Process for the simultaneous graining and chromium-plating of steel plates as supports for lithographic applications
Assignee: Hoechst AG
•
Filing: 1985-07-03
•
Granted: 1986-10-28
•
Expires: 2005-07-03
Abstract
Abstract A process for producing chromium-plated, steel-based printing plate carriers comprises (A) simultaneously roughening and partially chromium-plating a substrate using alternating current in an electrolyte containing chromium, chloride, sulfate and, if appropriate, strontium ions and then, in the same electrolyte, (B) employing direct current to effect final chromium-plating. The printing plate supports produced in this manner have a uniform surface topography and peak-to-valley height values that are favorable for coating.
Inventors
- 👤 Engelbert Pliefke
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 17:44
CPC Classifications
C; C25; C25D; C25D3/00; C25D3/02; C25D3/04; B; B41; B41N; B41N1/00; B41N1/04; B41N1/08; C25F; C25F3/00; C25F3/02; C25F3/06; Y; Y10; Y10S; Y10S205/00; Y10S205/921
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
64 words
A process for preparing a chromium-plated steel or steel-based substrate suitable for use as a lithographic printing plate support, comprising the steps of: (A) plating said substrate with alternating current in an acid electrolyte bath containing chromium ions, chloride ions and sulfate ions with alternating current; and (B) in the same electrolyte bath, carrying out an electrochemical treatment of said substrate with direct current.
Claim 2
Dependent Claim
64 words
A process for preparing a chromium-plated steel or steel-based substrate suitable for use as a lithographic printing plate support, comprising the steps of: (A) plating said substrate with alternating current in an acid electrolyte bath containing chromium ions, chloride ions and sulfate ions with alternating current; and (B) in the same electrolyte bath, carrying out an electrochemical treatment of said substrate with direct current.
Claim 3
Dependent Claim
24 words
A process as claimed in claim 1, wherein said electrolyte bath has a concentration of chromium ion between about 10 and about 300 g/l.
Claim 4
Dependent Claim
21 words
A process as claimed in claim 2, wherein said concentration of chromium ion is between about 30 and about 100 g/l.
Claim 5
Dependent Claim
15 words
A process as claimed in claim 1, wherein said electrolyte bath further contains strontium ions.
Claim 6
Dependent Claim
23 words
A process as claimed in claim 4, wherein said electrolyte bath has a concentration of strontium ion of about 100 g/l or less.
Claim 7
Dependent Claim
24 words
A process as claimed in claim 1, wherein said electrolyte bath has a concentration of sulfate ion between about 0.1 and about 10 g/l.
Claim 8
Dependent Claim
24 words
A process as claimed in claim 1, wherein said electrolyte bath has a concentration of chloride ion between about 1 and about 50 g/l.
Claim 9
Dependent Claim
23 words
A process as claimed in claim 1, wherein said alternating current has a density between about 10 and about 150 A/dm 2 .
Claim 10
Dependent Claim
20 words
A process as claimed in claim 8, wherein said density is between about 30 and about 100 A/dm 2 .
Claim 11
Dependent Claim
23 words
A process as claimed in claim 1, wherein said direct current has a density between about 10 and about 100 A/dm 2 .
Claim 12
Dependent Claim
20 words
A process as claimed in claim 10, wherein said density is between about 10 and about 70 A/dm 2 .
Claim 13
Dependent Claim
24 words
A process as claimed in claim 1, wherein said electrolyte bath during said process has a temperature between about 20° and about 60° C.
Claim 14
Dependent Claim
26 words
A process as claimed in claim 1, wherein said substrate has a residence time in said electrolyte bath of between about 10 and about 300 seconds.
Claim 15
Dependent Claim
26 words
A process as claimed in claim 1, wherein said electrolyte bath has a flow velocity over said substrate of between about 5 and about 100 cm/second.
References Cited (Backward Citations)
US2907273A
Cited
US2939826A
Cited
US3041257A
Cited
US3303113A
Cited
FR2081148A1
Cited
US3951759A
Cited
US3929591A
Cited
US3979212A
Cited
US4234396A
Cited
EP0020021A2
Cited
US4371430A
Cited
US4445998A
Cited
JPS58107497A
Cited
EP0097503A2
Cited
EP0097502A2
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-10-27 | 1990-04-28 | 1990-10-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-10-27 | 1994-04-28 | 1994-10-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-10-27 | 1998-04-28 | 1998-10-28 | $7700.00 | Window Closed / Lapsed |