Process and apparatus for manufacturing axi-symmetrical three-dimensional structures
Assignee: Safran Aircraft Engines SAS
•
Filing: 1984-12-20
•
Granted: 1986-11-11
•
Expires: 2004-12-20
Abstract
Abstract The present invention relates to a process for manufacturing an axi-symmetrical three-dimensional structure formed by superposed layers of fibrous material bonded together, said process comprising the following steps of:--bringing onto a rotary mandrel having the section of the structure to be manufactured, a tape of fibrous material whose width is several times less than the length of a generatrix of said structure:--winding the tape over the mandrel to form superposed layers, each layer being formed by successive turns of the tape of fibrous material, and--during winding, successively bonding the layers together by needling, said needling being effected at the place where the tape is superposed on the mandrel or on the previously formed layer. The invention also relates to an apparatus for carrying out said process.
Inventors
- 👤 Pierre Olry
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 04:09
CPC Classifications
D; D04; D04H; D04H18/00; D04H18/02; B; B29; B29C; B29C53/00; B29C53/80; B29C53/8008; B29C53/8041
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
193 words
A process for manufacturing a three-dimensional axi-symmetrical and non-cylindrical structure constituted by superposed and interbonded layers of fibrous material comprising the steps of: delivering onto a rotating mandrel having an axi-symmetrical and non-cylindrical profile corresponding to that of the structure to be manufactured a tape of a fibrous material having a width that is several times less than the length of a generatrix of said structure; winding the tape over the mandrel to form superposed layers in such a way that each of the layers is constituted by plural, successive turns of the tape of the fibrous material; and simultaneously with said winding step, interbonding the layers together by successively needling their constitutive turns by means of an assembly of needles which extend over a distance substantially equal to the width of said tape and longitudinally movable relative to the mandrel in order to perform said needling over the width of the layers in such a way as to be sequentially positioned at the location where the tape is delivered for needling the tape simultaneously as it is being delivered thereto and wound therearound substantially across the width of each of the layers.
Claim 2
Dependent Claim
193 words
A process for manufacturing a three-dimensional axi-symmetrical and non-cylindrical structure constituted by superposed and interbonded layers of fibrous material comprising the steps of: delivering onto a rotating mandrel having an axi-symmetrical and non-cylindrical profile corresponding to that of the structure to be manufactured a tape of a fibrous material having a width that is several times less than the length of a generatrix of said structure; winding the tape over the mandrel to form superposed layers in such a way that each of the layers is constituted by plural, successive turns of the tape of the fibrous material; and simultaneously with said winding step, interbonding the layers together by successively needling their constitutive turns by means of an assembly of needles which extend over a distance substantially equal to the width of said tape and longitudinally movable relative to the mandrel in order to perform said needling over the width of the layers in such a way as to be sequentially positioned at the location where the tape is delivered for needling the tape simultaneously as it is being delivered thereto and wound therearound substantially across the width of each of the layers.
Claim 3
Dependent Claim
20 words
The process of claim 1, wherein each layer is formed by winding the tape of fibrous material in contiguous turns.
Claim 4
Dependent Claim
43 words
The process of claim 1, wherein said assembly of needles is driven along a line reproducing a generatrix of the mandrel or of the structure during the manufacture thereof at a speed which is a function of the rotation speed of the mandrel.
Claim 5
Dependent Claim
12 words
The process of claim 1, wherein the depth of needling is constant.
Claim 6
Dependent Claim
13 words
The process of claim 1, wherein the surface density of needling is constant.
Claim 7
Dependent Claim
33 words
The process of claim 1, further including the step of introducing reinforcing elements of fibrous material between adjacent layers of the structure so as to cross the turns formed by winding the tape.
Claim 8
Dependent Claim
39 words
The process of claim 1, further including a base layer disposed on the mandrel before winding on the tape so as to allow penetration of the needles without damaging them during needling of the initial layers of the structure.
