US4618650A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Siloxane containing network polymer
Assignee: Goodyear Tire and Rubber Co
•
Filing: 1985-09-04
•
Granted: 1986-10-21
•
Expires: 2005-09-04
Abstract
Abstract Metals from groups I and II are commonly used to catalyze the polymerization of monomers into polymers. The polymers formed in such polymerizations are terminated with the metal used to catalyze the polymerization and are sometimes referred to as living polymers. Such polymers can be crosslinked to produce a polymeric network by utilizing the process of the present invention. More specifically, the present invention discloses a process for endlinking a living polymer comprising reacting the living polymer which is metal terminated with a halogenated silicon containing compound to produce a polymer which is terminated with halogenated silicon moieties; followed by reacting that polymer with a tertiary alcohol to produce a polymer which is terminated with hydroxy silyl moieties. The polymer which is terminated with hydroxy silyl moieties can then be endlinked into a network polymer that contains siloxane linkages by simply heating it.
Inventors
- 👤 Adel F. Halasa
- 👤 George Jalics
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 17:48
CPC Classifications
C; C08; C08F; C08F236/00; C08F236/02; C08F236/04; C08C; C08C19/00; C08C19/30; C08C19/42; C08C19/44; C08F8/00; C08F8/42; C08G; C08G77/00; C08G77/42
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
131 words
A process for crosslinking a metal terminated polymer comprising: (a) reacting the metal terminated polymer with a molar excess of a halogenated silicon containing compound, wherein the halogenated silicon containing compound contains at least two halogen atoms which are bonded directly to a silicon atom, to produce a polymer which is terminated with halogenated silicon moieties wherein the halogenated silicon moieties contain at least one halogen atom which is bonded directly to a silicon atom; (b) reacting the polymer which is terminated with halogenated silicon moieties with a molar excess of a tertiary alcohol to produce a polymer which is terminated with hydroxy silyl moieties; and (c) allowing the polymer which is terminated with the hydroxy silyl moieties to crosslink under conditions sufficient to produce a crosslinked polymer containing siloxane linkages.
Claim 2
Dependent Claim
131 words
A process for crosslinking a metal terminated polymer comprising: (a) reacting the metal terminated polymer with a molar excess of a halogenated silicon containing compound, wherein the halogenated silicon containing compound contains at least two halogen atoms which are bonded directly to a silicon atom, to produce a polymer which is terminated with halogenated silicon moieties wherein the halogenated silicon moieties contain at least one halogen atom which is bonded directly to a silicon atom; (b) reacting the polymer which is terminated with halogenated silicon moieties with a molar excess of a tertiary alcohol to produce a polymer which is terminated with hydroxy silyl moieties; and (c) allowing the polymer which is terminated with the hydroxy silyl moieties to crosslink under conditions sufficient to produce a crosslinked polymer containing siloxane linkages.
Claim 3
Dependent Claim
202 words
A process for crosslinking a metal terminated polymer comprising: (a) reacting the metal terminated polymer with a molar excess of a halogenated silicon containing compound having the structural formula ##STR16## wherein X represents a halogen and wherein Z 1 and Z 2 can be the same or different and are selected from the group consisting of halogens and alkyl groups, to produce a polymer which is terminated with halogenated silicon moieties, wherein the halogenated silicon moieties have the structural formula ##STR17## wherein X represents a halogen and wherein Z 1 and Z 2 can be the same or different and are selected from the group consisting of halogens and alkyl groups; (b) reacting the polymer which is terminated with halogenated silicon moieties with a molar excess of a tertiary alcohol to produce a polymer which is terminated with hydroxy silyl moieties, wherein the hydroxy silyl moieties have the structural formula ##STR18## wherein A 1 and A 2 can be the same or different and are selected from the group consisting of alkyl groups and hydroxyl groups; and (c) allowing the polymer which is terminated with the hydroxy silyl moieties to crosslink under conditions sufficient to produce a crosslinked polymer containing siloxane linkages.
