Magnetic recording media
Assignee: Sony Corp
•
Filing: 1981-12-24
•
Granted: 1983-01-11
•
Expires: 2001-12-24
Abstract
Abstract The magnetic recording medium contains as a binder a thermoplastic polyurethane resin having a molecular weight larger than about 5,000 and produced by the polyaddition of a long chain diol (A) having a molecular weight ranging from about 500 to 3,000, an organic diisocyanate (C) and a short chain triol (D) having a molecular weight lower than about 500 and specified structures and, as desired, a short chain diol (B) having a molecular weight ranging from about 50 to 500, in specified ratios. The binder may contain a nitrocellulose, a vinyl chloride resin, a polyvinyl butyral, a bisphenol A type polyether or a vinyl chloride-hydroxy carboxylate copolymer as a binder component. The binder provides particularly enhanced heat resistance and solvent resistance with improved dispersibility of a pigment or the like and other resins and favorable compatibility with a solvent or the like.
Inventors
- 👤 Masashi Somezawa
- 👤 Yoshinobu Ninomiya
- 👤 Akira Hashimoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 09:50
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/702; G11B5/7021; C; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/10; C08G18/12; C08G18/28; C08G18/65; C08G18/66; C08G18/6603; C09; C09D; C09D175/00; C09D175/04; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31511; Y10T428/31551; Y10T428/31609; Y10T428/31786; Y10T428/31794; Y10T428/31855; Y10T428/31935; Y10T428/31971
Claims Analysis
Total Claims: 55
Claim 1
Independent Claim
401 words
A magnetic recording medium comprising a non-magnetic supporting material, magnetic or magnetizable particles or powders, and a thermoplastic polyurethane resin comprising a combination of units represented by formulas (I): ##STR10## wherein W is a residue derived by the elimination of the two hydroxyl groups from a long chain diol (A) having a molecular weight in a range of about 500 to 3,000; X is a residue derived by the elimination of the two isocyanate groups from an organic isocyanate (C); Y is a residue derived by the elimination of the two hydroxyl groups from the short chain triol (D) having a molecular weight in a range lower than about 500; Z is a residue derived by a elimination of the two hydroxyl groups from the short chain diol (B) having a molecular weight in a range of about 50 to 500; n 1 and n 2 are each a positive integer; and n 3 is 0 or a positive integer; said short chain triol (D) being represented by the formula (II): ##STR11## or by the formula (III): ##STR12## wherein R 1 is a group represented by the formula: --CH.sub.2).sub.m (OCH.sub.2 CH.sub.2).sub.n (where m and n are each an integer from 0 to 6, provided that, when one of m and n is 0, the other is an integer other than 0); R 2 is a group represented by the formula: --CH.sub.2).sub.p (OCH.sub.2 CH.sub.2).sub.q (where p and q are each an integer from 0 to 6, provided that, when one of p and q is 0, the other is an integer other than 0); R 3 is a group represented by formula: ##STR13## (where r is an integer from 0 to 3) or a group represented by formula: ##STR14## (where r has the same meaning as above); and R 4 is a group represented by formula: --C.sub.s H.sub.2s+1 (where s is an integer from 0 to 4); obtainable by the polyaddition reaction of the long chain diol (A), the organic diisocyanate (C) and the short chain triol (D) and, as desired, the short chain diol (B) in the ratios of: b/a≦3 (i) < c/(a+b)<3 (ii) 1/2≦[c-(a+b)]/d<1 (iii) (wherein a is a molar number of the long chain diol (A); b is a molar number of the short chain diol (B); c is a molar number of the organic diisocyanate (C); and d is a molar number of the short chain triol (D)).