Claim 9
Dependent Claim
184 words
A process for manufacturing a three-dimensional axi-symmetrical and non-cylindrical structure constituted by superposed and interbonded layers of fibrous material comprising the steps of: delivering onto a rotating mandrel having an axi-symmetrical and non-cylindrical profile corresponding to that of the structure to be manufactured a tape of a fibrous material having a width that is several times less than the length of the generatrix of the said structure; winding the tape over the mandrel to form superposed layers in such a way that each of the layers is constituted by plural, successive turns of the tape of fibrous material; simultaneously with said winding step, simultaneously bonding the layers together by successively needling their constitutive turns onto the mandrel and onto the previously formed layers simultaneously as the tape is being delivered and wound onto the mandrel and onto the previously formed layers; and at the end of the winding and bonding of each layer, moving apart said mandrel said assembly of needles relatively by a distance equal to the thickness of a needled layer to provide a constant needling depth during the whole manufacturing process.
Claim 10
Dependent Claim
184 words
A process for manufacturing a three-dimensional axi-symmetrical and non-cylindrical structure constituted by superposed and interbonded layers of fibrous material comprising the steps of: delivering onto a rotating mandrel having an axi-symmetrical and non-cylindrical profile corresponding to that of the structure to be manufactured a tape of a fibrous material having a width that is several times less than the length of the generatrix of the said structure; winding the tape over the mandrel to form superposed layers in such a way that each of the layers is constituted by plural, successive turns of the tape of fibrous material; simultaneously with said winding step, simultaneously bonding the layers together by successively needling their constitutive turns onto the mandrel and onto the previously formed layers simultaneously as the tape is being delivered and wound onto the mandrel and onto the previously formed layers; and at the end of the winding and bonding of each layer, moving apart said mandrel said assembly of needles relatively by a distance equal to the thickness of a needled layer to provide a constant needling depth during the whole manufacturing process.
Claim 11
Dependent Claim
46 words
The process of claim 8, wherein each layer is constituted as successive turns of the tape of fibrous material, and wherein said assembly of needles is driven longitudinally with respect to the mandrel along the line reproducing a generatrix of the mandrel during the manufacture thereof.
Claim 12
Independent Claim
170 words
An apparatus for manufacturing a three-dimensional, axis-symmetrical and non-cylindrical structure constituted as superposed layers of fibrous material bonded together, comprising: a rotary mandrel having a three-dimensional axi-symmetrical and non-cylindrical profile corresponding to that of the structure to be manufactured; supply means for delivering a tape of fibrous material onto said mandrel in order to so form thereon said superposed layers as plural, successive turns of said tape; an assembly of needles extending over a length substantially equal to the width of said tape; first driving means for so moving said assembly of needles and to said mandrel relatively to each other as to allow the needles to penetrate perpendicularly to the tape at the location where said tape is superposed onto the mandrel and onto the previously formed layer; and second driving means for so moving said assembly of needles and to said mandrel relatively to each other as to trace along a locus line reproducing a generatrix of the surface of the mandrel and of the structure being manufactured.
Claim 13
Independent Claim
170 words
An apparatus for manufacturing a three-dimensional, axis-symmetrical and non-cylindrical structure constituted as superposed layers of fibrous material bonded together, comprising: a rotary mandrel having a three-dimensional axi-symmetrical and non-cylindrical profile corresponding to that of the structure to be manufactured; supply means for delivering a tape of fibrous material onto said mandrel in order to so form thereon said superposed layers as plural, successive turns of said tape; an assembly of needles extending over a length substantially equal to the width of said tape; first driving means for so moving said assembly of needles and to said mandrel relatively to each other as to allow the needles to penetrate perpendicularly to the tape at the location where said tape is superposed onto the mandrel and onto the previously formed layer; and second driving means for so moving said assembly of needles and to said mandrel relatively to each other as to trace along a locus line reproducing a generatrix of the surface of the mandrel and of the structure being manufactured.
Claim 14
Dependent Claim
45 words
The apparatus of claim 10, further including third driving means operative after the formation of each of said layers for moving said assembly of needles relative to said mandrel a preselected distance apart selected to be equal to the thickness of an already needled layer.
Claim 15
Dependent Claim
71 words
The apparatus of claim 10, wherein said tape supply means includes means for delivering the tape at a constant speed, and a control device for controlling the rotation speed of the mandrel so that the tangential speed thereof and of the structure being formed, at the level where the tape is delivered onto the mandrel and onto a previously formed layer, is equal to the speed of supply of the tape.
