Metal-coated hollow microspheres

Claim 2

A process for preparing metal-coated hollow microspheres comprising the combination of steps of: (a) vigorously admixing a major quantity of hollow microspheres with a thermosetting binder adhesive until said microspheres are wet-out, said hollow microspheres having an average particle size diameter ranging from about 60 microns to about 180 microns; (b) slowly adding metal flakes to the thus wet-out microspheres from step (a) until said wet-out microspheres are coated with said metal flakes;

Claim 3

(c) applying heat and slowly increasing the temperature of the metal-coated microspheres from step (b) up to about 350° F. to thereby cure said binder and bind said metal flakes to said microspheres; and (d) intermittently mixing-agitating the metal-coated microspheres from step (c) in the absence of any further heating until said metal-coated microspheres are dry.

Claim 4

(c) applying heat and slowly increasing the temperature of the metal-coated microspheres from step (b) up to about 350° F. to thereby cure said binder and bind said metal flakes to said microspheres; and (d) intermittently mixing-agitating the metal-coated microspheres from step (c) in the absence of any further heating until said metal-coated microspheres are dry.

Claim 5

Process according to claim 1, wherein said thermosetting binder adhesive is composed of a polymerizable organo-silane composition and a copolymerizable monomer or copolymer.

Claim 6

Process according to claim 2, wherein said polymerizable organo-silane is 3[2(vinyl benzylamino)ethylamino]propyltrimethoxy silane and said copolymerizable monomer is gamma-butyrolactone.

Claim 7

Process according to claim 1, wherein said thermo-setting binder adhesive is added in amount about 3 to about 4 percent by weight of the final product.

Claim 8

Process according to claim 1, wherein said metal flakes have an average size of about 6 microns to 10 microns.

Claim 9

Process according to claim 1, wherein said hollow microspheres have an average particle size of about 100 microns to about 150 microns.

Claim 10

Process according to claim 1, where in said step (c) the temperature is raised to about 220° F. to about 240° F.

Claim 11

Process according to claim 1, where in step (a) heat is applied until a temperature of about 140° F. to about 160° F. is obtained.

Claim 12

Process according to claim 1, wherein said metal flake is composed of zinc, aluminum, silver, copper, stainless steel, platinum, gold or a combination thereof.

Claim 13

A process for preparing metal-coated hollow microspheres comprising the combination of steps of: (a) vigorously admixing a major quantity of hollow microspheres having an average particle size diameter ranging from about 60 microns to about 180 microns with about 3 to about 6 weight percent, based on the weight of the final product, of a thermosetting binder adhesive comprising an organo functional silane and a copolymerizable monomer, until said microspheres are wet-out; (b) slowly adding metal flakes to the thus wet-out microspheres from step (a) until said wet-out microspheres are coated with said metal flakes, said metal flakes having an average particle size of about 6 microns to about 10 microns; (c) applying heat and slowly increasing the temperature of the metal-coated microspheres from step (b) up to about 350° F. to thereby cure said binder and bind said metal flakes to said microspheres; and (d) intermittently mixing-agitating the metal-coated microspheres from step (c) in the absence of any futher heating, until said metal-coated microspheres are dry.

Claim 14

A process for preparing metal-coated hollow microspheres comprising the combination of steps of: (a) vigorously admixing a major quantity of hollow microspheres having an average particle size diameter ranging from about 60 microns to about 180 microns with about 3 to about 6 weight percent, based on the weight of the final product, of a thermosetting binder adhesive comprising an organo functional silane and a copolymerizable monomer, until said microspheres are wet-out; (b) slowly adding metal flakes to the thus wet-out microspheres from step (a) until said wet-out microspheres are coated with said metal flakes, said metal flakes having an average particle size of about 6 microns to about 10 microns; (c) applying heat and slowly increasing the temperature of the metal-coated microspheres from step (b) up to about 350° F. to thereby cure said binder and bind said metal flakes to said microspheres; and (d) intermittently mixing-agitating the metal-coated microspheres from step (c) in the absence of any futher heating, until said metal-coated microspheres are dry.

Claim 15

Process according to claim 10, where in step (b) about 15 to about 30 weight percent metal flakes, relative to said wet-out microspheres from step (a), are employed.

Claim 16

Process according to claim 11, wherein said mircospheres have an average particle size of about 165 to 170 microns and about 18 to about 22 weight percent metal flakes, relative to said wet-out microspheres from step (a), are employed.