Claim 2
Dependent Claim
401 words
A magnetic recording medium comprising a non-magnetic supporting material, magnetic or magnetizable particles or powders, and a thermoplastic polyurethane resin comprising a combination of units represented by formulas (I): ##STR10## wherein W is a residue derived by the elimination of the two hydroxyl groups from a long chain diol (A) having a molecular weight in a range of about 500 to 3,000; X is a residue derived by the elimination of the two isocyanate groups from an organic isocyanate (C); Y is a residue derived by the elimination of the two hydroxyl groups from the short chain triol (D) having a molecular weight in a range lower than about 500; Z is a residue derived by a elimination of the two hydroxyl groups from the short chain diol (B) having a molecular weight in a range of about 50 to 500; n 1 and n 2 are each a positive integer; and n 3 is 0 or a positive integer; said short chain triol (D) being represented by the formula (II): ##STR11## or by the formula (III): ##STR12## wherein R 1 is a group represented by the formula: --CH.sub.2).sub.m (OCH.sub.2 CH.sub.2).sub.n (where m and n are each an integer from 0 to 6, provided that, when one of m and n is 0, the other is an integer other than 0); R 2 is a group represented by the formula: --CH.sub.2).sub.p (OCH.sub.2 CH.sub.2).sub.q (where p and q are each an integer from 0 to 6, provided that, when one of p and q is 0, the other is an integer other than 0); R 3 is a group represented by formula: ##STR13## (where r is an integer from 0 to 3) or a group represented by formula: ##STR14## (where r has the same meaning as above); and R 4 is a group represented by formula: --C.sub.s H.sub.2s+1 (where s is an integer from 0 to 4); obtainable by the polyaddition reaction of the long chain diol (A), the organic diisocyanate (C) and the short chain triol (D) and, as desired, the short chain diol (B) in the ratios of: b/a≦3 (i) < c/(a+b)<3 (ii) 1/2≦[c-(a+b)]/d<1 (iii) (wherein a is a molar number of the long chain diol (A); b is a molar number of the short chain diol (B); c is a molar number of the organic diisocyanate (C); and d is a molar number of the short chain triol (D)).
Claim 3
Dependent Claim
20 words
The magnetic recording medium according to claim 1, wherein the thermoplastic polyurethane resin is cured with a polyisocyanate curing agent.
Claim 4
Dependent Claim
25 words
The magnetic recording medium according to claim 1, wherein the long chain diol is a polyester diol, a polyether diol or a polyether ester diol.
Claim 5
Dependent Claim
38 words
The magnetic recording medium according to claim 3, wherein the polyester diol is obtainable by the reaction of an aliphatic dicarboxylic acid, an aromatic dicarboxylic acid or a lower alcohol ester of the dicarboxylic acid with a glycol.
Claim 6
Dependent Claim
23 words
The magnetic recording medium according to claim 4, wherein the aliphatic dicarboxylic acid is succinic acid, adipic acid, sebacic acid or azelaic acid.
Claim 7
Dependent Claim
19 words
The magnetic recording medium according to claim 4, wherein the aromatic dicarboxylic acid is terephthalic acid or isophthalic acid.
Claim 8
Dependent Claim
22 words
The magnetic recording medium according to claim 4, wherein the lower alcohol ester of dicarboxylic acid is a methyl or ethyl ester.
Claim 9
Dependent Claim
34 words
The magnetic recording medium according to claim 4, wherein the glycol is ethylene glycol, 1,3-propylene glycol, 1,4-butylene glycol, 1,6-hexane glycol, diethylene glycol, neopentyl glycol or an ethylene oxide or propylene oxide adduct of bisphenol.
Claim 10
Dependent Claim
25 words
The magnetic recording medium according to claim 1, wherein the long chain diol is a polyester diol, a polyether diol or a polyether ester glycol.
Claim 11
Dependent Claim
38 words
The magnetic recording medium according to claim 9, wherein the polyester diol is obtained by the reaction of an aliphatic dicarboxylic acid, an aromatic dicarboxylic acid or a lower alcohol ester of the dicarboxylic acid with a glycol.
Claim 12
Dependent Claim
23 words
The magnetic recording medium according to claim 10, wherein the aliphatic dicarboxylic acid is succinic acid, adipic acid, sebacic acid or azelaic acid.
Claim 13
Dependent Claim
19 words
The magnetic recording medium according to claim 10, wherein the aromatic dicarboxylic acid is terephthalic acid or isophthalic acid.
Claim 14
Dependent Claim
19 words
The magnetic recording medium according to claim 10, wherein the lower alcohol ester is a methyl or ethyl ester.
Claim 15
Dependent Claim
35 words
The magnetic recording medium according to claim 10, wherein the glycol is ethylene glycol, 1,3-propylene glycol, 1,4-butylene glycol, 1,6-hexane glycol, diethylene glycol, neopentyl glycol, or an ethylene oxide or propylene oxide adduct of bisphenol A.
Claim 16
Dependent Claim
21 words
The thermoplastic polyurethane resin according to claim 9, wherein the polyether diol is obtained by the cleavage polymerization of a lactone.
Claim 17
Dependent Claim
13 words
The magnetic recording medium according to claim 15, wherein the lactone is ε-caprolactone.
