Method for depolymerizing polymers
Assignee: MOORE & MUNGER Inc DELAWARE Corp
•
Filing: 1985-02-08
•
Granted: 1986-11-25
•
Expires: 2005-02-08
Abstract
Abstract A method for depolymerizing a non-thermosetting polymer is described. The method comprises the steps of heating the polymer until it is molten and then reacting the molten polymer with oxygen in the absence of a catalyst at a temperature between about 270 DEG F. and about 415 DEG F. by sparging the molten material at a flow rate of at least 2 cubic feet per minute per 1000 pounds of polymer with oxygen-containing gas bubbles having a diameter of less than about 10.0 mm. Advantages of the invention include reduced reaction temperatures, reduced reaction times, elimination of the need for a catalyst, and improved end-products. Treatment of amorphous polypropylene and mixtures of alpha-olefins and Fischer-Tropsch waxes are preferred applications of the invention.
Inventors
- 👤 Janardan D. Upadhyaya
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 10:25
CPC Classifications
C; C08; C08F; C08F8/00; C08F8/50
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
97 words
A method for depolymerizing a meltable, organic polymer wherein said polymer is selected from the group consisting of polyolefins, Fischer-Tropsch waxes, petroleum waxes, and mixtures thereof, comprising the steps of heating the polymer until it is molten and then reacting the molten polymer with oxygen in the absence of a catalyst at a temperature between about 270° F. and about 415° F. by sparging the molten material at a flow rate of at least 2 cubic feet per minute per 1000 pounds of polymer with oxygen-containing gas bubbles having a diameter of less than about 10.0 mm.
Claim 2
Independent Claim
97 words
A method for depolymerizing a meltable, organic polymer wherein said polymer is selected from the group consisting of polyolefins, Fischer-Tropsch waxes, petroleum waxes, and mixtures thereof, comprising the steps of heating the polymer until it is molten and then reacting the molten polymer with oxygen in the absence of a catalyst at a temperature between about 270° F. and about 415° F. by sparging the molten material at a flow rate of at least 2 cubic feet per minute per 1000 pounds of polymer with oxygen-containing gas bubbles having a diameter of less than about 10.0 mm.
Claim 3
Dependent Claim
21 words
The method of claim 1 wherein the diameter of the gas bubbles is between about 0.5 mm and about 5.0 mm.
Claim 4
Dependent Claim
24 words
The method of claim 1 wherein the flow rate is between 2 and about 20 cubic feet per minute per 1000 pounds of polymer.
Claim 5
Dependent Claim
19 words
The method of claim 1 wherein the reaction between the molten polymer and oxygen is conducted at atmospheric pressure.
Claim 6
Dependent Claim
30 words
The method of claim 1 wherein the reaction is run at a temperature between about 25° F. and about 50° F. above the melting point of the polymer being depolymerized.
Claim 7
Dependent Claim
11 words
The method of claim 1 wherein the oxygen-containing gas is air.
Claim 8
Dependent Claim
19 words
The method of claim 1 including the additional step of stirring the molten polymer while it is being sparged.
Claim 9
Dependent Claim
56 words
The method of claim 1 wherein the polymer is amorphous polypropylene, the reaction is conducted at a temperature between about 385° F. and about 405° F., the oxygen-containing gas is air, and the depolymerized polymer has a viscosity at 347° F. of between about 100 and 250 centipoise and a softening point of below 267° F.
Claim 10
Dependent Claim
39 words
The method of claim 1 wherein the polymer is a mixture of a polyolefin prepared from an alpha-olefin and a Fischer-Tropsch wax, the reaction is conducted at a temperature below about 347° F., and the oxygen-containing gas is air.
Claim 11
Dependent Claim
12 words
The method of claim 9 wherein the alpha-olefin is C 30+ alpha-olefin.
References Cited (Backward Citations)
US3160621A
Cited
US2911384A
Cited
US2828296A
Cited
US2928797A
Cited
US3110708A
Cited
US3232917A
Cited
US3177193A
Cited
US3130186A
Cited
US3383375A
Cited
US3201381A
Cited
US3227703A
Cited
US3519588A
Cited
US3563972A
Cited
US3655834A
Cited
US3700639A
Cited
US3898209A
Cited
US4145526A
Cited
US4145493A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-11-24 | 1990-05-26 | 1990-11-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-11-24 | 1994-05-26 | 1994-11-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-11-24 | 1998-05-26 | 1998-11-25 | $7700.00 | Window Closed / Lapsed |