Claim 17

Metal-coated hollow microspheres obtained by: (a) vigorously admixing a major quantity of hollow microspheres having an average particle size diameter ranging from about 60 microns to about 180 microns, with about 3 to about 6 weight percent, based on the weight of the final product, of a thermosetting binder adhesive, said adhesive comprising an organo functional silane and a copolymerizable monomer, until said microspheres are wet-out; (b) adding metal flakes to the thus wet-out microspheres from step (a) until said wet-out microspheres are coated with said metal flakes, said metal flakes having an average particle size of about 2 microns to about 10 microns; (c) applying heat and slowly increasing the temperature of the metal-coated microspheres from step (b) until a temperature of up to about 350° F. is reached to thereby cure said binder and bind said metal flakes to said microspheres; and (d) intermittently admixing-agitating the metal-coated microspheres from step (c) in the absence of further heating until said metal-coated micrspheres are dry after which said metal-coated microspheres are recovered as product.

Claim 18

Metal-coated hollow microspheres obtained by: (a) vigorously admixing a major quantity of hollow microspheres having an average particle size diameter ranging from about 60 microns to about 180 microns, with about 3 to about 6 weight percent, based on the weight of the final product, of a thermosetting binder adhesive, said adhesive comprising an organo functional silane and a copolymerizable monomer, until said microspheres are wet-out; (b) adding metal flakes to the thus wet-out microspheres from step (a) until said wet-out microspheres are coated with said metal flakes, said metal flakes having an average particle size of about 2 microns to about 10 microns; (c) applying heat and slowly increasing the temperature of the metal-coated microspheres from step (b) until a temperature of up to about 350° F. is reached to thereby cure said binder and bind said metal flakes to said microspheres; and (d) intermittently admixing-agitating the metal-coated microspheres from step (c) in the absence of further heating until said metal-coated micrspheres are dry after which said metal-coated microspheres are recovered as product.

Claim 19

Process according to claim 2, which also includes: pre-heating said microspheres and said binder in said step (a) and continuing said pre-heating treatment until a temperature of about 140° F. to 160° F. is obtained; raising the temperature in said step (c) to about 220° F. to about 240° F.; and said hollow microspheres having an average particle size diameter of about 100 microns to about 180 microns and said metal flakes having an average particle size of about 6 microns to about 10 microns comprising zinc, aluminum, silver, copper, stainless steel, platinum, gold or a mixture thereof.

Claim 20

Process according to claim 14 wherein said thermosetting binder adhesive is 3 propyltrimethoxy silane and said copolymerizer monomer is gamma-butyrolactone.

Claim 21

The process according to claim 10, wherein: heat is applied in step (a) until the mixture of said hollow microspheres and said binder is heated to a temperature of about 140° F. to about 160° F.; and the temperature in said step (c) is raised to about 220° F. to about 300° F., said hollow microspheres having an average particle size diameter ranging from about 100 microns to about 180 microns, said metal flakes being composed of zinc, aluminum, silver, copper, stainless steel, platinum, gold or a combination thereof.

Claim 22

Metal-coated hollow microspheres, comprising non-conductive hollow microspheres having an average particle size diameter ranging from about 60 microns to about 180 microns, metal flakes substantially coating individual said hollow microspheres, said metal flakes having an interior surface bound to an exterior surface of a hollow microspheres by a thermosetting binder adhesive.

Claim 23

Metal-coated hollow microspheres, comprising non-conductive hollow microspheres having an average particle size diameter ranging from about 60 microns to about 180 microns, metal flakes substantially coating individual said hollow microspheres, said metal flakes having an interior surface bound to an exterior surface of a hollow microspheres by a thermosetting binder adhesive.

Claim 24

Metal-coated hollow microspheres according to claim 17 wherein said hollow microspheres have an average particle size diameter of about 100 microns to about 180 microns, said metal flakes have an average particle size of about 6 microns to about 10 microns, and said thermosetting binder adhesive comprises the reaction product of an organo functional silane and a copolymerizable monomer.

Claim 25

Metal coated hollow microspheres according to claim 18 wherein said metal flakes are composed of zinc, aluminum, silver, copper, stainless steel, platinum, gold or a combination thereof.

Claim 26

Metal coated hollow microspheres according to claim 17 wherein said metal coated hollow microspheres have an average particle size diameter ranging from about 100 microns to about 150 microns.