Claim 18
Dependent Claim
15 words
The magnetic recording medium according to claim 9, wherein the polyether diol is polyether glycol.
Claim 19
Dependent Claim
22 words
The magnetic recording medium according to claim 17, wherein the polyether glycol is polyethylene glycol, polypropylene ether glycol or polytetramethylene ether glycol.
Claim 20
Dependent Claim
36 words
The magnetic recording medium according to claim 9, wherein the polyether ester glycol is a polyester glycol obtained by the reaction of a polyalkylene ether glycol with an aliphatic dicarboxylic acid or an aromatic dicarboxylic acid.
Claim 21
Dependent Claim
23 words
The magnetic recording medium according to claim 19, wherein the polyalkylene ether glycol is polyethylene glycol, polypropylene ether glycol or polytetramethylene ether glycol.
Claim 22
Dependent Claim
22 words
The magnetic recording medium according to claim 19, where the aliphatic acid is succinic acid, adipic acid sebacic acid or azelaic acid.
Claim 23
Dependent Claim
18 words
The magnetic recording medium according to claim 19, wherein the aromatic acid is terephthalic acid or isophthalic acid.
Claim 24
Dependent Claim
22 words
The magnetic recording medium according to claim 1, where the short chain diol (B) is an aliphatic glycol or an aromatic diol.
Claim 25
Dependent Claim
24 words
The magnetic recording medium according to claim 23, wherein the aliphatic glycol is ethylene glycol, propylene glycol, 1,4-butylene glycol, 1,6-hexane glycol or neopentyl glycol.
Claim 26
Dependent Claim
30 words
The magnetic recording medium according to claim 23, wherein the aromatic glycol is an ethylene oxide or propylene oxide adduct of bisphenol A or an ethylene oxide adduct of hydroquinone.
Claim 27
Dependent Claim
24 words
The magnetic recording medium according to claim 1, wherein the organic diisocyanate (C) is an aromatic diisocyanate, an aliphatic diisocyanate or an alicyclic diisocyanate.
Claim 28
Dependent Claim
23 words
The magnetic recording medium according to claim 26, wherein the organic diisocyanate (C) is tolylene diisocyanate, 4,4'-diphenylmethane diisocyanate, para-xylene diisocyanate or isophorone diisocyanate.
Claim 29
Dependent Claim
39 words
The magnetic recording medium according to claim 1, wherein the short chain triol of the formula (II) is glycerine, an ethylene oxide adduct of glycerine, an ethylene oxide adduct of glycerine ethylene oxide, 2-methylpropane-1,2,3-triol, 4-bis[(2-hydroxyethyl)]-2-hydroxypentane, 3-methylpentane-1,3,5-triol or 1,2,6-hexane triol.
Claim 30
Dependent Claim
32 words
The magnetic recording medium according to claim 1, wherein the short chain triol of the formula (III) is 1-bis-(2-hydroxylethyl)amino-2-propanol, propylene oxide adduct of diethanol amine or ethylene oxide adduct of N-isopropanol diethanolamine.
Claim 31
Dependent Claim
36 words
The magnetic recording medium according to claim 1, wherein the thermoplastic polyurethane resin is used with a nitrocellulose, a vinyl chloride resin, a polyvinyl butyral, a bisphenol A type polyether or a vinyl chloride-hydroxy carboxylate copolymer.
Claim 32
Dependent Claim
25 words
The magnetic recording medium according to claim 30, wherein the nitrocellulose is one having a nitrogen content in a range from about 10 to 13%.
Claim 33
Dependent Claim
32 words
The magnetic recording medium according to claim 31, wherein the nitrocellulose is contained in the amount ranging from about 10 to 60% by weight based on the total weight of the binder.
Claim 34
Dependent Claim
40 words
The magnetic recording medium according to claim 30, wherein the vinyl chloride resin is a hard copolymer containing a vinyl alcohol component in a range from about more than 5% by weight based on the total weight of the binder.
Claim 35
Dependent Claim
20 words
The magnetic recording medium according to claim 33, wherein the vinyl chloride resin comprises a copolymerizable monomer as a component.
Claim 36
Dependent Claim
23 words
The magnetic recording medium according to claim 34, wherein the copolymerizable monomer is an aliphatic acid vinyl ester or an unsaturated aliphatic acid.
Claim 37
Dependent Claim
21 words
The magnetic recording medium according to claim 35, wherein the unsaturated aliphatic acid is acrylic acid, methacrylic acid or methyl methacrylate.
