Iron on mixed zirconia-titania substrate Fischer-Tropsch catalyst and method of making same
Assignee: Air Products and Chemicals Inc
•
Filing: 1985-07-03
•
Granted: 1986-11-25
•
Expires: 2005-07-03
Abstract
Abstract A Fischer-Tropsch catalyst comprising iron co-deposited with or deposited on particles comprising a mixture of zirconia and titania, preferably formed by co-precipitation of compounds convertible to zirconia and titania, such as zirconium and titanium alkoxide. The invention also comprises the method of making this catalyst and an improved Fischer-Tropsch reaction process in which the catalyst is utilized.
Inventors
- 👤 Paul N. Dyer
- 👤 Andrew F. Nordquist
- 👤 Ronald Pierantozzi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 22:34
CPC Classifications
B; B01; B01J; B01J23/00; B01J23/70; B01J23/76; B01J23/78; C; C07; C07C; C07C1/00; C07C1/02; C07C1/04; C07C1/0425; C07C1/043; C07C1/0435; C07C1/044; C07C1/0445; B01J21/00; B01J21/06; B01J21/063; B01J21/066; C07C2521/00; C07C2521/06; C07C2523/00; C07C2523/02; C07C2523/04; C07C2523/70; C07C2523/74; C07C2523/745; C07C2523/76; C07C2523/78
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
46 words
A composition comprising porous, solid particles, said particles containing a mixture of zirconium and titanium dioxides, said particles further containing, at least on the surfaces thereof, iron or iron oxide, and said particles still further containing up to 10%, by weight, of an alkali metal compound.
Claim 2
Dependent Claim
46 words
A composition comprising porous, solid particles, said particles containing a mixture of zirconium and titanium dioxides, said particles further containing, at least on the surfaces thereof, iron or iron oxide, and said particles still further containing up to 10%, by weight, of an alkali metal compound.
Claim 3
Dependent Claim
47 words
A composition comprising porous, solid particles, said particles containing a mixture of zirconium and titanium dioxides, said particles further containing, interdispersed with said zirconium and titanium dioxides, iron or iron oxide, and said particles still further containing up to 10%, by weight, of an alkali metal compound.
Claim 4
Dependent Claim
47 words
A composition comprising porous, solid particles, said particles containing a mixture of zirconium and titanium dioxides, said particles further containing, interdispersed with said zirconium and titanium dioxides, iron or iron oxide, and said particles still further containing up to 10%, by weight, of an alkali metal compound.
Claim 5
Dependent Claim
26 words
The composition according to claim 1, comprising, by weight, 5-15% iron with an atomic ratio of zirconium to titanium in the range of 2:1 to 1:2.
Claim 6
Dependent Claim
26 words
The composition according to claim 2, comprising, by weight, 5-15% iron with an atomic ratio of zirconium to titanium in the range of 2:1 to 1:2.
Claim 7
Dependent Claim
24 words
The composition according to claim 1, comprising, by weight, 5-15% iron with an atomic ratio of zirconium to titanium on the order of 1:1.
Claim 8
Dependent Claim
24 words
The composition according to claim 2, comprising, by weight, 5-15% iron with an atomic ratio of zirconium to titanium on the order of 1:1.
Claim 9
Dependent Claim
13 words
The composition according to claim 1, wherein said iron oxide is ferric oxide.
Claim 10
Dependent Claim
18 words
The composition according to claim 1, having a surface area of at least 100 square meters per gram.
Claim 11
Independent Claim
111 words
A method of making a catalytically active material wherein said method comprises: (a) co-precipitating zirconium dioxide and titanium dioxide precursors, convertible upon drying and calcining in air or an oxygen-containing atmosphere to ziroconium dioxide and titanium dioxide; (b) drying and calcining said co-precipitate in an oxygen-containing atmosphere to form porous solid particles comprising a mixture of zirconium dioxide and titanium dioxide; (c) combining with said co-precipitate, at least on the surface of said co-precipitate, an iron precursor, convertible upon drying and calcining in air or an oxygen-containing atmosphere to iron oxide; and (d) drying and calcining said deposit in an oxygen-containing atmosphere or air to convert said precursor to iron oxide.
Claim 12
Independent Claim
111 words
A method of making a catalytically active material wherein said method comprises: (a) co-precipitating zirconium dioxide and titanium dioxide precursors, convertible upon drying and calcining in air or an oxygen-containing atmosphere to ziroconium dioxide and titanium dioxide; (b) drying and calcining said co-precipitate in an oxygen-containing atmosphere to form porous solid particles comprising a mixture of zirconium dioxide and titanium dioxide; (c) combining with said co-precipitate, at least on the surface of said co-precipitate, an iron precursor, convertible upon drying and calcining in air or an oxygen-containing atmosphere to iron oxide; and (d) drying and calcining said deposit in an oxygen-containing atmosphere or air to convert said precursor to iron oxide.
Claim 13
Dependent Claim
29 words
The method according to claim 9, which comprises the further step of reducing in a reducing atmosphere for a sufficient time to convert said iron oxide to elemental iron.
Claim 14
Dependent Claim
22 words
Method, as recited in claim 9, wherein an iron precursor is combined by co-precipitation with said zirconium dioxide and titanium dioxide precursors.
Claim 15
Dependent Claim
31 words
Method, as recited in claim 9, wherein said zirconium dioxide and titanium dioxide precursors are co-precipitated by hydrolyzing a solution of zirconium alkoxide and titanium alkoxide in an anhydrous, non-reactive solvent.
Claim 16
Dependent Claim
17 words
Method, as recited in claim 12, wherein said alkoxides comprise from 1 to 5 alkyl carbon atoms.
Claim 17
Dependent Claim
30 words
A method, as recited in claim 12, wherein said resultant catalytically active material is further enhanced, with respect to its catalytic activity by deposition thereon of an alkali metal compound.
Claim 18
Dependent Claim
16 words
A method, as recited in claim 14, wherein said alkali compound is potassium bicarbonate or carbonate.
Claim 19
Dependent Claim
43 words
A method, as recited in claim 9, wherein said convertible iron precursor is selected from the group consisting of iron oxide, hydrated iron oxide, iron hydroxide, iron acetate, iron benzoate, iron maleate, iron nitrate, iron gluconate, iron citrate, iron lactate and iron sulfate.
Claim 20
Dependent Claim
28 words
A method, as recited in claim 16, wherein said iron precursor is soluble and is deposited from solution onto said co-precipitated and dried zirconium dioxide-titanium dioxide porous material.
Claim 21
Dependent Claim
21 words
Method, as recited in claim 11, wherein said iron precursor is ferric oxide produced by neutralizing a solution including ferric acetate.
Claim 22
Dependent Claim
23 words
Method, as recited in claim 9, wherein said iron precursor is soluble and is co-precipitated with said zirconium dioxide and titanium dioxide precursors.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-11-24 | 1990-05-26 | 1990-11-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-11-24 | 1994-05-26 | 1994-11-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-11-24 | 1998-05-26 | 1998-11-25 | $7700.00 | Window Closed / Lapsed |