Ceramic high dielectric composition
Assignee: Panasonic Holdings Corp
•
Filing: 1982-12-20
•
Granted: 1986-10-07
•
Expires: 2002-12-20
Abstract
Abstract PCT No. PCT/JP82/00472 Sec. 371 Date Aug. 17, 1983 Sec. 102(e) Date Aug. 17, 1983 PCT Filed Dec. 20, 1982 PCT Pub. No. WO83/02270 PCT Pub. Date Jul. 7, 1983.This invention relates to ceramic high dielectric composition with BaTiO3 as host component; and by containing 1-5 weight part of CaTiO3 and 2-3 weight parts of Ta2O5 to 100 weight parts of the BaTiO3, a composition having dielectric constant of 3000 or above, a small voltage dependency, a large bending strength and good high frequency characteristic is provided; and it has a good characteristic when used as thin film type dielectric body like laminated ceramic capacitor.
Inventors
- 👤 Gen Itakura
- 👤 Tadayoshi Ushijima
- 👤 Kenji Kusakabe
- 👤 Takayuki Kuroda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 19:25
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/46; C04B35/462; C04B35/465; C04B35/468; C04B35/4682; H; H01; H01G; H01G4/00; H01G4/002; H01G4/018; H01G4/06; H01G4/08; H01G4/12; H01G4/1209; H01G4/1218; H01G4/1227
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
136 words
In a ceramic composition having a high dielectric constant, said ceramic composition containing a host material, the improvement in which the host material consists essentially of: 1-5 parts by weight CaTiO 3 ; 2-3 parts by weight Ta 2 O 5 ; up to 0.2 by weight MnO 2 ; up to 0.5 by weight SiO 2 ; and the remainder is BaTiO 3 wherein each of the aforesaid parts by weight are parts by weight per 100 parts by weight BaTiO 3 , said ceramic composition having a dielectric constant ξ 25 of at least 3,000 measured at 25° C. with a 1 KHz at 1 VAC, a voltage dependency tan δ not more than 2.0 measured at an effective voltage of 50 V/mm and a bending strength of at least 690 Kg/cm 2 .
Claim 2
Dependent Claim
136 words
In a ceramic composition having a high dielectric constant, said ceramic composition containing a host material, the improvement in which the host material consists essentially of: 1-5 parts by weight CaTiO 3 ; 2-3 parts by weight Ta 2 O 5 ; up to 0.2 by weight MnO 2 ; up to 0.5 by weight SiO 2 ; and the remainder is BaTiO 3 wherein each of the aforesaid parts by weight are parts by weight per 100 parts by weight BaTiO 3 , said ceramic composition having a dielectric constant ξ 25 of at least 3,000 measured at 25° C. with a 1 KHz at 1 VAC, a voltage dependency tan δ not more than 2.0 measured at an effective voltage of 50 V/mm and a bending strength of at least 690 Kg/cm 2 .
Claim 3
Dependent Claim
131 words
In a ceramic composition having a high dielectric constant, said ceramic composition containing a host material, the improvement in which the host material consists essentially of: 1-5 parts by weight CaTiO 3 ; 1-4 parts by weight Ta 2 O 5 ; 1-4 parts by weight Gd 2 O 3 ; and the remainder is BaTiO 3 , wherein each of the foresaid parts by weight are parts by weight per 100 parts by weight of BaTiO 3 , said ceramic composition having a dielectric constant ξ 25 of at least 3,000 measured at 25° C. with a 1 KHz at 1 VAC, a voltage dependency tan δ not more than 2.0 measured at an effective voltage of 50 V/mm and a bending strength of at least 690 Kg/cm 2 .
Claim 4
Dependent Claim
131 words
In a ceramic composition having a high dielectric constant, said ceramic composition containing a host material, the improvement in which the host material consists essentially of: 1-5 parts by weight CaTiO 3 ; 1-4 parts by weight Ta 2 O 5 ; 1-4 parts by weight Gd 2 O 3 ; and the remainder is BaTiO 3 , wherein each of the foresaid parts by weight are parts by weight per 100 parts by weight of BaTiO 3 , said ceramic composition having a dielectric constant ξ 25 of at least 3,000 measured at 25° C. with a 1 KHz at 1 VAC, a voltage dependency tan δ not more than 2.0 measured at an effective voltage of 50 V/mm and a bending strength of at least 690 Kg/cm 2 .
Claim 5
Dependent Claim
27 words
The ceramic composition of claim 2 which further includes from 0.01 to 0.5 weight percent of at least one oxide of Mn, Cr, Fe, Ni or Co.
Claim 6
Dependent Claim
129 words
In a ceramic composition having a high dielectric constant, said ceramic composition containing a host material, the improvement in which the host material consists essentially of: 1-5 parts by weight CaTiO 3 ; 1-4 parts by weight Ta 2 O 5 ; 1-4 parts by weight Nd 2 O 3 ; and the remainder is BaTiO 3 , wherein each of the parts by weight are parts by weight per 100 parts by weight BaTiO 3 , said ceramic composition having a dielectric constant ξ 25 of at least 3,000 measured at 25° C. with a 1 KHz at 1 VAC, a voltage dependency tan δ not more than 2.0 measured at an effective voltage of 50 V/mm and a bending strength of at least 690 Kg/cm 2 .