Claim 16
Dependent Claim
30 words
The apparatus of claim 10, wherein said second driving means moves said assembly of needles along said locus line at a speed depending on the rotation speed of the mandrel.
Claim 17
Dependent Claim
37 words
The apparatus of claim 10, further including needle support means for pivoting said assembly of needles about an axis perpendicular to the meridian plane and containing said locus line along which said assembly of needles is driven.
Claim 18
Dependent Claim
155 words
A three-dimensional, axi-symmetrical and non-cylindrical structure constituted by superposed and interbonded layers of fibrous material produced by the process of delivering onto a rotating mandrel having an axi-symmetrical and non-cylindrical profile corresponding to that of the structure to be manufactured a tape of the fibrous material having a width that is several times less than the length of the generatrix of said structure produced by the steps of: winding the tape over the mandrel to form superposed layers in such a way that each of the layers is constituted by plural, successive turns of the tape of the fibrous material; simultaneously with said winding step, interbonding the layers together by successively needling their constitutive turns at the location where the tape is sequentially delivered onto the mandrel and onto the previously formed layer to form a three-dimensional, axis-symmetrical and non-cylindrical structure; and removing said structure off of said mandrel after said interbonding step is completed.
Claim 19
Dependent Claim
155 words
A three-dimensional, axi-symmetrical and non-cylindrical structure constituted by superposed and interbonded layers of fibrous material produced by the process of delivering onto a rotating mandrel having an axi-symmetrical and non-cylindrical profile corresponding to that of the structure to be manufactured a tape of the fibrous material having a width that is several times less than the length of the generatrix of said structure produced by the steps of: winding the tape over the mandrel to form superposed layers in such a way that each of the layers is constituted by plural, successive turns of the tape of the fibrous material; simultaneously with said winding step, interbonding the layers together by successively needling their constitutive turns at the location where the tape is sequentially delivered onto the mandrel and onto the previously formed layer to form a three-dimensional, axis-symmetrical and non-cylindrical structure; and removing said structure off of said mandrel after said interbonding step is completed.
Claim 20
Dependent Claim
191 words
A three-dimensional axi-symmetrical and non-cylindrical structure constituted by superposed and interbonded layers of fibrous material manufactured produced by the steps of: delivering onto a rotating mandrel having an axi-symmetrical and non-cylindrical profile corresponding to that of the structure to be manufactured a tape of a fibrous material having a width that is several times less than the length of a generatrix of a structure; winding the tape over the mandrel to form superposed layers in such a way that each of the layers is constituted by plural, successive turns of the tape of the fibrous material; simultaneously with said winding step, interbonding the layers together by successively needling their constitutive turns over the width of the layers as the tape is delivered onto the mandrel and onto the previously formed layer to sequentially form said structure; at the end of the winding and bonding of each layer, relatively moving apart said mandrel and said assembly of needles by a distance equal to the thickness of a needled layer to provide a constant needling depth; and removing the structure from the mandrel after a predetermined number of layers has been built up.
Claim 21
Dependent Claim
191 words
A three-dimensional axi-symmetrical and non-cylindrical structure constituted by superposed and interbonded layers of fibrous material manufactured produced by the steps of: delivering onto a rotating mandrel having an axi-symmetrical and non-cylindrical profile corresponding to that of the structure to be manufactured a tape of a fibrous material having a width that is several times less than the length of a generatrix of a structure; winding the tape over the mandrel to form superposed layers in such a way that each of the layers is constituted by plural, successive turns of the tape of the fibrous material; simultaneously with said winding step, interbonding the layers together by successively needling their constitutive turns over the width of the layers as the tape is delivered onto the mandrel and onto the previously formed layer to sequentially form said structure; at the end of the winding and bonding of each layer, relatively moving apart said mandrel and said assembly of needles by a distance equal to the thickness of a needled layer to provide a constant needling depth; and removing the structure from the mandrel after a predetermined number of layers has been built up.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-11-10 | 1990-05-12 | 1990-11-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-11-10 | 1994-05-12 | 1994-11-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-11-10 | 1998-05-12 | 1998-11-11 | $7700.00 | Window Closed / Lapsed |