Claim 4
Dependent Claim
202 words
A process for crosslinking a metal terminated polymer comprising: (a) reacting the metal terminated polymer with a molar excess of a halogenated silicon containing compound having the structural formula ##STR16## wherein X represents a halogen and wherein Z 1 and Z 2 can be the same or different and are selected from the group consisting of halogens and alkyl groups, to produce a polymer which is terminated with halogenated silicon moieties, wherein the halogenated silicon moieties have the structural formula ##STR17## wherein X represents a halogen and wherein Z 1 and Z 2 can be the same or different and are selected from the group consisting of halogens and alkyl groups; (b) reacting the polymer which is terminated with halogenated silicon moieties with a molar excess of a tertiary alcohol to produce a polymer which is terminated with hydroxy silyl moieties, wherein the hydroxy silyl moieties have the structural formula ##STR18## wherein A 1 and A 2 can be the same or different and are selected from the group consisting of alkyl groups and hydroxyl groups; and (c) allowing the polymer which is terminated with the hydroxy silyl moieties to crosslink under conditions sufficient to produce a crosslinked polymer containing siloxane linkages.
Claim 5
Dependent Claim
25 words
A process as specified in claim 2 wherein the molar excess of said halogenated silicon containing compound is a molar excess of 200% to 2000%.
Claim 6
Dependent Claim
22 words
A process as specified in claim 3 wherein said crosslinking is conducted at a temperature of from 0° C. to 150° C.
Claim 7
Dependent Claim
15 words
A process as specified in claim 4 wherein said tertiary alcohol is tertiary butyl alcohol.
Claim 8
Dependent Claim
21 words
A process as specified in claim 5 wherein X represents a halogen selected from the group consisting of chlorine and bromine.
Claim 9
Dependent Claim
18 words
A process as specified in claim 6 wherein said alkyl groups contain from 1 to 20 carbon atoms.
Claim 10
Dependent Claim
23 words
A process as specified in claim 7 wherein the molar excess of said tertiary alcohol is a molar excess of 200% to 2000%.
Claim 11
Dependent Claim
12 words
A process as specified in claim 8 wherein the halogen is chlorine.
Claim 12
Dependent Claim
18 words
A process as specified in claim 9 wherein said alkyl groups contain from 1 to 8 carbon atoms.
Claim 13
Dependent Claim
25 words
A process as specified in claim 10 wherein the molar excess of said halogenated silicon containing compound is a molar excess of 400% to 1000%.
Claim 14
Dependent Claim
26 words
A process as specified in claim 11 wherein Z 1 and Z 2 represent chlorine atoms and wherein A 1 and A 2 represent chlorine atoms.
Claim 15
Dependent Claim
12 words
A process as specified in claim 12 wherein said metal is lithium.
Claim 16
Dependent Claim
14 words
A process as specified in claim 13 wherein said metal terminated polymer is polybutadiene.
Claim 17
Dependent Claim
22 words
A process as specified in claim 14 wherein said crosslinking is conducted at a temperature of from 110° C. to 140° C.
Claim 18
Dependent Claim
64 words
A process as specified in claim 1 wherein said halogenated silicon containing compound has a structural formula selected from the group consisting ##STR19## wherein X represents a halogen atom, wherein Z 1 and Z 2 can be the same or different and are selected from the group consisting of halogen atoms and alkyl groups and wherein n represents an integer from 1 to 20.
Claim 19
Dependent Claim
11 words
A crosslinked polymer made by the process specified in claim 1.
Claim 20
Dependent Claim
11 words
A crosslinked polymer made by the process specified in claim 2.
Claim 21
Dependent Claim
11 words
A crosslinked polymer made by the process specified in claim 13.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-10-20 | 1990-04-21 | 1990-10-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-10-20 | 1994-04-21 | 1994-10-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-10-20 | 1998-04-21 | 1998-10-21 | $7700.00 | Window Closed / Lapsed |