Process for forming unusually strong joints between metals and ceramics by brazing at temperatures that do no exceed 750 degree C.

Claim 2

A process for brazing high melting point iron-containing metals to ceramics at temperatures not greater than 750° C. comprising, in a vacuum: (a) cleaning a surface to be brazed of a ceramic to remove surface oxygen therefrom; (b) coating said cleaned surface of ceramic with a thin layer of an active substrate that is from 0.3 to 1 micron thick; (c) cleaning a surface to be brazed of a high-melting point iron-containing metal to remove any surface carbon therefrom; (d) coating said surface to be brazed of said metal with a thin noncarbon containing metal coating to prevent any carbon contained in said metal from reacting with a brazing alloy; (e) forming an assembly of said ceramic surface and said metal surface in sandwich fashion with a brazing alloy placed therebetween, said brazing alloy having a melting point of less than 750° C., wetting said metal surface and forming a trimetal intermetallic with said active substrate upon brazing; (f) heating said assembly to the melting point of said brazing alloy for a period suitable to permit flow and wetting by said brazing alloy; and (g) cooling said assembly to form a brazed joint between said ceramic surface and said metal surface.

Claim 3

The process of claim 1 wherein said brazing alloy is a silver-copper eutectic alloy to which has been added a sufficient amount of a melting point depressant selected from the group consisting of Sn, Ge, Mn and combinations thereof to lower the melting point of said brazing alloy to not more than 750° C.

Claim 4

The process of claim 2 wherein said brazing alloy is an Ag-Cu-Sn composition.

Claim 5

The process of claim 3 wherein said ceramic is selected from the group of silica whisker-reinforced alumina, alumina or partially stabilized zirconia.

Claim 6

The process of claim 3 wherein said active substrate is selected from the group consisting of Ti, Zr, Ta and Nb and their compounds.

Claim 7

The process of claim 5 wherein said active substrate is Ti.

Claim 8

The process of claim 6 wherein said ceramic is partially stabilized zirconia.

Claim 9

The process of claim 6 wherein the composition of said brazing alloy is 60Ag-30Cu-10Sn by weight.

Claim 10

The process of claim 3 wherein said noncarbon containing metal coating comprises a layer of iron with a subsequent layer of nickel or a layer of copper.

Claim 11

The process of claim 9 wherein said high melting point iron-containing metal comprises low alloy steel, stainless steel, special purpose steel or nodular cast iron.

Claim 12

The process of claim 10 wherein said noncarbon containing metal coating is copper having a thickness in the range of 1 to 2 mils.

Claim 13

The process of claim 11 wherein said high melting point iron-containing metal is nodular cast iron having a composition of not less than 80% pearlite.

Claim 14

The process of claim 12 wherein said ceramic is partially stabilized zirconia.

Claim 15

The process of claim 13 wherein the composition of said brazing alloy is 60Ag-30Cu-10Sn by weight.

Claim 16

the process of claim 14 wherein said active substrate is Ti.

Claim 17

A process for brazing high melting point iron-containing metals to ceramics at a temperature not greater than 750° C. comprising, in a vacuum: (a) cleaning a surface to be brazed of a ceramic to remove surface oxygen therefrom; (b) coating said cleaned surface of said ceramic with a thin layer of an active substrate that is from 0.3 to 1 micron thick; (c) cleaning a surface to be brazed of a high melting point iron-containing metal to remove any surface carbon therefrom; (d) coating said surface to be brazed of said metal with a thin noncarbon containing metal coating to prevent any carbon contained in said metal from reacting with a brazing alloy; (e) forming an assembly of said ceramic surface and said metal surface in sandwich fashion with a transition piece placed therebetween, a first brazing alloy between said ceramic surface and said transition piece, and a second brazing alloy between said metal surface and said transistion piece; said first brazing alloy having a melting point of less than 750° C, forming a trimetal intermetallic with said active substrate upon brazing, and being capable of wetting said transition piece upon brazing; said second brazing alloy having a melting point of less than 750° C., being capable of wetting said metal surface and transition piece upon brazing; (f) heating said assembly to the melting point of the brazing alloy having the higher melting point for a period suitable to permit flow and wetting by said brazing alloys; and (g) cooling said assembly to form a brazed joint between said ceramic surface, said transition piece and said metal surface.

Claim 18

A process for brazing high melting point iron-containing metals to ceramics at a temperature not greater than 750° C. comprising, in a vacuum: (a) cleaning a surface to be brazed of a ceramic to remove surface oxygen therefrom; (b) coating said cleaned surface of said ceramic with a thin layer of an active substrate that is from 0.3 to 1 micron thick; (c) cleaning a surface to be brazed of a high melting point iron-containing metal to remove any surface carbon therefrom; (d) coating said surface to be brazed of said metal with a thin noncarbon containing metal coating to prevent any carbon contained in said metal from reacting with a brazing alloy; (e) forming an assembly of said ceramic surface and said metal surface in sandwich fashion with a transition piece placed therebetween, a first brazing alloy between said ceramic surface and said transition piece, and a second brazing alloy between said metal surface and said transistion piece; said first brazing alloy having a melting point of less than 750° C, forming a trimetal intermetallic with said active substrate upon brazing, and being capable of wetting said transition piece upon brazing; said second brazing alloy having a melting point of less than 750° C., being capable of wetting said metal surface and transition piece upon brazing; (f) heating said assembly to the melting point of the brazing alloy having the higher melting point for a period suitable to permit flow and wetting by said brazing alloys; and (g) cooling said assembly to form a brazed joint between said ceramic surface, said transition piece and said metal surface.

