Magnetic recording medium with electron beam cured magnetic layer
Assignee: Fujifilm Holdings Corp
•
Filing: 1983-10-18
•
Granted: 1986-10-28
•
Expires: 2003-10-18
Abstract
Abstract A magnetic recording medium is disclosed. The medium is comprised of a support base having an average center line roughness (Ra) of 0.035 μm or less which has coated thereon a magnetic layer. The magnetic layer is comprised of ferromagnetic fine particles dispersed in a binder comprising (1) a polymer selected from the group consisting of nitrocellulose resins, vinyl chloride-vinyl acetate resins and vinyl chloride-vinyl propionate type resins; (2) a urethane resin; and (3) a compound having 2 or more acrylate groups or methacrylate groups in the molecule thereof. The magnetic layer is cured by radiation with electron beams and has excellent electromagnetic properties as well as high durability. The magnetic medium provides less abrasiveness and the magnetic coating composition is stable and homogeneous during storage.
Inventors
- 👤 Tsutomu Okita
- 👤 Nobutaka Yamaguchi
- 👤 Hiroshi Hashimoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 11:15
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/702; G11B5/7026; G11B5/7021; G11B5/7022; G11B5/84; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10T; Y10T428/00; Y10T428/24; Y10T428/24355; Y10T428/24372; Y10T428/24413; Y10T428/31504; Y10T428/31551; Y10T428/31609; Y10T428/31855; Y10T428/31935
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
186 words
A magnetic recording medium comprising a support base having an average center line roughness (Ra) of 0.035 μm or less, the support base having coated thereon a magnetic layer containing ferromagnetic fine particles and the layer further containing: (1) a polymer selected from the group consisting of vinyl chloride-vinyl acetate-type resins and vinyl chloride-vinyl propionate-type resins having a molecular weight in the range of about 20,000 to about 100,000 and having a vinyl chloride/vinyl acetate weight ratio of 80/20 to 95/5 or a vinyl chloride/vinyl propionate weight ratio of from 80/20 to 95/5; (2) a urethane resin; and (3) a compound having two or more of acrylate groups or methacrylate groups in the molecule thereof, said magnetic layer being cured by radiation with electron beams, wherein the mixing ratio of the polymer (1)/the urethane resin (2) is in the range of 20 to 90 parts by weight/80 to 10 parts by weight and wherein the compound (3) is present in an amount of 50 to 400 parts by weight per 100 parts by weight of the mixtures of the polymer (1) and the urethane resin (2).
Claim 2
Dependent Claim
186 words
A magnetic recording medium comprising a support base having an average center line roughness (Ra) of 0.035 μm or less, the support base having coated thereon a magnetic layer containing ferromagnetic fine particles and the layer further containing: (1) a polymer selected from the group consisting of vinyl chloride-vinyl acetate-type resins and vinyl chloride-vinyl propionate-type resins having a molecular weight in the range of about 20,000 to about 100,000 and having a vinyl chloride/vinyl acetate weight ratio of 80/20 to 95/5 or a vinyl chloride/vinyl propionate weight ratio of from 80/20 to 95/5; (2) a urethane resin; and (3) a compound having two or more of acrylate groups or methacrylate groups in the molecule thereof, said magnetic layer being cured by radiation with electron beams, wherein the mixing ratio of the polymer (1)/the urethane resin (2) is in the range of 20 to 90 parts by weight/80 to 10 parts by weight and wherein the compound (3) is present in an amount of 50 to 400 parts by weight per 100 parts by weight of the mixtures of the polymer (1) and the urethane resin (2).
Claim 3
Dependent Claim
51 words
A magnetic recording medium as claimed in claim 1, wherein said polymer (1) is selected from the group consisting of, a copolymer of vinyl chloride-vinyl acetate-vinyl alcohol (vinyl alcohol content being 1 to 15 wt%) and a copolymer of vinyl chloride-vinyl acetate-maleic acid (maleic acid content being 0.5 to 10 wt%).
Claim 4
Dependent Claim
27 words
A magnetic recording medium as claimed in claim 1, wherein said urethane resin (2) has a molecular weight in the range of about 5,000 to about 100,000.
Claim 5
Dependent Claim
24 words
A magnetic recording medium as claimed in claim 3, wherein the urethane resin has a molecular weight in the range of 10,000 to 50,000.
Claim 6
Dependent Claim
24 words
A magnetic recording medium as claimed in claim 1, wherein the compound (3) has a molecular weight in the range of 1,000 to 20,000.
Claim 7
Dependent Claim
36 words
A magnetic recording medium as claimed in claim 1, wherein the mixing ratio of the polymer (1)/the urethane resin (2) is in the range of 40 to 80 parts by weight/60 to 20 parts by weight.
Claim 8
Dependent Claim
45 words
A magnetic recording medium as claimed in claim 1, wherein the compound (3) is present in an amount in the range of 80 to 250 parts by weight per 100 parts by weight of the mixture of the polymer (1) and the urethane resin (2).
Claim 9
Dependent Claim
30 words
A magnetic recording medium as claimed in claim 1, wherein the magnetic layer is cured by electron beams applying an absorption dose in the range of 0.5 to 20 megarads.
Claim 10
Dependent Claim
22 words
A magnetic recording medium as claimed in claim 8, wherein the absorption dose is in the range of 1 to 15 megarads.
Claim 11
Dependent Claim
25 words
A magnetic recording medium as claimed in claim 1, wherein said average center line roughness (Ra) is in the range of 0.005 to 0.035 μm.
Claim 12
Dependent Claim
20 words
A magnetic recording medium as claimed in claim 1, wherein said polyurethane is a polyether urethane or a polyester urethane.
Claim 13
Dependent Claim
29 words
A magnetic recording medium as claimed in claim 1, wherein said compound (3) is selected from the group consisting of diethylene glycol diacrylate, trimethylolpropane triacrylate and triethylene glycol diacrylate.
Claim 14
Dependent Claim
127 words
A magnetic recording medium as claimed in claim 1, wherein said urethane resin (2) has a molecular weight in the range of about 5,000 to about 100,000, the mixing ratio of the polymer (1)/the urethane resin (2) is in the range of 20 to 90 parts by weight/80 to 10 parts by weight, wherein the compound (3) is present in an amount in the range of 80 to 250 parts by weight per 100 parts by weight of the mixture of the polymer (1) and the urethane resin (2), wherein the magnetic layer is cured by electron beams applying an absorption dose in the range of 0.5 to 20 megarads and wherein the average center line roughness (Ra) is in the range of 0.005 to 0.35 μm.
Claim 15
Dependent Claim
29 words
A magnetic recording medium as claimed in claim 13, wherein said compound (3) is selected from the group consisting of diethylene glycol diacrylate, trimethylolpropane triactrylate and triethylene glycol diacrylate.
References Cited (Backward Citations)
US4004997A
Cited
US4307154A
Cited
US4368239A
Cited
US4337288A
Cited
WO1981002646A1
Cited
US4343831A
Cited
US4400435A
Cited
US4368242A
Cited
US4435485A
Cited
US4448846A
Cited
US4368238A
Cited
US4448848A
Cited
US4496626A
Cited
US4407853A
Cited
US4560616A
Cited
US4508782A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-10-27 | 1990-04-28 | 1990-10-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-10-27 | 1994-04-28 | 1994-10-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-10-27 | 1998-04-28 | 1998-10-28 | $7700.00 | Window Closed / Lapsed |