Process for preparing fine grain titanium carbide powder
Assignee: United States, ENERGY THE, Department of
•
Filing: 1985-03-12
•
Granted: 1986-11-11
•
Expires: 2005-03-12
Abstract
Abstract A method for preparing finely divided titanium carbide powder in which an organotitanate is reacted with a carbon precursor polymer to provide an admixture of the titanium and the polymer at a molecular-level due to a crosslinking reaction between the organotitanate and the polymer. The resulting gel is dried, pyrolyzed to drive off volatile components and provide carbon. The resulting solids are then heated at an elevated temperature to convert the titanium and carbon to high-purity titanium carbide powder in a submicron size range.
Inventors
- 👤 Mark A. Janey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 20:44
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/5607; C04B35/5611; C01; C01B; C01B32/00; C01B32/90; C01B32/914; C01B32/921; C04B35/01; C04B35/10; C04B35/111; C04B35/117; C01P; C01P2004/00; C01P2004/01; C01P2004/03
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
127 words
A method for preparing titanium carbide powder of a purity greater than 99.9% in a submicron particle size range, comprising the steps of forming a mixture consisting essentially of a liquid organotitanate or an organotitanate in a solution and a solution of a carbon precursor polymer with the organotitanate and the carbon precursor polymer being in essentially stoichiometric concentrations with respect to titanium and carbon and with the organotitanate providing a crosslinking reaction with the carbon precursor polymer for forming a gel, heating the gel to successively dry the gel, drive volatile components from the gel and pyrolyze the polymer to form free carbon, and thereafter heating the remaining components of the gel to a temperature sufficient to convert the titanium and carbon to titanium carbide powder.
Claim 2
Independent Claim
127 words
A method for preparing titanium carbide powder of a purity greater than 99.9% in a submicron particle size range, comprising the steps of forming a mixture consisting essentially of a liquid organotitanate or an organotitanate in a solution and a solution of a carbon precursor polymer with the organotitanate and the carbon precursor polymer being in essentially stoichiometric concentrations with respect to titanium and carbon and with the organotitanate providing a crosslinking reaction with the carbon precursor polymer for forming a gel, heating the gel to successively dry the gel, drive volatile components from the gel and pyrolyze the polymer to form free carbon, and thereafter heating the remaining components of the gel to a temperature sufficient to convert the titanium and carbon to titanium carbide powder.
Claim 3
Dependent Claim
29 words
The method claimed in claim 1, wherein the organotitanate is selected from the group consisting of tetra isopropyl titanate, lactic acid chelate, tetrabutyl titanate, acetylacetonate chelate and triethanolamine chelate.
Claim 4
Dependent Claim
30 words
The method claimed in claim 1, wherein the carbon precursor polymer is selected from the group of polymers having active hydrogens on a hydroxyl, amino, amido, carboxyl or thio group.
Claim 5
Dependent Claim
16 words
The method claimed in claim 2 wherein the carbon precursor polymer is methylcellulose or phenolic resin.
Claim 6
Dependent Claim
37 words
The method claimed in claim 1, wherein the temperature sufficient to convert the titanium and carbon to titanium carbide is in the range of 1400° to 1600° C. for a duration of about one to two hours.
Claim 7
Dependent Claim
35 words
The method claimed in claim 1, including the additional step of heating the mixture to a temperature sufficient to effect the crosslinking reaction between the organotitanate and the carbon precursor polymer for forming the gel.
References Cited (Backward Citations)
US4126652A
Cited
JPS54107500A
Cited
EP0021844A1
Cited
US4536358A
Cited
JPS59161430A
Cited
JPS59162176A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-11-10 | 1990-05-12 | 1990-11-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-11-10 | 1994-05-12 | 1994-11-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-11-10 | 1998-05-12 | 1998-11-11 | $7700.00 | Window Closed / Lapsed |