Low temperature impact resistant carbonate polymer blends
Assignee: Dow Chemical Co
•
Filing: 1984-08-07
•
Granted: 1986-11-25
•
Expires: 2004-08-07
Abstract
Abstract Blends of carbonate polymer, such as a polycarbonate of bisphenol-A, and a rubber-modified copolymer, such as an acrylonitrile/butadiene/styrene (ABS) resin prepared by mass, bulk or mass suspension polymerization techniques, provide articles which exhibit good low temperature physical properties and can exhibit a low gloss finish. Such blends are particularly useful in the manufacture of molded parts. Such blends are color stable and can exhibit small amounts of yellowing. Such blends are particularly useful in low temperature applications such as below about 0 DEG F.
Inventors
- 👤 Christian A. Weber
- 👤 William P. Paige
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 01:58
CPC Classifications
C; C08; C08L; C08L51/00; C08L51/04; C08L55/00; C08L55/02; C08L69/00; C08L69/005
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
167 words
In a process for using carbonate polymer blends in a molded article which article is employed at less than about 0° F., the improvement which comprises employing as such a molded or extruded article exhibiting an impact strength at 0° F. of at least 50 percent of that impact strength of the article at 70° F., said article comprising a carbonate polymer blended with a functionally effective amount of a rubber-modified copolymer wherein said rubber-modified copolymer comprises from about 5 to about 25 weight percent rubber component, from about 50 to about 90 weight percent monovinylidene aromatic monomer, and from about 5 to about 25 weight percent monoethylenically unsaturated polar monomer, wherein said rubber-modified copolymer is a composition prepared using mass, bulk or mass suspension polymerization techniques and contains a random copolymer of a monovinylidene aromatic monomer and a polar comonomer and a rubber component grafted with a copolymer of the monovinylidene aromatic monomer and the polar comonomer, wherein the carbonate polymer is a homopolycarbonate of bisphenol-A.
Claim 2
Dependent Claim
167 words
In a process for using carbonate polymer blends in a molded article which article is employed at less than about 0° F., the improvement which comprises employing as such a molded or extruded article exhibiting an impact strength at 0° F. of at least 50 percent of that impact strength of the article at 70° F., said article comprising a carbonate polymer blended with a functionally effective amount of a rubber-modified copolymer wherein said rubber-modified copolymer comprises from about 5 to about 25 weight percent rubber component, from about 50 to about 90 weight percent monovinylidene aromatic monomer, and from about 5 to about 25 weight percent monoethylenically unsaturated polar monomer, wherein said rubber-modified copolymer is a composition prepared using mass, bulk or mass suspension polymerization techniques and contains a random copolymer of a monovinylidene aromatic monomer and a polar comonomer and a rubber component grafted with a copolymer of the monovinylidene aromatic monomer and the polar comonomer, wherein the carbonate polymer is a homopolycarbonate of bisphenol-A.
Claim 3
Dependent Claim
138 words
A process for preparing a molded or extruded article exhibiting an impact strength at 0° F. of at least 50 percent of that impact strength of 70° F., wherein a carbonate polymer is blended with a functionally effective amount of a rubber-modified copolymer, wherein said rubber-modified copolymer comprises from about 5 to about 25 weight percent rubber component, from about 50 to about 90 weight percent monovinylidene aromatic monomer, and from about 5 to about 25 weight percent monoethylenically unsaturated polar monomer, wherein said rubber-modified copolymer is a composition prepared using mass, bulk or mass suspension polymerization techniques and contains a random copolymer of a monovinylidene aromatic monomer and a polar comonomer and a rubber component grafted with a copolymer of the monovinylidene aromatic monomer and the polar comonomer, wherein the carbonate polymer is a homopolycarbonate of bisphenol-A.
Claim 4
Dependent Claim
138 words
A process for preparing a molded or extruded article exhibiting an impact strength at 0° F. of at least 50 percent of that impact strength of 70° F., wherein a carbonate polymer is blended with a functionally effective amount of a rubber-modified copolymer, wherein said rubber-modified copolymer comprises from about 5 to about 25 weight percent rubber component, from about 50 to about 90 weight percent monovinylidene aromatic monomer, and from about 5 to about 25 weight percent monoethylenically unsaturated polar monomer, wherein said rubber-modified copolymer is a composition prepared using mass, bulk or mass suspension polymerization techniques and contains a random copolymer of a monovinylidene aromatic monomer and a polar comonomer and a rubber component grafted with a copolymer of the monovinylidene aromatic monomer and the polar comonomer, wherein the carbonate polymer is a homopolycarbonate of bisphenol-A.
Claim 5
Dependent Claim
32 words
A process of claim 1 wherein said monovinylidene aromatic monomer is styrene or a mixture of styrene and α-methylstyrene, said monoethylenically unsaturated polar monomer is acrylonitrile and said rubber component is butadiene.
Claim 6
Dependent Claim
15 words
A process of claim 1 wherein said rubber-modified copolymer is prepared using mass polymerization techniques.
Claim 7
Dependent Claim
35 words
A process of claim 1 wherein said carbonate polymer blend comprises greater than about 20 to about 95 weight percent carbonate polymer, and from about 5 to less than about 80 weight percent rubber-modified copolymer.
Claim 8
Dependent Claim
32 words
A process of claim 1 wherein said carbonate polymer blend comprises from about 30 to about 70 weight percent carbonate polymer, and from about 30 to about 70 weight percent rubber-modified copolymer.
Claim 9
Dependent Claim
28 words
A process of claim 1 wherein said article exhibits an impact strength at 0° F. of greater than 80 percent than that of said article at 70° C.
References Cited (Backward Citations)
US3130177A
Cited
US3880783A
Cited
US4205140A
Cited
US4163762A
Cited
WO1980000027A1
Cited
EP0024644A2
Cited
US4526926A
Cited
US4550138A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-11-24 | 1990-05-26 | 1990-11-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-11-24 | 1994-05-26 | 1994-11-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-11-24 | 1998-05-26 | 1998-11-25 | $7700.00 | Window Closed / Lapsed |