Method of forming a reactive metal anode having an edge seal
Assignee: Westinghouse Electric Corp
•
Filing: 1985-03-14
•
Granted: 1986-10-21
•
Expires: 2005-03-14
Abstract
Abstract An edge seal for a lithium or other consumable metal anode comprises a hydrophobic, chemically inert polymer coating having a high ratio of flexural modulus to flexural strength, a low Izod impact value, and low elongation properties. The seal is applied to the edge of the anode under an atmosphere of gas which is non-reactive with the anodic metal.
Inventors
- 👤 Arnold Z. Gordon
- 👤 Jerry L. Morris
- 👤 Gary E. Mason
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 16:45
CPC Classifications
H; H01; H01M; H01M12/00; H01M12/02; H01M4/00; H01M4/02; H01M4/06; H01M4/08; H01M4/12; H01M50/00; H01M50/10; H01M50/183; H01M50/186; H01M50/19; H01M50/193; H01M50/40; H01M50/409; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
186 words
A method of forming a sealed reactive metal anode useful in an electrochemical cell comprising said anode, a cathode and an electrolyte in which said anode and cathode are in operation during operation of said cell, said method comprising the steps of: (a) providing an anode of said reactive metal, said anode defining a first surface which contacts said electrolyte and at least one additional surface at the perimeter of at least a portion of said first surface; and, (b) coating said additional surface with a hydrophobic polymer which is substantially chemically inert with respect to said reactive metal and said electrolyte and wherein: (i) the ratio of the flexural modulus to the flexural strength of said polymer is at least about 25; (ii) the Izod impact value of said polymer is less than or equal to about 2.0 ft.-lb./in.; and, (iii) the percent elongation of said polymer is less than or equal to about 20%, said first surface being substantially free of said hydrophobic polymer, and said coating step (b) being carried out in an atmosphere which is non-reactive with respect to said reactive metal.
Claim 2
Independent Claim
186 words
A method of forming a sealed reactive metal anode useful in an electrochemical cell comprising said anode, a cathode and an electrolyte in which said anode and cathode are in operation during operation of said cell, said method comprising the steps of: (a) providing an anode of said reactive metal, said anode defining a first surface which contacts said electrolyte and at least one additional surface at the perimeter of at least a portion of said first surface; and, (b) coating said additional surface with a hydrophobic polymer which is substantially chemically inert with respect to said reactive metal and said electrolyte and wherein: (i) the ratio of the flexural modulus to the flexural strength of said polymer is at least about 25; (ii) the Izod impact value of said polymer is less than or equal to about 2.0 ft.-lb./in.; and, (iii) the percent elongation of said polymer is less than or equal to about 20%, said first surface being substantially free of said hydrophobic polymer, and said coating step (b) being carried out in an atmosphere which is non-reactive with respect to said reactive metal.
Claim 3
Dependent Claim
29 words
The method of claim 1 wherein said additional surface is coated by a method selected from the group consisting of abrasion coating, solution coating, aerosol spraying and pressure application.
Claim 4
Dependent Claim
13 words
The method of claim 1 wherein said non-reactive atmosphere comprises a Noble gas.
Claim 5
Dependent Claim
19 words
The method of claim 3 wherein said Noble gas is selected from the group consisting of argon and helium.
Claim 6
Dependent Claim
14 words
The method of claim 1 wherein said non-reactive atmosphere comprises a rigorously dry gas.
Claim 7
Dependent Claim
23 words
The method of claim 5 wherein said dry gas is selected from the group consisting of dry air, oxygen, nitrogen and carbon dioxide.
Claim 8
Dependent Claim
21 words
The method of claim 1 wherein said polymer is selected from the group consisting of paraffins, polyolefins, polyacrylates, polystyrenes and polyethers.
Claim 9
Dependent Claim
11 words
The method of claim 1 wherein said polymer contains a filler.
Claim 10
Dependent Claim
31 words
The method of claim 8 wherein said filler is selected from the group consisting of pyrolized polyacrylonitrile fiber, glass, glass fiber, pyrolized pitch fiber, graphite fiber, aluminum flakes and mineral filler.
Claim 11
Dependent Claim
17 words
The method of claim 1 wherein the physical characteristics of said polymer further satisfy the equation: ##EQU2##
Claim 12
Dependent Claim
10 words
The method of claim 1 wherein said polymer is polymethylmethacrylate.
Claim 13
Dependent Claim
10 words
The method of claim 1 wherein said polymer is polystyrene.
Claim 14
Dependent Claim
13 words
The method of claim 1 wherein said reactive metal is an alkali metal.
Claim 15
Dependent Claim
11 words
The method of claim 13 wherein said alkali metal is lithium.
Claim 16
Dependent Claim
10 words
The method of claim 14 wherein said polymer is polymethylmethacrylate.
Claim 17
Dependent Claim
10 words
The method of claim 14 wherein said polymer is polystyrene.
References Cited (Backward Citations)
US3892594A
Cited
US3791871A
Cited
US4053685A
Cited
US3967000A
Cited
US3976509A
Cited
US4007057A
Cited
US4315062A
Cited
US4188462A
Cited
US4398346A
Cited
US4402995A
Cited
US4503088A
Cited
US4414293A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-10-20 | 1990-04-21 | 1990-10-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-10-20 | 1994-04-21 | 1994-10-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-10-20 | 1998-04-21 | 1998-10-21 | $7700.00 | Window Closed / Lapsed |