Claim 7
Dependent Claim
129 words
In a ceramic composition having a high dielectric constant, said ceramic composition containing a host material, the improvement in which the host material consists essentially of: 1-5 parts by weight CaTiO 3 ; 1-4 parts by weight Ta 2 O 5 ; 1-4 parts by weight Nd 2 O 3 ; and the remainder is BaTiO 3 , wherein each of the parts by weight are parts by weight per 100 parts by weight BaTiO 3 , said ceramic composition having a dielectric constant ξ 25 of at least 3,000 measured at 25° C. with a 1 KHz at 1 VAC, a voltage dependency tan δ not more than 2.0 measured at an effective voltage of 50 V/mm and a bending strength of at least 690 Kg/cm 2 .
Claim 8
Dependent Claim
27 words
The ceramic composition of claim 4 which further includes from 0.01 to 0.5 weight percent of at least one oxide of Mn, Cr, Fe, Ni or Co.
Claim 9
Dependent Claim
130 words
In a ceramic composition having a high dielectric constant, said ceramic composition containing a host material, the improvement in which the host material consists essentially of: 1-5 parts by weight CaTiO 3 ; 1-4 parts by weight Ta 2 O 5 ; 1-4 parts by weight LA 2 O 3 ; and the remainder is BaTiO 3 , wherein each of the aforesaid parts by weight are parts by weight per 100 parts by weight BaTiO 3 , said ceramic composition having a dielectric constant ξ 25 of at least 3,000 measured at 25° C. with a 1 KHz at 1 VAC, a voltage dependency tan δ not more than 2.0 measured at an effective voltage of 50 V/mm and a bending strength of at least 690 Kg/cm 2 .
Claim 10
Dependent Claim
130 words
In a ceramic composition having a high dielectric constant, said ceramic composition containing a host material, the improvement in which the host material consists essentially of: 1-5 parts by weight CaTiO 3 ; 1-4 parts by weight Ta 2 O 5 ; 1-4 parts by weight LA 2 O 3 ; and the remainder is BaTiO 3 , wherein each of the aforesaid parts by weight are parts by weight per 100 parts by weight BaTiO 3 , said ceramic composition having a dielectric constant ξ 25 of at least 3,000 measured at 25° C. with a 1 KHz at 1 VAC, a voltage dependency tan δ not more than 2.0 measured at an effective voltage of 50 V/mm and a bending strength of at least 690 Kg/cm 2 .
Claim 11
Dependent Claim
27 words
The ceramic composition of claim 6 which further includes from 0.01 to 0.5 weight percent of at least one oxide of Mn, Cr, Fe, Ni or Co.
Claim 12
Dependent Claim
126 words
A ceramic composition having a high dielectric constant and containing BaTiO 3 as host material, the improvement in which the host material consists essentially of: 1-5 parts by weight of CaTiO 3 ; 2-3 parts by weight of Ta 2 O 5 ; and the remainder of the host material is BaTiO 3 , wherein each of the aforesaid parts by weight are parts by weight per 100 parts by weight of BaTiO 3 , said ceramic compostion having a dielectric constant ξ 25 of at least 3,000 measured at 25° C. with a 1 KHz at 1 VAC, a voltage dependency tan δ not more than 2.0 measured at an effective voltage of 50/V/mm and a bending strength of at least 690 Kg/cm 2 .
Claim 13
Dependent Claim
126 words
A ceramic composition having a high dielectric constant and containing BaTiO 3 as host material, the improvement in which the host material consists essentially of: 1-5 parts by weight of CaTiO 3 ; 2-3 parts by weight of Ta 2 O 5 ; and the remainder of the host material is BaTiO 3 , wherein each of the aforesaid parts by weight are parts by weight per 100 parts by weight of BaTiO 3 , said ceramic compostion having a dielectric constant ξ 25 of at least 3,000 measured at 25° C. with a 1 KHz at 1 VAC, a voltage dependency tan δ not more than 2.0 measured at an effective voltage of 50/V/mm and a bending strength of at least 690 Kg/cm 2 .
Claim 14
Dependent Claim
49 words
A ceramic capacitor consisting of a ceramic dielectric body formed by the ceramic composition of claim 8 having a plurality of internal electrodes therein and a pair of external electrodes attached to the surface of the dielectric body each external electrode in electrical contact with alternating adjacent inner electrodes.
References Cited (Backward Citations)
US29484A
Cited
US4073989A
Cited
US3268783A
Cited
US3490927A
Cited
US3753911A
Cited
USRE29484E
Cited
US4014707A
Cited
JPS5169198A
Cited
JPS51149599A
Cited
US4096098A
Cited
JPS5270399A
Cited
JPS5272499A
Cited
US4222783A
Cited
US4275521A
Cited
JPS5553006A
Cited
US4403236A
Cited
US4468472A
Cited
US4525767A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1989-10-06 | 1990-04-07 | 1990-10-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1993-10-06 | 1994-04-07 | 1994-10-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1997-10-06 | 1998-04-07 | 1998-10-07 | $7700.00 | Window Closed / Lapsed |