Claim 19

The process of claim 16 wherein said transition piece is a metal that is ductile and remains ductile upon heating to brazing temperature and subsequent cooling and, has a coefficient of expansion compatible with said ceramic.

Claim 20

The process of claim 17 wherein said transition piece is titanium.

Claim 21

The process of claim 18 wherein the composition of said first brazing alloy is 60Ag-30Cu-10Sn by weight.

Claim 22

The process of claim 19 wherein the composition of said second brazing alloy is 60Ag-30Cu-10Sn by weight.

Claim 23

The process of claim 20 wherein said ceramic is partially stabilized zirconia.

Claim 24

The process of claim 21 wherein said active substrate is Ti.

Claim 25

The process of claim 22 wherein said high melting point iron-containing metal comprises low alloy steel, stainless steel, special purpose steel or nodular cast iron.

Claim 26

The process of claim 23 wherein said noncarbon containing metal coating is copper having a thickness in the range of 1 to 2 mils.

Claim 27

The process of claim 24 wherein said high melting point iron-containing metal is nodular cast iron having a composition of not less than 80% pearlite.

Claim 28

A process for brazing high melting point iron-coating metals to ceramics at a temperature not greater than 750° C. comprising, in a vacuum; (a) cleaning a surface to be brazed of a ceramic to remove surface oxygen therefrom; (b) coating said cleaned surface of said ceramic with a thin layer of an active substrate that is from 0.3 to 1 micron thick; (c) forming an assembly of said ceramic surface and a first surface of a transition piece that is ductile and has a coefficient of expansion compatible with said ceramic in sandwich fashion with a first brazing alloy therebetween, said first brazing alloy having a melting point of less than 750° C., forming a trimetal intermetallic with said active substrate, and capable of wetting said transition piece upon brazing; (d) heating said assembly to the melting point of said first brazing alloy for a period suitable to permit flow and wetting by said first brazing alloy; (e) cooling said assembly to form a brazed joint between said ceramic surface and said transition piece; (f) cleaning a surface to be brazed of a high melting point iron-containing metal to remove any surface carbon therefrom; (g) coating said surface to be brazed of said metal with a thin noncarbon containing metal coating to prevent any carbon contained in said metal from reacting with a brazing alloy; (h) forming an assembly of said metal surface and a second surface of said transition piece in sandwich fashion with a second brazing alloy placed therebetween, said second brazing alloy having a melting point the same as or less than said frist brazing alloy and being capable of wetting said metal surface and said second surface of said transition piece upon brazing; (i) heating said assembly to the melting point of said second brazing alloy for a period suitable to permit flow and wetting by said second brazing alloy; and (j) cooling said assembly to form a brazed joint between said metal surface and said transition piece.

Claim 29

A process for brazing high melting point iron-coating metals to ceramics at a temperature not greater than 750° C. comprising, in a vacuum; (a) cleaning a surface to be brazed of a ceramic to remove surface oxygen therefrom; (b) coating said cleaned surface of said ceramic with a thin layer of an active substrate that is from 0.3 to 1 micron thick; (c) forming an assembly of said ceramic surface and a first surface of a transition piece that is ductile and has a coefficient of expansion compatible with said ceramic in sandwich fashion with a first brazing alloy therebetween, said first brazing alloy having a melting point of less than 750° C., forming a trimetal intermetallic with said active substrate, and capable of wetting said transition piece upon brazing; (d) heating said assembly to the melting point of said first brazing alloy for a period suitable to permit flow and wetting by said first brazing alloy; (e) cooling said assembly to form a brazed joint between said ceramic surface and said transition piece; (f) cleaning a surface to be brazed of a high melting point iron-containing metal to remove any surface carbon therefrom; (g) coating said surface to be brazed of said metal with a thin noncarbon containing metal coating to prevent any carbon contained in said metal from reacting with a brazing alloy; (h) forming an assembly of said metal surface and a second surface of said transition piece in sandwich fashion with a second brazing alloy placed therebetween, said second brazing alloy having a melting point the same as or less than said frist brazing alloy and being capable of wetting said metal surface and said second surface of said transition piece upon brazing; (i) heating said assembly to the melting point of said second brazing alloy for a period suitable to permit flow and wetting by said second brazing alloy; and (j) cooling said assembly to form a brazed joint between said metal surface and said transition piece.

Claim 30

The process of claim 26 wherein said transition piece is a metal that is ductile and remains ductile upon heating to brazing temperature and subsequent cooling and has a coefficient of expansion compatible with said ceramic.

Claim 31

The process of claim 27 wherein said transition piece is titanium.

Claim 32

The process of claim 28 wherein the composition of said first brazing alloy is 60Ag-30Cu-10Sn by weight.

Claim 33

The process of claim 29 wherein the composition of said second brazing alloy is 60Ag-30Cu-10Sn by weight.

Claim 34

The process of claim 30 wherein said ceramic is partially stabilized zirconia.

Claim 35

The process of claim 31 wherein said active substrate is Ti.

Claim 36

The process of claim 32 wherein said high melting point iron-containing metal comprises low alloy steel, stainless steel, special purpose steel or nodular cast iron.

Claim 37

The process of claim 33 wherein said noncarbon containing metal coating is copper having a thickness in the range of 1 to 2 mils.

Claim 38

The process of claim 34 wherein said high melting point iron-containing metal is nodular cast iron having a composition of not less than 80% pearlite.

Claim 39

The process of claim 6 wherein said titanium is applied by physical vapor deposition.

Claim 40

The process of claim 15 wherein said titanium is applied by physical vapor deposition.

Claim 41

The process of claim 22 wherein said titanium is applied by physical vapor deposition.

Claim 42

The process of claim 32 wherein said titanium is applied by physical vapor deposition.