | 1998-12-02 | $7700.00 | Window Closed / Lapsed |