Claim 38
Dependent Claim
20 words
The magnetic recording medium according to claim 35, wherein the aliphatic acid vinyl ester is vinyl acetate or vinyl propionate.
Claim 39
Dependent Claim
35 words
The magnetic recording medium according to claim 34, wherein the vinyl chloride resin is vinyl chloride-vinyl alcohol copolymer, vinyl chloride-vinyl acetate-vinyl alcohol copolymer, vinyl chloride-vinyl propionate-vinyl alcohol copolymer or vinyl chloride-vinyl acetate-methyl methacrylate-vinyl alcohol copolymer.
Claim 40
Dependent Claim
36 words
The magnetic recording medium according to any one of claim 38, wherein the vinyl chloride resin is contained in the amount of about 10 to 20% by weight based on the total weight of the biner.
Claim 41
Dependent Claim
26 words
The magnetic recording medium according to claim 30, wherein the polyvinyl butyral is one obtained by the condensation reaction of a polyvinyl alcohol with butyl aldehyde.
Claim 42
Dependent Claim
37 words
The magnetic recording medium according to claim 40, wherein the polyvinyl butyral has a polymerization degree in a range from about 100 to 2,000 and a butylation degree in a range from about 55 to 80 mmol.
Claim 43
Dependent Claim
33 words
The magnetic recording medium according to claim 40, wherein the polyvinyl butyral is contained in the amount ranging from about 25 to 75% by weight based on the total weight of the binder.
Claim 44
Dependent Claim
29 words
The magnetic recording medium according to claim 30, wherein the bisphenol A type polyether is one obtained by the reaction of a bisphenol A with an alkylene oxide halogenide.
Claim 45
Dependent Claim
18 words
The magnetic recording medium according to claim 43, wherein the bisphenol A is 2,2-bis(4-oxyphenyl)propane or a derivative thereof.
Claim 46
Dependent Claim
17 words
The magnetic recording medium according to claim 43, wherein the alkylene oxide halogenide is epichlorohydrin or 1-chloro-2-methyl-2,3-epoxypropane.
Claim 47
Dependent Claim
20 words
The magnetic recording medium according to claim 45, wherein the bisphenol A type polyether contains an aliphatic saturated dicarboxylic acid.
Claim 48
Dependent Claim
28 words
The magnetic recording medium according to claim 46, wherein the aliphatic saturated dicarboxylic acid is glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid or sebacic acid.
Claim 49
Dependent Claim
35 words
The magnetic recording medium according to claim 43, wherein the bisphenol A type polyether is contained in the amount ranging from about 25 to 75% by weight based on the total weight of the binder.
Claim 50
Dependent Claim
59 words
The magnetic recording medium according to claim 30, wherein the vinyl chloride-hydroxy carboxylate copolymer is a copolymer having units represented by formula: ##STR15## (wherein: R 5 is hydrogen atom or methyl group; t is an integer from about 200 to 800; u is an integer from about 10 to 250; and w is an integer from 2 to 4).
Claim 51
Dependent Claim
32 words
The magnetic recording medium according to claim 49, wherein the copolymer is contained in the amount ranging from about 20 to 80% by weight based on the total weight of the binder.
Claim 52
Dependent Claim
22 words
The magnetic recording medium according to claim 2, wherein the polyisocyanate is an aliphatic polyisocyanate, an alicyclic polyisocyanate or an aromatic polyisocyanate.
Claim 53
Dependent Claim
15 words
The magnetic recording medium according to claim 51, wherein the aliphatic polyisocyanate is hexamethylene diisocyanate.
Claim 54
Dependent Claim
20 words
The magnetic recording medium according to claim 51, wherein the alicyclic polyisocyanate is isophorone diisocyanate, dicyclohexylmethane diisocyanate or methylcyclohexane diisocyanate.
Claim 55
Dependent Claim
33 words
The magnetic recording medium according to claim 51, wherein the aromatic polyisocyanate is tolylene diisocyanate, diphenylmethane diisocyanate, ditolylene diisocyanate, naphthalane diisocyanate, dianisidine diisocyanate, xylylene diisocyanate, tris(isocyanate phenyl)thiophosphate, triphenylmethane tricyanate or a polynuclear polyisocyanate.
References Cited (Backward Citations)
US4320171A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1986-01-10 | 1986-07-12 | 1987-01-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1990-01-10 | 1990-07-12 | 1991-01-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1994-01-10 | 1994-07-12 | 1995-01-11 | $7700.00 | Window Closed / Lapsed |