Patent US4621017A successfully refreshed from Google Patents.
US4621017A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Corrosion and wear resistant graphite material and method of manufacture
Assignee: Unifrax I LLC
•
Filing: 1984-03-05
•
Granted: 1986-11-04
•
Expires: 2004-03-05
Abstract
Abstract The invention provides a composite carbon or graphite having desirable properties such as corrosion and wear resistance. The invention combines a graphite substrate with a protective porous zone of silicon carbide. The whole body of graphite plus silicon carbide then is infiltrated with aluminum phosphate. An adhered barrier of silicon carbide, ranging in thickness between 0.015 and 0.050 inch thick is integrated with a graphite stratum to form a very hard surface, resistant to mechanical and chemical wear. The silicon carbide barrier is closely compatible to the graphite substrate, in resistance to thermal shock and in qualities of thermal expansion. In order to improve oxidation resistance further, a new composition was formed by infiltrating aluminum phosphate through the silicon carbide into the graphite to form a single body of composite graphite.
Inventors
- 👤 Richard C. Chandler
- 👤 Lutfi H. Amra
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 02:11
CPC Classifications
F; F04; F04B; F04B15/00; F04B15/04; C; C04; C04B; C04B41/00; C04B41/45; C04B41/52; C04B41/80; C04B41/81; C04B41/89; Y; Y10; Y10T; Y10T428/00; Y10T428/25; Y10T428/256; Y10T428/30
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
75 words
A process for the manufacture of carbonaceous articles having enhanced oxidation-resistance and erosion-resistance characteristics, comprising the steps of: (a) forming a carbonaceous article into a desired shape having a desired surface finish: (b) forming a layer of silicon carbide at the surface of the article; and (c) impregnating the silicon carbide-coated article with aluminum phosphate, the aluminum phosphate being distributed through the silicon carbide layer and into at least a portion of the carbonaceous article.
Claim 2
Dependent Claim
75 words
A process for the manufacture of carbonaceous articles having enhanced oxidation-resistance and erosion-resistance characteristics, comprising the steps of: (a) forming a carbonaceous article into a desired shape having a desired surface finish: (b) forming a layer of silicon carbide at the surface of the article; and (c) impregnating the silicon carbide-coated article with aluminum phosphate, the aluminum phosphate being distributed through the silicon carbide layer and into at least a portion of the carbonaceous article.
Claim 3
Dependent Claim
19 words
The process of claim 1, wherein the layer of silicon carbide is formed by a chemical vapor reaction technique.
Claim 4
Dependent Claim
28 words
The process of claim 1, wherein the surface layer of silicon carbide extends inwardly from the surface of the article to a depth within range of 0.035-0.045 inch.
Claim 5
Dependent Claim
25 words
The process of claim 1, wherein the impregnation with aluminum phosphate is carried out at room temperature and at a pressure of about 90 psig.
Claim 6
Dependent Claim
72 words
The process of claim 1, wherein the step of impregnating the article with aluminum phosphate includes: (a) drying the article to drive off volatiles; (b) applying a vacuum to the article to complete the elimination of volatiles; (c) immersing the article in a solution containing aluminum phosphate; (d) pressurizing the article; (e) draining excess solution from the article; (f) heating the article; and, (g) permitting the article to cool to room temperature.
Claim 7
Dependent Claim
25 words
The process of claim 5, wherein the step of drying includes drying the article for approximately eight hours at a temperature of about 105° Centigrade.
Claim 8
Dependent Claim
39 words
The process of claim 5, wherein the step of applying a vacuum to the article includes placing the article under a vacuum of approximately 27-30 inches of water for a period of about three hours while maintaining room temperature.
Claim 9
Dependent Claim
28 words
The process of claim 5, wherein the step of pressurizing the article includes pressurizing the article to approximately 90 psig and maintaining that pressure for about three hours.
Claim 10
Dependent Claim
33 words
The process of claim 5, wherein the step of heating the article includes heating the article from room temperature to approximately 400° Centigrade within a period of approximately eight hours at atmospheric pressure.
Claim 11
Dependent Claim
24 words
The process of claim 9, wherein the step of heating the article includes maintaining the article at approximately 400° Centigrade for about three hours.
Claim 12
Dependent Claim
14 words
An article produced by the process according to either of claims 1 or 5.
References Cited (Backward Citations)
US1948382A
Cited
US2528210A
Cited
US2685539A
Cited
US2685540A
Cited
US2906632A
Cited
US3250322A
Cited
FR1388539A
Cited
US3342627A
Cited
US3510347A
Cited
US3553010A
Cited
US3925577A
Cited
US4104417A
Cited
US4465777A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-11-03 | 1990-05-05 | 1990-11-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-11-03 | 1994-05-05 | 1994-11-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-11-03 | 1998-05-05 | 1998-11-04 | $7700.00 | Window Closed / Lapsed |